Textbook Question
Chapter 5, Problem 11RQ
Although full anneals often produce the softest and most ductile structures, what might be some of the objections or undesirable features of these treatments.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Regarding annealing, choose the right answer
(One or more):
The actual annealing time must be long
enough to allow for any necessary
transformation reactions that may occur
Annealing can be performed to release
internal stresses of the material
The main purpose of annealing is to
decrease or restore material's ductility
Time isn't a significant parameter in
annealing process
If the rate of temperature change is too
great, temperature gradients and internal
stresses may be induced that may lead to
warping or even cracking
Which of the following may occur during an annealing heat treatment? (Please choose all that apply)
Stresses may be relieved
Ductility may decrease
Toughness may increase
Strength may increase
What is the advantage of nitriding? Select all correct answers.
Some complex components can be nitride without difficulty.
Better wear resistance.
Better fatigue resistance.
The cheapest method of case hardening.
What is the correct definition of plastic deformation?
The behavior of a material when its size changes by the addition of heat.
The behavior of a material that deforms under load and returns to its original shape when the load is removed.
Deformation caused by cleavage, where the material is actually pulled apart across atomic planes within the crystals or along the grain boundaries.
The behavior of a material that deforms under load and does not fully return to its original shape when the load is removed.
Chapter 5 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 5 - What is heat treatment?Ch. 5 - What types of properties can be altered through...Ch. 5 - Why should people performing hot forming or...Ch. 5 - What is the broad goal of the processing heat...Ch. 5 - Why might equilibrium phase diagrams be useful...Ch. 5 - What are the A1, A3, and Acm lines?Ch. 5 - What are some possible objectives of annealing...Ch. 5 - Why might it be important to include a preceding...Ch. 5 - Describe the cooling conditions of a full anneal.Ch. 5 - Why are the hypereutectoid steels not...
Ch. 5 - Although full anneals often produce the softest...Ch. 5 - What is the major process difference between full...Ch. 5 - Although normalizing is less expensive than a full...Ch. 5 - Prob. 14RQCh. 5 - What types of steel would be candidates for a...Ch. 5 - How might steel composition influence the...Ch. 5 - Other than increasing strength, for what three...Ch. 5 - What are the six major mechanisms that can be used...Ch. 5 - Prob. 19RQCh. 5 - What is required for a metal to be a candidate for...Ch. 5 - What are the three steps in an age�hardening...Ch. 5 - What is the difference between a coherent...Ch. 5 - What is overaging? Why does strength decrease?Ch. 5 - Describe the various aging responses (maximum...Ch. 5 - What is the difference between natural and...Ch. 5 - Why might naturally aging aluminum rivets be...Ch. 5 - Why is it important not to expose precipitation...Ch. 5 - Why is it more difficult to understand the...Ch. 5 - What types of heating and cooling conditions are...Ch. 5 - What are the stable equilibrium phases for steels...Ch. 5 - What are some nonequilibrium structures that...Ch. 5 - Prob. 32RQCh. 5 - What is the major factor that influences the...Ch. 5 - For a given steel, describe the relative strengths...Ch. 5 - Most structure changes proceed to completion over...Ch. 5 - What is retained austenite, and why is it an...Ch. 5 - What types of steels are more prone to retained...Ch. 5 - Why are martensitic structures usually tempered...Ch. 5 - Why does tempering offer a spectrum of possible...Ch. 5 - In what ways is the quench�and�temper heat...Ch. 5 - What is a C�C�T diagram? Why is it more useful...Ch. 5 - What is the critical cooling rate, and how is it...Ch. 5 - What two features combine to determine the...Ch. 5 - What conditions are used to standardize the quench...Ch. 5 - How do the various locations of a Jominy test...Ch. 5 - How do the data collected from a Jominy test...Ch. 5 - What is the assumption that allows the data from a...Ch. 5 - What is hardenability? How is it different from...Ch. 5 - What capabilities are provided by...Ch. 5 - When selecting a steel for an application, what...Ch. 5 - What are the three stages of liquid quenching?Ch. 5 - What are some of the major advantages and...Ch. 5 - Why does brine provide faster cooling than