Question
Chapter 11, Problem 10ETSQ
To determine
The best way to increase the fatigue crack propagation cycle to failure.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A ceramic part is used under a complete reverse cyclic stress with a stress amplitude (S) of 250 MPa. The yield strength and fracture toughness of materials is 550 MPa and 12.5 MPa*sqrt(m), respectively. Y is 1.4. What is the critical surface crack length?
A structural component in the shape of a flat plate 20.8 mm thick is to be made
from a metal with yield strength of 533 MPa and a critical fracture toughness of
22.0 MPa-m!2. Assume a crack forms in the plate, and the geometry of the crack
yields a Y value of 1.5. If the plate is designed to a design stress equivalent to 0.3
times the yield strength, what is the critical crack length?
Equations:
1/2
()
Om
К
= 2
σο
K. = YocTa
%3D
Pt
A chemicals company is looking to optimise the materials selection for their synthesis vessel with safety being the key priority. The tank can
be treated as a small thin-walled spherical pressure vessel and the engineers are considering a 'yield before break' design concept.
Given that a crack of length will propagate by fast fracture when the stress intensity factor reaches the fracture toughness of the material
select the correct materials property index relevant to this design criterion.
Fracture toughness K₁=Yo√na
IC
OM=
OM=
OM=
KIC
of
OM=
d
OM=
P
K 2
IC
K
IC
P
o a
M=
K
IC
K
2
IC
Chapter 11 Solutions
Materials Science And Engineering Properties
Ch. 11 - Prob. 1CQCh. 11 - Prob. 2CQCh. 11 - Prob. 3CQCh. 11 - Prob. 4CQCh. 11 - Prob. 5CQCh. 11 - Prob. 6CQCh. 11 - Prob. 7CQCh. 11 - Prob. 8CQCh. 11 - Prob. 9CQCh. 11 - Prob. 10CQ
Ch. 11 - Prob. 11CQCh. 11 - Prob. 12CQCh. 11 - Prob. 13CQCh. 11 - Prob. 14CQCh. 11 - Prob. 15CQCh. 11 - Prob. 16CQCh. 11 - Prob. 17CQCh. 11 - Prob. 18CQCh. 11 - Prob. 19CQCh. 11 - Prob. 20CQCh. 11 - Prob. 21CQCh. 11 - Prob. 22CQCh. 11 - Prob. 23CQCh. 11 - Prob. 24CQCh. 11 - Prob. 25CQCh. 11 - Prob. 26CQCh. 11 - Prob. 27CQCh. 11 - Prob. 28CQCh. 11 - Prob. 29CQCh. 11 - Prob. 30CQCh. 11 - Prob. 1ETSQCh. 11 - Prob. 2ETSQCh. 11 - Prob. 3ETSQCh. 11 - Prob. 4ETSQCh. 11 - Prob. 5ETSQCh. 11 - Prob. 6ETSQCh. 11 - Prob. 7ETSQCh. 11 - Prob. 8ETSQCh. 11 - Prob. 9ETSQCh. 11 - Prob. 10ETSQCh. 11 - Prob. 11.1PCh. 11 - Prob. 11.2PCh. 11 - Prob. 11.3PCh. 11 - Prob. 11.4PCh. 11 - Prob. 11.5PCh. 11 - Prob. 11.6PCh. 11 - Prob. 11.7PCh. 11 - Prob. 11.8PCh. 11 - Prob. 11.9PCh. 11 - Prob. 11.10PCh. 11 - Prob. 11.11PCh. 11 - Prob. 11.12PCh. 11 - Prob. 11.13PCh. 11 - Prob. 11.14P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- q3arrow_forwardAn aircraft component is fabricated from an aluminum alloy that has a plane strain fracture toughness of 34 MPaym. It has been determined that fracture results at a stress of 221 MPa when the maximum (or critical) internal crack length is 2.94 mm. a) Determine the value of Yona for this same component and alloy at a stress level of 287 MPa when the maximum internal crack length is 1.47 mm. MPaymarrow_forwardi need the answer quicklyarrow_forward
- For a specimen of a steel alloy with a plane strain fracture toughness of 80 MPa√m, fracture results at a stress of 510 MPa when the maximum (or critical) internal crack length is 6 mm. For the same alloy, will fracture occur at a stress level of 380 MPa when the maximum internal crack is 9.0 mm? Why or why not? Select the most appropriate answer based on your calculation. Select one: a. It will not fracture b. Not enough information c. It will fracturearrow_forward(b) The difference between the theoretical and measured fracture strengths of brittle materials is explained by the presence of small flaws or cracks. In terms of these pre-existing flaws or cracks, briefly describe the occurring phenomena when a brittle material fractures in tension. (i) (ii) Explain why ductile materials do not fail in a brittle manner even though they have small flaws and crack present. If so, explain the process of ductile fracture of the materials.arrow_forwardA component made of Aluminium 6061-T651 has an edge crack with length equal to 15 mm, as shown The yield stress of the material is oy = 280 MPa and its fracture toughness (Kic) ranges from 40 MN/m3/2 to 60 MN/m³/2 Consider now the same edge crack in a semi-infinite plate. Determine the critical stress to avoid fracture. P I I I I ← 15 mm P↓ 100 mm 30 mmarrow_forward
- A specimen of a 4340 steel alloy having a plane strain fracture toughness of 45 MPA/M is exposed to a stress of 1000 MPa (145,000 psi). Will this specimen experience fracture if it is known that the largest surface crack is 0.75 mm (0.03 in.) long? Why or why not? Assume that the parameter Y has a value of 1.0.arrow_forwardA structural component in the shape of a flat plate 24.3 mm thick is to be fabricated from a metal alloy for which the yield strength and plane strain fracture toughness values are 533 MPa and 22.0 MPa-m1/2, respectively. For this particular geometry, the value of Y is 1.3. Assuming a design stress of 0.4 times the yield strength, calculate the critical length of a surface flaw. What formulas do i use ? And how do i use them?arrow_forwardNiloarrow_forward
- (b) An aluminium plate (100 mm width x 300 mm height x 4 mm thick) with a centre-crack is subjected to a mode-l service load of 40 kN. Assume that the fracture toughness of the material is 24 MPa Vm and Y-1.0. (ii) What is the safety factor on crack length? Assume that the yield strength of aluminium is 425 MPa.arrow_forwardThe following data were obtained from a series of Charpy impact tests performed on four steels, each having a different manganese content. Plot the data and determine (a) the transition temperature of each (defined by the mean of the absorbed energies in the ductile and brittle regions); and (b) the transition temperature of each (defined as the temperature that provides 50 J of absorbed energy)arrow_forwardA very large, steel plate of yield stress 200 MPa has a crack at the centre of length 18 mm, orientated along the x-axis. If the plate is subjected to far field tensile loading of magnitude 179 MPa and is assumed to be in a state of plane strain, determine the extent of the plastic region at the crack tip, along the x-axis. You may assume Poisson's ratio is (1/3). Express your answer as an integer value of mm.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning