Chapter 5, Problem 54RQ
Why is an oil quench less likely to produce quench cracks than water or brine?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
normalizing advantages over quenching (heat treatment process)
1.Mention four quenchants and describe how each of them affect the strength of the material being quenched arranging them in a decending ordrer.
2. Draw a typical time temperature transformation diagram showing how a material is cooled under critical cooiling rate.
3. explain non equilibrium cooling
What happens to a quench hardened tool or machine part that was not tempered when it is subject to shock loads or bending stress?
Chapter 5 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 5 - What is heat treatment?Ch. 5 - What types of properties can be altered through...Ch. 5 - Why should people performing hot forming or...Ch. 5 - What is the broad goal of the processing heat...Ch. 5 - Why might equilibrium phase diagrams be useful...Ch. 5 - What are the A1, A3, and Acm lines?Ch. 5 - What are some possible objectives of annealing...Ch. 5 - Why might it be important to include a preceding...Ch. 5 - Describe the cooling conditions of a full anneal.Ch. 5 - Why are the hypereutectoid steels not...
Ch. 5 - Although full anneals often produce the softest...Ch. 5 - What is the major process difference between full...Ch. 5 - Although normalizing is less expensive than a full...Ch. 5 - Prob. 14RQCh. 5 - What types of steel would be candidates for a...Ch. 5 - How might steel composition influence the...Ch. 5 - Other than increasing strength, for what three...Ch. 5 - What are the six major mechanisms that can be used...Ch. 5 - Prob. 19RQCh. 5 - What is required for a metal to be a candidate for...Ch. 5 - What are the three steps in an age�hardening...Ch. 5 - What is the difference between a coherent...Ch. 5 - What is overaging? Why does strength decrease?Ch. 5 - Describe the various aging responses (maximum...Ch. 5 - What is the difference between natural and...Ch. 5 - Why might naturally aging aluminum rivets be...Ch. 5 - Why is it important not to expose precipitation...Ch. 5 - Why is it more difficult to understand the...Ch. 5 - What types of heating and cooling conditions are...Ch. 5 - What are the stable equilibrium phases for steels...Ch. 5 - What are some nonequilibrium structures that...Ch. 5 - Prob. 32RQCh. 5 - What is the major factor that influences the...Ch. 5 - For a given steel, describe the relative strengths...Ch. 5 - Most structure changes proceed to completion over...Ch. 5 - What is retained austenite, and why is it an...Ch. 5 - What types of steels are more prone to retained...Ch. 5 - Why are martensitic structures usually tempered...Ch. 5 - Why does tempering offer a spectrum of possible...Ch. 5 - In what ways is the quench�and�temper heat...Ch. 5 - What is a C�C�T diagram? Why is it more useful...Ch. 5 - What is the critical cooling rate, and how is it...Ch. 5 - What two features combine to determine the...Ch. 5 - What conditions are used to standardize the quench...Ch. 5 - How do the various locations of a Jominy test...Ch. 5 - How do the data collected from a Jominy test...Ch. 5 - What is the assumption that allows the data from a...Ch. 5 - What is hardenability? How is it different from...Ch. 5 - What capabilities are provided by...Ch. 5 - When selecting a steel for an application, what...Ch. 5 - What are the three stages of liquid quenching?Ch. 5 - What are some of the major advantages and...Ch. 5 - Why does brine provide faster cooling than water?Ch. 5 - Why is an oil quench less likely to produce quench...Ch. 5 - What are some of the attractive qualities of a...Ch. 5 - Prob. 56RQCh. 5 - Prob. 57RQCh. 5 - Prob. 58RQCh. 5 - Prob. 59RQCh. 5 - How might the thermally induced residual stresses...Ch. 5 - Prob. 61RQCh. 5 - Prob. 62RQCh. 5 - Prob. 63RQCh. 5 - What is thermomechanical processing?Ch. 5 - Prob. 65RQCh. 5 - Prob. 66RQCh. 5 - Prob. 67RQCh. 5 - Prob. 68RQCh. 5 - Prob. 69RQCh. 5 - Prob. 70RQCh. 5 - Prob. 71RQCh. 5 - Prob. 72RQCh. 5 - Prob. 73RQCh. 5 - Why does a carburized part have to be further...Ch. 5 - Prob. 75RQCh. 5 - Prob. 76RQCh. 5 - Prob. 77RQCh. 5 - Describe the distinguishing features of a box...Ch. 5 - What are some possible functions of artificial...Ch. 5 - Prob. 80RQCh. 5 - Prob. 81RQCh. 5 - Prob. 82RQCh. 5 - What are some current goals of the heat treatment...Ch. 5 - Prob. 1PCh. 5 - Prob. 2PCh. 5 - Prob. 3PCh. 5 - Prob. 4PCh. 5 - Prob. 5PCh. 5 - Prob. 6PCh. 5 - What problems might be expected if the material on...Ch. 5 - Describe some heat treatment processes or...Ch. 5 - Prob. 1.3CSCh. 5 - Prob. 1.4CSCh. 5 - Prob. 1.5CSCh. 5 - Prob. 1.6CSCh. 5 - Prob. 1.7CSCh. 5 - Prob. 1.8CSCh. 5 - Prob. 2.1CSCh. 5 - Prob. 2.2CSCh. 5 - How would you alter the procedures or policies of...
