Textbook Question
Chapter 3, Problem 3.25QP
A No. 10 steel rebar is tested in tension. By monitoring the load reading of the testing machine, it was found that the specimen yielded at a load of 41,600 lb and fractured at 48,300 lb.
- 1. Determine the tensile stresses at yield and at fracture.
- 2. Estimate how much increase in length would occur at 70% of the yield stress in a 2-in. gauge length.
Expert Solution & Answer
Trending nowThis is a popular solution!
Students have asked these similar questions
A steel specimen is tested in tension. The specimen is 25 mm wide by 5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 55 kN and fractured at 78 kN.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much elongation would occur at 60% of the yield stress in a 50-mm gauge length.
A steel specimen is tested in tension. The specimen is 1 in. wide by 0.5 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 36 kips and fractured at 48 kips.a. Determine the tensile stress at yield and at fracture.b. If the original gauge length was 4 in., estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
Chapter 3 Solutions
Materials for Civil and Construction Engineers (4th Edition)
Ch. 3 - What is the chemical composition of steel? What is...Ch. 3 - Why does the ironcarbon phase diagram go only to...Ch. 3 - Draw a simple ironcarbon phase diagram showing the...Ch. 3 - What is the typical maximum percent of carbon in...Ch. 3 - Calculate the amounts and compositions of phases...Ch. 3 - Briefly discuss four heat treatment methods to...Ch. 3 - Define alloy steels. Explain why alloys are added...Ch. 3 - Prob. 3.8QPCh. 3 - Specifically state the shape and size of the...Ch. 3 - What are the typical uses of structural steel?
Ch. 3 - What is the range of thicknesses of cold-formed...Ch. 3 - Why is coil steel used for cold-formed steel...Ch. 3 - If a steel with a 33 ksi yield strength is used...Ch. 3 - Why is reinforcing steel used in concrete? Discuss...Ch. 3 - What is high-performance steel? State two HPS...Ch. 3 - Name three mechanical tests used to measure...Ch. 3 - The following laboratory tests are performed on...Ch. 3 - Sketch the stress-strain behavior of steel, and...Ch. 3 - Three steel bars with a diameter of 25 mm and...Ch. 3 - Three steel bars with a diameter of 0.5 in. and...Ch. 3 - Draw a typical stressstrain relationship for steel...Ch. 3 - Getting measurements from Figure 3.18, determine...Ch. 3 - A steel specimen is tested in tension. The...Ch. 3 - A steel specimen is tested in tension. The...Ch. 3 - A No. 10 steel rebar is tested in tension. By...Ch. 3 - A mild steel specimen originally 300 mm long is...Ch. 3 - A tension stress of 70 ksi was applied on a 12-in....Ch. 3 - A tensile stress is applied along the long axis of...Ch. 3 - A cylindrical steel alloy rod with a 0.5 in....Ch. 3 - A round steel alloy bar with a diameter of 0.75...Ch. 3 - A 19-mm reinforcing steel bar and a gauge length...Ch. 3 - Testing a round steel alloy bar with a diameter of...Ch. 3 - During the tension test on a steel rod within the...Ch. 3 - A grade 36 round steel bar with a diameter of 0.5...Ch. 3 - A high-yield-strength alloy steel bar with a...Ch. 3 - Estimate the cross-sectional area of a 350S125-27...Ch. 3 - An ASTM A615 grade 60 number 10 rebar with a gauge...Ch. 3 - A 32-mm rebar with a gauge length of 200 mm was...Ch. 3 - A steel pipe having a length of 3 ft. an outside...Ch. 3 - A steel pipe having a length of 1 m, an outside...Ch. 3 - A drill rod with a diameter of 10 mm is made of...Ch. 3 - A drill rod with, a diameter of 1/2 in. is made of...Ch. 3 - Prob. 3.43QPCh. 3 - An engineering technician performed a tension test...Ch. 3 - A Charpy V Notch (CVN) test was performed on a...Ch. 3 - Prob. 3.46QPCh. 3 - Prob. 3.47QPCh. 3 - How can the flaws in steel and welds be detected?...Ch. 3 - Determine the welding zone classification of A36...Ch. 3 - Briefly define steel corrosion. What are the four...Ch. 3 - Discuss the main methods used to protect steel...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.arrow_forwardThe results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.arrow_forwardA tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.arrow_forward
- A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?arrow_forwardA steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips. a. Determine the tensile stresses at yield and at fracture. b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge length. Step-by-step solution: Step 1 of 4 Given that: Width of the specimen, b = 1 in Thickness of the specimen, t = 0.25 in Yield load on the specimen, Py = 12.5 kips Fracture load on the specimen, Pf = 17.5 kips Gauge length, L = 2 in Percentage of yield stress = 60%arrow_forwardA steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge length.arrow_forward
- 3. A steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips. а. Determine the tensile stresses at yield and at fracture. b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge lengtharrow_forwardA No. 10 steel rebar is tested in tension. By monitoring the load reading of the testing machine, it was found that the specimen yielded at a load of 41,600 lb and fractured at 48,300 lb.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much increase in length would occur at 70% of the yield stress in a 2-in. gauge length.arrow_forwardDuring a tensile test on a specimen of steel the following data was recorded diameter of the specimen is 6.6mm,gage length 5mm,elongation of a load of 6.0KN is 0.043mm.load at yield point is 9.7KN at failure is 14.2KN ,reduction of the area is 45 percent. Calculate Young's modulus of elasticity, the yield stress and the ultimate stressarrow_forward
- This figure shows typical stress-strain behaviour for a brass. The inset figure shows the behaviour at low strains. 500 70 Tosle strength 450 MPa 166,000 ps 60 400 300 MP 40 30 200 Yeld steg 250 MPa (,0a 200 20아 100- 20 100 10 0.20 030 040 If the cylindrical test sample is initially 14cm long with an initial radius of 2mm, estimate the true stress in MPa at the ultimate tensile stress. (Enter your answer to the nearest whole number) an esarrow_forward(b) (i) A tensile test specimen made from 0.4% C steel has a circular cross section of diameter d mm and a gauge length of 25 mm. When a load of 4500 N is applied during the test, the gauge length of the specimen extends to 25.02 mm. If the Young's Modulus of the steel is 199 GPa, calculate the diameter of the tensile test specimen used. 4arrow_forward7) A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iii) Percentage elongation. (iv) Percentage reduction in area. (v) Ultimate tensile stress.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Steel Design (Activate Learning with these NEW ti...Civil EngineeringISBN:9781337094740Author:Segui, William T.Publisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
Steel Design (Activate Learning with these NEW ti...
Civil Engineering
ISBN:9781337094740
Author:Segui, William T.
Publisher:Cengage Learning
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY