Textbook Question
Chapter 2, Problem 60QTP
A cable is made of two strands of different materials, A and B, and cross-sections, as follows:
For material A, K = 60,000 psi, n = 0.5, Ao = 0.6 in2;
for material B, K = 30,000 psi, n = 0.5, Ao = 0.3 in2.
Calculate the maximum tensile force that this cable can withstand prior to necking.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A cable is made of two strands of different materials, A and B, and cross sections as follows:
For material A: K=70,000 psi, n=0.5, A0=0.6 in2.
For material B: K=25,000 psi, n=0.5, A0=0.3 in2
Calculate the maximum tensile force that this cable can withstand.
A sample of silicone breast implant, polydimethylsiloxane (PDMS), is placed under unconfined compression. The magnitudes of the resulting longitudinal and transverse strains have been measured to be 2.7 and 1.341, respectively. The young's modulus of the implant is 500 kPa. Calculate the shear and bulk moduli.
The tensile modulus of a 0°, 90°, and 45° graphite/epoxy ply is measured as follows to give E₁ =
26.25 Msi, E2 = 1.494 Msi, Ex = 2.427 Msi for the 45° ply, respectively.
1. What is the value Ex for a 30° ply?
2. Can you calculate the values of v12 and G12 from the previously measured three values of
elastic moduli?
Chapter 2 Solutions
Manufacturing Engineering & Technology
Ch. 2 - Distinguish between engineering stress and true...Ch. 2 - In a stress-strain curve, what is the proportional...Ch. 2 - Describe the events that take place when a...Ch. 2 - What is ductility, and how is it measured?Ch. 2 - In the equation =Kn, which represents the true...Ch. 2 - What is strain-rate sensitivity, and how is it...Ch. 2 - What test can measure the properties of a material...Ch. 2 - What testing procedures can be used to measure the...Ch. 2 - Describe the differences between brittle and...Ch. 2 - What is hardness? Explain.
Ch. 2 - Describe the features of a Rockwell hardness test.Ch. 2 - What is a Leeb test? How is it different from a...Ch. 2 - Differentiate between stress relaxation and creep.Ch. 2 - Describe the difference between elastic and...Ch. 2 - Explain what uniform elongation means in tension...Ch. 2 - Describe the difference between deformation rate...Ch. 2 - Describe the difficulties involved in conducting a...Ch. 2 - What is Hookes law? Youngs modulus? Poissons...Ch. 2 - Describe the difference between transgranular and...Ch. 2 - What is the reason that yield strength is...Ch. 2 - Why does the fatigue strength of a specimen or...Ch. 2 - If striations are observed under microscopic...Ch. 2 - What is an Izod test? Why are Izod tests useful?Ch. 2 - Why does temperature increase during plastic...Ch. 2 - What is residual stress? How can residual stresses...Ch. 2 - On the same scale for stress, the tensile true...Ch. 2 - What are the similarities and differences between...Ch. 2 - Can a material have a negative Poissons ratio?...Ch. 2 - It has been stated that the higher the value of m,...Ch. 2 - Explain why materials with high m values, such as...Ch. 2 - With a simple sketch, explain whether it is...Ch. 2 - Explain why the difference between engineering...Ch. 2 - Consider an elastomer, such as a rubber band. This...Ch. 2 - If a material (such as aluminum) does not have an...Ch. 2 - What role, if any, does friction play in a...Ch. 2 - Which hardness tests and scales would you use for...Ch. 2 - Consider the circumstance where a Vickers hardness...Ch. 2 - Which of the two tests, tension or compression,...Ch. 2 - List and explain briefly the conditions that...Ch. 2 - List the factors that you would consider in...Ch. 2 - On the basis of Fig. 2.5, can you calculate the...Ch. 2 - If a metal tension-test specimen is rapidly pulled...Ch. 2 - Comment on your observations regarding the...Ch. 2 - Will the disk test be applicable to a ductile...Ch. 2 - What hardness test is suitable for determining the...Ch. 2 - Wire rope consists of many wires that bend and...Ch. 2 - A statistical sampling of Rockwell C hardness...Ch. 2 - In a Brinell hardness test, the resulting...Ch. 2 - Some coatings are extremely thinsome as thin as a...Ch. 2 - Select an appropriate hardness test for each of...Ch. 2 - A paper clip is made of wire 0.5 mm in diameter....Ch. 2 - A 250-mm-long strip of metal is stretched in two...Ch. 2 - Identify the two materials in Fig. 2.5 that have...Ch. 2 - Plot the ultimate strength vs. stiffness for the...Ch. 2 - If you remove the layer of material ad from the...Ch. 2 - Prove that the true strain at necking equals the...Ch. 2 - Percent elongation is always defined in terms of...Ch. 2 - You are given the K and n values of two different...Ch. 2 - A cable is made of two strands of different...Ch. 2 - On the basis of the information given in Fig. 2.5,...Ch. 2 - In a disk test performed on a specimen 1.00 in. in...Ch. 2 - A piece of steel has a hardness of 300 HB....Ch. 2 - A metal has the following properties: UTS = 70,000...Ch. 2 - Using only Fig. 2.5, calculate the maximum load in...Ch. 2 - Estimate the modulus of resilience for a highly...Ch. 2 - A metal has a strength coefficient K = 100,000 psi...Ch. 2 - Plot the true stresstrue strain curves for the...Ch. 2 - The design specification for a metal requires a...Ch. 2 - Calculate the major and minor pyramid angles for a...Ch. 2 - If a material has a target hardness of 300 HB,...Ch. 2 - A Rockwell A test was conducted on a material and...Ch. 2 - For a cold-drawn 0.5% carbon steel, will a...Ch. 2 - A material is tested in tension. Over a 1-in. gage...Ch. 2 - A horizontal rigid bar cc is subjecting specimen a...Ch. 2 - List and explain the desirable mechanical...Ch. 2 - When making a hamburger, you may have observed the...Ch. 2 - An inexpensive claylike material called Silly...Ch. 2 - In tension testing of specimens, mechanical and...Ch. 2 - Demonstrate the impact toughness of a piece of...Ch. 2 - Using a large rubber band and a set of weights,...Ch. 2 - Find or prepare some solid circular pieces of...Ch. 2 - Take several rubber bands and pull them at...Ch. 2 - Devise a simple fixture for conducting the bend...Ch. 2 - By pressing a small ball bearing against the top...Ch. 2 - Describe your observations regarding Fig. 2.14c.Ch. 2 - Embed a small steel ball in a soft block of...Ch. 2 - Devise a simple experiment, and perform tests on...Ch. 2 - Obtain some solid and some tubular metal pieces,...Ch. 2 - Explain how you would obtain an estimate of the...Ch. 2 - Without using the words stress or strain, define...Ch. 2 - We know that it is relatively easy to subject a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A cable is made of material of (K = 60,000 psi, n = 0.5) Calculate the true and engineering UTS for this cable prior to necking.σ= Kεnarrow_forwardA bar of 50 mm diameter is subjected to a pull of 150 kN. The measured extension on gauge length of 400 mm is 0.6 mm and the change in diameter is 0.005 mm. Calculate: (i) Young’s Modulus, (ii) Poisson’s ratio (iii) Bulk Modulus and (iv) Shear Modulus.arrow_forwardWhat minimum diameter is required for the wire?arrow_forward
- Problem Solving: Show your solution 1. A string 4 mm in diameter has original length 2 m. The string is pulled by a force of 200 N. If the final length of the spring is 2.02 m, determine : (a) stress (b) strain (c) Young’s modulus 2. A string has a diameter of 1 cm and the original length of 2 m. The string is pulled by a force of 200 N. Determine the change in length of the string! Young’s modulus of the string = 5 x 109 N/m2arrow_forwardDetermine the width and thickness of the leaves (in mm) of a leaf spring using the following specifications: Total load = 140 kN; Number of springs supporting the load = 4; Maximum number of leaves = 10; Span of the spring = 1000 mm; Permissible deflection = 80 mm; Modulus of elasticity, E = 200 kN/mm2; and allowable stress in spring material is 600 MPa.arrow_forwardsolve asap with complete explanationarrow_forward
- #5arrow_forwardTwo links are connected by a single pin and a tensile force F is applied. The links and the pin are made from Aluminum(sigma_y = 35ksi and T_y = 20ksi). The dimension of the link is 5 inch high by 0.5 inch thick. Find the optimal diameter for the pin and the maximum force,F that can be applied to the linkage before incuring permanent deformation.arrow_forwardIf an isotropic material has a Young's modulus of 120 Gpa and a Poisson's ratio of 0.3, calculate its shear modulus. Select one: O G= 25 Gpa O G= 46 Gpa O G = 77 Gpa O G= 39 Gpa O G= 29 Gpaarrow_forward
- A helical spring is made by wrapping wire 25mmØ around a forming cylinder 175mm in diameter. (a)Compute the number of turns required to permit a stretch of 100mm without exceeding a shear stress of 100MPa. Assume G = 82,800 GPa (b) If the number of turns is 10 and shearing stress is limited to 90MPa, what is the diameter of the wire? (c) If helical spring is made by wrapping wire 20mm in diameter, compute the number of turns? Is the number of turns increase or decrease when diameter decrease from 25mm to 20mm?arrow_forwardA vertical close-coiled helical compression spring must have a stiffness of 900 N/m under a load of 45 N and the maximum shear stress induced due to this load is to be 120 MPa. With the spring fully compressed the vertical height over the coils is 45 mm. Calculate (a) the wire diameter; (b) the mean coil diameter; and (c) the number of coils (G = 40 GPa)arrow_forwardProblem 6: A circular metal rod of diameter 1 cm is loaded in tension. The extension of a 25 cm is measured accurately and is 0.0227 cm when the tensile is 5kN. Estimate the value of Young's modulus of the metal.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Stresses Due to Fluctuating Loads Introduction - Design Against Fluctuating Loads - Machine Design 1; Author: Ekeeda;https://www.youtube.com/watch?v=3FBmQXfP_eE;License: Standard Youtube License