Solidification of metals

The term solidification indicates the conversion of material from the state of liquid to the state of solid. The solid-state is more compact and rigid than liquid, and the solidification indicates the transformation of material from a random state to a m…

Videos

Textbook Question

Chapter 5, Problem 74RQ

Why does a carburized part have to be further heatâ€�treated after the carbon is diffused into the surface? What are the various options?

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Chapter 5, Problem 73RQ

Chapter 5, Problem 75RQ

Students have asked these similar questions

During melting, what two principal impurities are introduced into the melt pool when the ladle is tapped through the open atmosphere? Group of answer choices Hydrogen and Nitrogen Hydrogen and Oxygen Oxygen and Carbon Nitrogen and Argon During ingot manufacture, which primary steel alloying element segregates with a low concentration at the bottom and a high concentration at the top of the ingot after solidification? Group of answer choices Iron Oxygen Carbon Nitrogen

Describe the phase transformation in tempering process

What are the possible defects of MIG welding on stainless steels?

Chapter 5 Solutions

Degarmo's Materials And Processes In Manufacturing

Ch. 5 - What is heat treatment?Ch. 5 - What types of properties can be altered through...Ch. 5 - Why should people performing hot forming or...Ch. 5 - What is the broad goal of the processing heat...Ch. 5 - Why might equilibrium phase diagrams be useful...Ch. 5 - What are theÂ A1,Â A3, andÂ Acm lines?Ch. 5 - What are some possible objectives of annealing...Ch. 5 - Why might it be important to include a preceding...Ch. 5 - Describe the cooling conditions of a full anneal.Ch. 5 - Why are the hypereutectoid steels not...

Ch. 5 - Although full anneals often produce the softest...Ch. 5 - What is the major process difference between full...Ch. 5 - Although normalizing is less expensive than a full...Ch. 5 - Prob. 14RQ Ch. 5 - What types of steel would be candidates for a...Ch. 5 - How might steel composition influence the...Ch. 5 - Other than increasing strength, for what three...Ch. 5 - What are the six major mechanisms that can be used...Ch. 5 - Prob. 19RQ Ch. 5 - What is required for a metal to be a candidate for...Ch. 5 - What are the three steps in an ageâ€�hardening...Ch. 5 - What is the difference between a coherent...Ch. 5 - What is overaging? Why does strength decrease?Ch. 5 - Describe the various aging responses (maximum...Ch. 5 - What is the difference between natural and...Ch. 5 - Why might naturally aging aluminum rivets be...Ch. 5 - Why is it important not to expose precipitation...Ch. 5 - Why is it more difficult to understand the...Ch. 5 - What types of heating and cooling conditions are...Ch. 5 - What are the stable equilibrium phases for steels...Ch. 5 - What are some nonequilibrium structures that...Ch. 5 - Prob. 32RQ Ch. 5 - What is the major factor that influences the...Ch. 5 - For a given steel, describe the relative strengths...Ch. 5 - Most structure changes proceed to completion over...Ch. 5 - What is retained austenite, and why is it an...Ch. 5 - What types of steels are more prone to retained...Ch. 5 - Why are martensitic structures usually tempered...Ch. 5 - Why does tempering offer a spectrum of possible...Ch. 5 - In what ways is the quenchâ€�andâ€�temper heat...Ch. 5 - What is a Câ€�Câ€�T diagram? Why is it more useful...Ch. 5 - What is the critical cooling rate, and how is it...Ch. 5 - What two features combine to determine the...Ch. 5 - What conditions are used to standardize the quench...Ch. 5 - How do the various locations of a Jominy test...Ch. 5 - How do the data collected from a Jominy test...Ch. 5 - What is the assumption that allows the data from a...Ch. 5 - What is hardenability? How is it different from...Ch. 5 - What capabilities are provided by...Ch. 5 - When selecting a steel for an application, what...Ch. 5 - What are the three stages of liquid quenching?Ch. 5 - What are some of the major advantages and...Ch. 5 - Why does brine provide faster cooling than water?Ch. 5 - Why is an oil quench less likely to produce quench...Ch. 5 - What are some of the attractive qualities of a...Ch. 5 - Prob. 56RQ Ch. 5 - Prob. 57RQ Ch. 5 - Prob. 58RQ Ch. 5 - Prob. 59RQ Ch. 5 - How might the thermally induced residual stresses...Ch. 5 - Prob. 61RQ Ch. 5 - Prob. 62RQ Ch. 5 - Prob. 63RQ Ch. 5 - What is thermomechanical processing?Ch. 5 - Prob. 65RQ Ch. 5 - Prob. 66RQ Ch. 5 - Prob. 67RQ Ch. 5 - Prob. 68RQ Ch. 5 - Prob. 69RQ Ch. 5 - Prob. 70RQ Ch. 5 - Prob. 71RQ Ch. 5 - Prob. 72RQ Ch. 5 - Prob. 73RQ Ch. 5 - Why does a carburized part have to be further...Ch. 5 - Prob. 75RQ Ch. 5 - Prob. 76RQ Ch. 5 - Prob. 77RQ Ch. 5 - Describe the distinguishing features of a box...Ch. 5 - What are some possible functions of artificial...Ch. 5 - Prob. 80RQ Ch. 5 - Prob. 81RQ Ch. 5 - Prob. 82RQ Ch. 5 - What are some current goals of the heat treatment...Ch. 5 - Prob. 1P Ch. 5 - Prob. 2P Ch. 5 - Prob. 3P Ch. 5 - Prob. 4P Ch. 5 - Prob. 5P Ch. 5 - Prob. 6P Ch. 5 - What problems might be expected if the material on...Ch. 5 - Describe some heat treatment processes or...Ch. 5 - Prob. 1.3CS Ch. 5 - Prob. 1.4CS Ch. 5 - Prob. 1.5CS Ch. 5 - Prob. 1.6CS Ch. 5 - Prob. 1.7CS Ch. 5 - Prob. 1.8CS Ch. 5 - Prob. 2.1CS Ch. 5 - Prob. 2.2CS Ch. 5 - How would you alter the procedures or policies of...

Additional Engineering Textbook Solutions

Find more solutions based on key concepts

In a glass factory a 2m -wide sheet of glass at 1500 K comes out of the final rollers, which fix the thickness ...

Fundamentals Of Thermodynamics

The impulses created by a falling weight onto a sample of URETHANE foam and CONFOR foam.

Engineering Mechanics: Statics & Dynamics (14th Edition)

F43. Determine the moment of the force about point O.

Engineering Mechanics: Statics

Calculate the drag forces on a 1/200 scale model of the Willis Tower that is tested in a large water flume unde...

Fox and McDonald's Introduction to Fluid Mechanics

8.17 Two channels area welded together at their flange tips to form a boxlike section as shown in Figure 8.18 ....

Applied Statics and Strength of Materials (6th Edition)

The two identical boards are bolted together to form the beam. Determine the maximum spacing s of the bolts to ...

Statics and Mechanics of Materials (5th Edition)

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.