Question
Chapter 11, Problem 28CQ
To determine
Whether it is safe to assume that a part could withstand an infinite number of stress applications that are of only
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Task (3)
you are asked to perform tensile test on specimens of two different materials (A and B) and you obtained the
stress-strain diagram of the two specimens as shown in Figure 2:
400
350
300
250
Material A
200
150
100
50
0.02
0.04
0.06
0.08
0.1
0.12
0.14
0.16
0.18
Strain (mm/mm)
50
Material B
30
20
10
0.02
0.04
0.06
0.08
0.1
Strain (mm/mm)
Figure 2: Tensile Test Analysis
Stress (MPa)
Stress (MPa)
A 7075-T651 alloy is used in a structural component in an airplane. The component must
not fail when subjected to a stress of 250 MPa. Several surface flaws have been detected on the
component. What is the largest (deepest) surface flaw that could be permitted with the 250
MPa maximum stress? Use data from Table 1 and assume this component geometry and loading
condition result in a Y value of 1.25.
Yield Strength
KI
Material
MPa
ksi
MPa√m
ksiVin.
Metals
Aluminum alloy (7075-T651)
495
72
24
22
After an inspection it is found that a structural ceramic part has no flaws greater than 100 micrometers in size, calculate the maximum service stress (in MPa) available with SiC. Assume that Y= 1
Chapter 11 Solutions
Materials Science And Engineering Properties
Ch. 11 - Prob. 1CQCh. 11 - Prob. 2CQCh. 11 - Prob. 3CQCh. 11 - Prob. 4CQCh. 11 - Prob. 5CQCh. 11 - Prob. 6CQCh. 11 - Prob. 7CQCh. 11 - Prob. 8CQCh. 11 - Prob. 9CQCh. 11 - Prob. 10CQ
Ch. 11 - Prob. 11CQCh. 11 - Prob. 12CQCh. 11 - Prob. 13CQCh. 11 - Prob. 14CQCh. 11 - Prob. 15CQCh. 11 - Prob. 16CQCh. 11 - Prob. 17CQCh. 11 - Prob. 18CQCh. 11 - Prob. 19CQCh. 11 - Prob. 20CQCh. 11 - Prob. 21CQCh. 11 - Prob. 22CQCh. 11 - Prob. 23CQCh. 11 - Prob. 24CQCh. 11 - Prob. 25CQCh. 11 - Prob. 26CQCh. 11 - Prob. 27CQCh. 11 - Prob. 28CQCh. 11 - Prob. 29CQCh. 11 - Prob. 30CQCh. 11 - Prob. 1ETSQCh. 11 - Prob. 2ETSQCh. 11 - Prob. 3ETSQCh. 11 - Prob. 4ETSQCh. 11 - Prob. 5ETSQCh. 11 - Prob. 6ETSQCh. 11 - Prob. 7ETSQCh. 11 - Prob. 8ETSQCh. 11 - Prob. 9ETSQCh. 11 - Prob. 10ETSQCh. 11 - Prob. 11.1PCh. 11 - Prob. 11.2PCh. 11 - Prob. 11.3PCh. 11 - Prob. 11.4PCh. 11 - Prob. 11.5PCh. 11 - Prob. 11.6PCh. 11 - Prob. 11.7PCh. 11 - Prob. 11.8PCh. 11 - Prob. 11.9PCh. 11 - Prob. 11.10PCh. 11 - Prob. 11.11PCh. 11 - Prob. 11.12PCh. 11 - Prob. 11.13PCh. 11 - Prob. 11.14P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- At the ultimate tensile strength. (a) The true stress is at its maximum. (b) The specimen always fractures. (c) The maximum load-carrying capacity is experienced. (d) The material yields.arrow_forwardThe frame of a space shuttle type vehicle must have a high yield strength and high stillness, and the most important design factor is weight. Of all the materials presented in this chapter, what material might be the most suitable for the frame of a space shuttle? Assume that there will be both tensile and compressive stresses. For a space shuttle, cost is not a limiting factor. (a) You can eliminate entire classes of materials from consideration with a brief statement about their unsuitability. (b) What material has the highest specific yield strength? Give the yield strength, specific gravity, specific yield strength, elastic modulus, and specific elastic modulus for this material. (c) What material has the highest specific elastic modulus? Give the yield strength, specific gravity, specific yield strength, elastic modulus, and specific elastic modulus for this material. (d) Compare the materials with the highest specific yield strength and highest specific elastic modulus for suitability in the space shuttle frame. (C) Discuss the suitability of the top-rated material for this design from the viewpoint of the ability to produce a frame.arrow_forwardMechanical Properties-Metals For a bronze alloy, the stress at which plastic deformation begins is 295 MPa and the modulus of elasticity (E) is 108 GPa. (a) What is the maximum load (Fy) that can be applied to a specimen having a cross-sectional area of 314 mm2 without plastic deformation? (b) If the original specimen length is 142 mm, what is the maximum length to which it may be stretched without causing plastic deformation?arrow_forward
- A batch of casted mild steel has a modulus of elasticity of 200 GPa and a yield strength of 250 MPa. Calculate for its modulus of resilience. After cold working the steel, the yield strength increases to 310 MPa. Calculate for the percent reduction in the average grain diameter given σo = 70 MPa and k = 0.74.arrow_forwardi need quickly please please please Which of these cast iron would allow the greatest amount of plastic deformation before fracture . Nodular cast iron Grey cast iron White cast iron None of them can be worked. If the diameter of steel specimen stretched by tension load is doubled , then it’s tensile strength will be Halved Remain unaffected Doubled Become four times Temperature is proportional with Percent of elongation Tensile strength Modulus of elasticity All above The tensile strength of a steel specimen that have a 182 HB , equals to 490 MPa 910 MPa 627 MPa Not given…arrow_forward(b) (i) A tensile test specimen made from 0.4% C steel has a circular cross section of diameter d mm and a gauge length of 25 mm. When a load of 4500 N is applied during the test, the gauge length of the specimen extends to 25.02 mm. If the Young's Modulus of the steel is 199 GPa, calculate the diameter of the tensile test specimen used. 4arrow_forward
- (a) the modulus of elasticity in GPa for the Aluminum B) the proportional limit in MPa for the Aluminum C) the ultimate strength in MPa for the Aluminum D) Ductility of material based on percent elongationarrow_forwardI need the answer as soon as possiblearrow_forwardA steel specimen is tested in tension. The specimen is 50 mm wide by 25 mm thick in the test region.The specimen yields at a load of 160 kN and fractures at 215 kN. Determine the tensile stress at fracture.arrow_forward
- Q3: A cylindrical specimen of steel having an original diameter of (12.8mm) is tensile tested to fracture and found to have engineering fracture strength of (450MP ). If its cross-sectional diameter at fracture is (10.7mm), determine: (1) the ductility in terms of percent reduction in area and (2) the true stress at fracture.arrow_forwardAn aluminum alloy rod with 10 mm diameter was subjected to a 5-kN tensile load. After the load was applied, the diameter was measured and found to be 9.997 mm. If the yield strength is 139 MPa, calculate the Poisson’s ratio of the material.arrow_forwardAn aluminum alloy rod with 10 mm diameter was subjected to a 5-kN tensile load. After the load was applied, the diameter was measured and found to be 9.997 mm.If the yield strength is 139 MPa, calculate the Poisson’s ratio of the material.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning