Textbook Question
Chapter 16, Problem 64SDP
Metal cans are either two-piece (in which the bottom and sides are integral) or three-piece (in which the sides, the bottom, and the top are each separate pieces). For a three-piece can, should the vertical seam in the can body be (a) in the rolling direction, (b) normal to the rolling direction, or (c) oblique to the rolling direction? Prove your answer.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Please answer all parts
please answer to both of these parts of the question, thanks
(a) Explain the advantage of corner radii of punch and die in Sheet Metal Drawing Process.
(b) Explain the disadvantages of Tube Drawing process in which mandrel is not used.
5. Determine the maximum possible reduction for cold rolling a 300mm thick slab when μ =
0.08, and roll diameter is 600mm. What is the maximum reduction on the same mill for
hot rolling when μ = 0.05.
6. Explain different types of defects which are possible in the welding process.
Chapter 16 Solutions
Manufacturing Engineering & Technology
Ch. 16 - How does sheet-metal forming differ from rolling,...Ch. 16 - What causes burrs? How can they be reduced or...Ch. 16 - Prob. 3RQCh. 16 - Describe the difference between compound,...Ch. 16 - Describe the characteristics of sheet metals that...Ch. 16 - Describe the features of forming-limit diagrams...Ch. 16 - List the properties of materials that influence...Ch. 16 - Give one specific application for each of the...Ch. 16 - Why do tubes buckle when bent? What is the effect...Ch. 16 - Define normal anisotropy, and explain why it is...
Ch. 16 - Describe earing and why it occurs.Ch. 16 - What are the advantages of rubber forming? Which...Ch. 16 - Explain the difference between deep drawing and...Ch. 16 - How is roll forming fundamentally different from...Ch. 16 - What is nesting? What is its significance?Ch. 16 - Describe the differences between compound,...Ch. 16 - What is microforming?Ch. 16 - Explain the advantages of superplastic forming.Ch. 16 - What is hot stamping? For what materials is it...Ch. 16 - What is springback? What is negative springback?Ch. 16 - Explain the differences that you have observed...Ch. 16 - Take any three topics from Chapter 2, and, with...Ch. 16 - Do the same as for Problem 16.22, but for Chapter...Ch. 16 - Identify the material and process variables that...Ch. 16 - Explain why springback in bending depends on yield...Ch. 16 - Explain why cupping tests may not predict well the...Ch. 16 - Identify the factors that influence the...Ch. 16 - Why are the beads in Fig. 16.36b placed in those...Ch. 16 - A general rule for dimensional relationships for...Ch. 16 - Section 16.2 stated that the punch stripping force...Ch. 16 - Is it possible to have ironing take place in an...Ch. 16 - Note the roughness of the periphery of the flanged...Ch. 16 - What recommendations would you make in order to...Ch. 16 - It has been stated that the quality of the sheared...Ch. 16 - Give several specific examples from this chapter...Ch. 16 - As you can see, some of the operations described...Ch. 16 - Through changes in clamping or die design, it is...Ch. 16 - How would you produce the part shown in Fig....Ch. 16 - It has been stated that the thicker the sheet...Ch. 16 - Prob. 41QTPCh. 16 - Calculate the value of R in Problem 16.41. Will...Ch. 16 - Estimate the limiting drawing ratio for the...Ch. 16 - Using Eq. (16.15) and the K value for TNT, plot...Ch. 16 - Section 16.5 states that the k values in bend...Ch. 16 - For explosive forming, calculate the peak pressure...Ch. 16 - Measure the respective areas of the solid outlines...Ch. 16 - Plot Eq. (16.6) in terms of the elastic modulus,...Ch. 16 - What is the minimum bend radius for a 1.0-mm-thick...Ch. 16 - Survey the technical literature and explain the...Ch. 16 - Using the data in Table 16.3 and referring to Eq....Ch. 16 - What is the force required to punch a square hole...Ch. 16 - In Case Study 16.2, it was stated that the reason...Ch. 16 - A cup is being drawn from a sheet metal that has a...Ch. 16 - Prob. 55QTPCh. 16 - Figure P16.57 shows a parabolic profile that will...Ch. 16 - Prob. 59SDPCh. 16 - Consider several shapes to be blanked from a large...Ch. 16 - Prob. 61SDPCh. 16 - Many axisymmetric missile bodies are made by...Ch. 16 - Metal cans are either two-piece (in which the...Ch. 16 - The design shown in Fig. P16.65 is proposed for a...Ch. 16 - Suggest consumer-product designs that could...Ch. 16 - How would you produce the part shown in Fig. 16.44...Ch. 16 - Using a ball-peen hammer, strike the surface of...Ch. 16 - Inspect a common paper punch and observe the shape...Ch. 16 - Obtain an aluminum beverage can and slit it in...Ch. 16 - Prob. 71SDPCh. 16 - Prob. 73SDPCh. 16 - On the basis of experiments, it has been suggested...Ch. 16 - Design a box that will contain a 4-in. 6-in. ...Ch. 16 - Repeat Problem 16.77, but design the box from a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A 10 mm thick plate is rolled to 7 mm thick in a rolling mill using 1000 mm diameter rigid rolls. The neutral point is located at an angle of 0.3 times the bite angle from the exit. What will be the thickness of the plate at the neutral point.arrow_forwardExplain briefly the relationship between the load-stroke in open die forging as illustrated in the figures bellow. Take in consideration the effect of coefficient of friction.arrow_forwardWhat is the difference between plate and sheet material?arrow_forward
- A compound die is used to blank and punch a large washer out of 6061ST aluminum alloy sheet stock 3.2 mm thick. The outside diameter of the washer is 25.0 mm, and the inside diameter is 12.0 mm. Determine (a) the punch and die sizes for the blanking and punching operations, (b) the force required to perform the blanking and punching operation under the following conditions: (a) blanking and punching occur simultaneously and (b) the punches are staggered so that punching occurs first, then blanking. The aluminum has a tensile strength = 350 MPa.arrow_forwardA solid cylinder of diameter 100 mm and height 50 mm is forged between two frictionless flat dies to a height of 25 mm. What is the percentage change in diameter?arrow_forwardExplain the basic operation of open-die forging. Use sketches to assist the explanation.arrow_forward
- Question 5 5.1 Calculate the final bend radius for a 3 mm thick 6061 T6 aluminum plate that is formed using a forming punch with an 8 mm radius, as shown in Figure 3. R 8 Figure 3: Bend profile that is formed using a V-block die and a punch with a 8 mm radius 5.2 Explain why there would be a difference between the initial and final bend radius during the bending process and how this occurrence depends upon material properties, sheet thickness and the bend radius.arrow_forwardList the types of forming. Your listing should be based on workpiece temperature. Write down only three advantages per each type.arrow_forward4) In the deep drawing of cups, blanks show a tendency to wrinkle up around the periphery (flange). The most likely cause and remedy of the phenomenon are respectively: Buckling due to circumferential compression; Increase blank holder pressure. High blank holder pressure and high friction; Reduce blank holder pressure and apply lubricant. High temperature causing an increase in circumferential length; Apply coolant to blank. Buckling due to circumferential compression; decrease blank holder pressure.arrow_forward
- Please Identify the correct answer along with concise reasoning( Step-by-step is preferred) on why the selected option is the right answer. Please also explain concisely why the remaining options are incorrect. I'll rate for the response positively if the answer is correct. Thx!arrow_forwardA cup of 5o mm diameter and 20 mm height is to be produced by drawing from a 1.5 mm thick sheet metal. What is the maximum drawing force ? If ultimate tensile strength of metal is 650 MPa.arrow_forwardQuestion 2. It is reduced to 80 mm with forging by stacking a part with a height of 120 mm and a diameter of 75 mm. The friction coefficient between the workpiece and the mold is 0.13. The flow curve of the workpiece is defined by a strength coefficient of 165 MPa and a ping-top of 0.24. Calculate the force during the process at the moments given below and obtain the force-workpiece height graph (1) as soon as it reaches the flow point (flow unit shape change = 0.002), (2) height h = 115 mm, (3) height h = 110 mm, (4) height h = 105 mm, (5) height h = 100 mm, (6) height h = 95 mm, (7) height h = 90 mm, (8) height h = 85 mm, (9) height h = 80 mm,arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage Learning
Welding: Principles and Applications (MindTap Cou...
Mechanical Engineering
ISBN:9781305494695
Author:Larry Jeffus
Publisher:Cengage Learning
Types of Manufacturing Process | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=koULXptaBTs;License: Standard Youtube License