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
Determine the magnitude and direction of the resultant FR = F1 + F2 + F3 of the three forces by first finding t...
Engineering Mechanics: Statics
What parts are included in the vehicle chassis?
Automotive Technology: Principles, Diagnosis, And Service (6th Edition) (halderman Automotive Series)
The 60-mm-diameter steel shaft is subjected to the torques shown. Determine the angle of twist of end A with re...
Statics and Mechanics of Materials (5th Edition)
Three rigid bodies, 2,3, and 4, are connected by four springs as shown in the figure. A horizontal force of 1,0...
Introduction To Finite Element Analysis And Design
1.1 What is the difference between an atom and a molecule? A molecule and a crystal?
Manufacturing Engineering & Technology
Refer to the mechanism of the previous problem. Develop general expressions for the n- and t-components of the ...
Engineering Mechanics: Statics
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Why is brine quenching faster than water quenching?arrow_forwardHow can wear provide a self-sharpening effect on some hard faced parts?arrow_forward36 Asiacell O Homework 4 -... -> 3 Class Materials Eng. Dep. Heat Treatment Ismail Ibrahim Marhoon Homework 4 Q1: 1.5 in diameter steel part is quenched in oil with no agitation. (H=0.20). If we use a 4340; 4140; 8640; 5140; 1040 steel, what would be the hardness number at the center of the part? Q2: Determine the best quenching medium to produce a minimum hardness of HRC 40 at the center of a 3.75 cm diameter 4320 steel bar. Given Cingrate t 00c00 143 to 4340 50 40 8640 ab 9310 30 4320 1050 1040 10 20 it 1 1 2n 10 20 30 Jominy distance th of an inch) Die he eted e TABLE The N canticient, or seveity of the querch, far several guenehing sedla H Coefticient Coaling Rate at he Center of a l-in. Bar (CA) Medium Ol no taton) 04 anitation) 025 18 45 HyD inc agtation H0 fegiutont Brine Ino agtaton) Brine lapttiori 10 4.0 190 20 60 90 230 Ad DISTANCE FROM OUENCHED END IN) DIAMETER IN)arrow_forward
- How can some nonferrous metal alloys such as aluminum or Monel be hardened?arrow_forward9 4.Scale formation is due to oxidation in hot working process. Select one: True Falsearrow_forwardThe purpose of heat treatment procedure for quenching is a. to decrease hardness b. to increase impact energy O c. to get finer grain size structure O d. to increase hardness O e. to improve ductilityarrow_forward
- False True Zinc, Lead, Tin, and Others.1 - Examples of Corrosion- Resistant Metals Copper is heavier than iron .2 Typically, nonferrous .3 metals and alloys are more :costly - True or False Workability, lightweight, .4 corrosion resistance, good electrical and thermal conductivity, optical reflectivity, array of finishes. It is easily recycled. Poor weldability when in pure form because of oxide coating. - Properties of Aluminum Nickel, Iron and Nickel, or.5 Cobalt. They were created for use at high temperatures, which means they have exceptional creep resistance. This comes with a sacrifice in weight. - What are Prefractory metals Ceramic brakes reduce .6 vehicle weight, resist heat- induced fading and are expected to last the life of the vehicle Nonferrous Metals and.7 alloys have lower strength and lower stiffness. They are corrosion resistive, have ease of fabrication, high electrical and thermal conductivity, light weight, strength at high temps and have colorarrow_forwardChoose the correct optionarrow_forwardWhat problems can occur to stainless steel as it is allowed to form carbide precipitation during welding?arrow_forward
- Can someone please help me to answer all of the following questions. PLEASE AND THANK YOU!!!!arrow_forwardAnswer with brief description is required. Post answer ASAParrow_forwardHow does polishing a connecting rod in a high speed internal combustion engine help to reduce the possibility of failure by fatiguearrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage LearningUnderstanding Motor ControlsMechanical EngineeringISBN:9781337798686Author:Stephen L. HermanPublisher:Delmar Cengage Learning
Welding: Principles and Applications (MindTap Cou...
Mechanical Engineering
ISBN:9781305494695
Author:Larry Jeffus
Publisher:Cengage Learning
Understanding Motor Controls
Mechanical Engineering
ISBN:9781337798686
Author:Stephen L. Herman
Publisher:Delmar Cengage Learning
Thermodynamics - Chapter 3 - Pure substances; Author: Engineering Deciphered;https://www.youtube.com/watch?v=bTMQtj13yu8;License: Standard YouTube License, CC-BY