water?Ch. 5 - Why is an oil quench less likely to produce quench...Ch. 5 - What are some of the attractive qualities of a...Ch. 5 - Prob. 56RQCh. 5 - Prob. 57RQCh. 5 - Prob. 58RQCh. 5 - Prob. 59RQCh. 5 - How might the thermally induced residual stresses...Ch. 5 - Prob. 61RQCh. 5 - Prob. 62RQCh. 5 - Prob. 63RQCh. 5 - What is thermomechanical processing?Ch. 5 - Prob. 65RQCh. 5 - Prob. 66RQCh. 5 - Prob. 67RQCh. 5 - Prob. 68RQCh. 5 - Prob. 69RQCh. 5 - Prob. 70RQCh. 5 - Prob. 71RQCh. 5 - Prob. 72RQCh. 5 - Prob. 73RQCh. 5 - Why does a carburized part have to be further...Ch. 5 - Prob. 75RQCh. 5 - Prob. 76RQCh. 5 - Prob. 77RQCh. 5 - Describe the distinguishing features of a box...Ch. 5 - What are some possible functions of artificial...Ch. 5 - Prob. 80RQCh. 5 - Prob. 81RQCh. 5 - Prob. 82RQCh. 5 - What are some current goals of the heat treatment...Ch. 5 - Prob. 1PCh. 5 - Prob. 2PCh. 5 - Prob. 3PCh. 5 - Prob. 4PCh. 5 - Prob. 5PCh. 5 - Prob. 6PCh. 5 - What problems might be expected if the material on...Ch. 5 - Describe some heat treatment processes or...Ch. 5 - Prob. 1.3CSCh. 5 - Prob. 1.4CSCh. 5 - Prob. 1.5CSCh. 5 - Prob. 1.6CSCh. 5 - Prob. 1.7CSCh. 5 - Prob. 1.8CSCh. 5 - Prob. 2.1CSCh. 5 - Prob. 2.2CSCh. 5 - How would you alter the procedures or policies of...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- What is a cost advantage of using preformed parts in afabrication?arrow_forwardلانقطة واحدة of Warm working The advantages over cold working are: 1) forces and power are higher,2) more intricate work geometries possible, and 3) need for annealing may be reduced .or eliminated T F Blow molding is an important industrial process for making one- piece hollow plastic parts with thick .walls T Sly The sequence of the Blow Molding is automated and often integrated with downstream operations such .as bottle filling and labeling T لنقطة واحدةarrow_forwardHow can the effects of cold working be removed?arrow_forward
- Heat treatment is the controlled heating and cooling of metals to alter their physical and mechanical properties without changing the product shape. When performing the cooling step of the tempering process, knife makers have used material such as clay to cover portions of the blade to slow the cooling rate of the covered steel. Why may this technique be beneficial for making a sword which holds a sharp edge while remaining flexible enough to withstand the forces subjected to it in battle?arrow_forwardWhat are the critical differences between work hardening and geometric hardening?arrow_forwardMaterials Science Engineering; CCT Diagramarrow_forward
- What are the harmful effects of Misfueling?arrow_forwardIn addition to standard PPE, what specific PPE and safety precautions should be used during heat treating?arrow_forwardfor fuselage of an aircraft product How might you propose to fabricate this product? 5. Would the product require heat treatment? For what purpose? What kind of treatment? 6. Would this product require any surface treatment or coating? For what purpose? What would you recommendarrow_forward
- 4. How might you propose to fabricate this product? 5. Would the product require heat treatment? For what purpose? What kind of treatment? 6. Would this product require any surface treatment or coating? For what purpose? What would you recommendarrow_forwardWhat is the typical industrial reduction ratio for an ingot while being processed into a forging? Group of answer choices 7:2 3:1 2:1 10:1 How are oxides removed from the melt pool during a casting process? Group of answer choices Machined after solidification Collected in slag Allowed to diffuse out into the air Vacuum degassingarrow_forwardIndustrial Pipes Is the residual tightening given in screw cases intended to compensate for internal pressure and should be added to the initial tightening?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Precision Machining Technology (MindTap Course Li...Mechanical EngineeringISBN:9781285444543Author:Peter J. Hoffman, Eric S. Hopewell, Brian JanesPublisher:Cengage Learning
Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage Learning
Precision Machining Technology (MindTap Course Li...
Mechanical Engineering
ISBN:9781285444543
Author:Peter J. Hoffman, Eric S. Hopewell, Brian Janes
Publisher:Cengage Learning
Welding: Principles and Applications (MindTap Cou...
Mechanical Engineering
ISBN:9781305494695
Author:Larry Jeffus
Publisher:Cengage Learning
Introduction to Ferrous and Non-Ferrous Metals.; Author: Vincent Ryan;https://www.youtube.com/watch?v=zwnblxXyERE;License: Standard Youtube License