Textbook Question
Chapter 10, Problem 56SDP
The fluidity test shown in Fig. 10.9 illustrates only the principle of this test. Design a setup for such a test, showing the type of materials and the equipment to be used. Explain the method by which you would determine the length of the solidified metal in the spiral passage.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A component is sand casted in pure aluminum. The level of the metal inside a
pouring basin is 215 mm above the level of the metal in the mould. For a
viscosity value of 0.0017 Ns/m² and a circular runner with a diameter of 11 mm,
calculate:
2.1
The velocity and rate of flow of the metal into the mould.
2.2 What effect does turbulent flow in a gating system have on the casting?
2.3 Which measures can be implemented to reduce turbulent flow?
Solve in digital format please, to copy in word
Investigate and describe the different types of fluidization.
Mention at least two examples of each, as well as advantages and/or disadvantages (if they exist)
Pure aluminium is poured into a sand mold. The metal level in the pouring basin is 203.2mm above the metal level in the mold, and the runner is circular with a 7.62 mm diameter.What is the velocity and the rate of flow of the metal into the mold? Is the flow turbulent orlaminar? Note that pure aluminum has a density of 2700 kg/m3and a viscosity of 0.004Ns/m
Chapter 10 Solutions
Manufacturing Engineering & Technology
Ch. 10 - Explain why casting is an important manufacturing...Ch. 10 - Why do most metals shrink when they are cast?Ch. 10 - What are the differences between the...Ch. 10 - What are dendrites? Why are they called so?Ch. 10 - Describe the difference between short and long...Ch. 10 - What is superheat? Is it important? What are the...Ch. 10 - Define shrinkage and porosity. How can you tell...Ch. 10 - What is the function of chills? What are they made...Ch. 10 - Why is the Reynolds number important in casting?Ch. 10 - What is a sprue? What shape should a sprue have if...
Ch. 10 - How is fluidity defined? Why is it important?Ch. 10 - Explain the reasons for hot tearing in castings.Ch. 10 - Why is it important to remove dross or slag during...Ch. 10 - Why is Bernoullis equation important in casting?Ch. 10 - Describe thixocasting and rheocasting.Ch. 10 - What is Chvorinovs Rule?Ch. 10 - How is a blister related to a scab?Ch. 10 - Is there porosity in a chocolate bar? In an ice...Ch. 10 - Describe the stages involved in the contraction of...Ch. 10 - Explain the effects of mold materials on fluid...Ch. 10 - It is known that pouring metal at a high rate into...Ch. 10 - Describe the events depicted in Fig. 10.5.Ch. 10 - Would you be concerned about the fact that...Ch. 10 - Review Fig. 10.8 and make a summary, explaining...Ch. 10 - Make a sketch of volume vs. temperature for a...Ch. 10 - What practical demonstrations can you suggest to...Ch. 10 - Explain why a casting may have to be subjected to...Ch. 10 - List and explain the reasons why porosity can...Ch. 10 - Why does porosity have detrimental effects on the...Ch. 10 - A spoked handwheel is to be cast in gray iron. In...Ch. 10 - Which of the following considerations are...Ch. 10 - Explain why the constant C in Eq. (10.7) depends...Ch. 10 - Are external chills as effective as internal...Ch. 10 - Explain why, as shown in Table 10.1, gray cast...Ch. 10 - Referring to Fig. 10.11, explain why internal...Ch. 10 - Note the shape of the two risers shown in Fig....Ch. 10 - Is there any difference in the tendency for...Ch. 10 - What is the influence of the cross-sectional area...Ch. 10 - It has long been observed that (a) low pouring...Ch. 10 - In casting metal alloys, what would you expect to...Ch. 10 - If you inspect a typical cube of ice, you are...Ch. 10 - How can you tell whether cavities in a casting are...Ch. 10 - Describe the drawbacks to having a riser that is...Ch. 10 - Reproduce Fig. 10.2 for a casting that is...Ch. 10 - List the process variables that affect the...Ch. 10 - Assume that you have a method of measuring...Ch. 10 - A round casting is 0.2 m (7.9 in.) in diameter and...Ch. 10 - A cylinder with a diameter of 2.0 in. and a height...Ch. 10 - The constant C in Chvorinovs rule is given as 2.5...Ch. 10 - Pure copper is poured into a sand mold. The metal...Ch. 10 - For the sprue described in Problem 10.58, what...Ch. 10 - When designing patterns for casting, pattern...Ch. 10 - Can you devise fluidity tests other than that...Ch. 10 - Figure P10.55 indicates various defects and...Ch. 10 - The fluidity test shown in Fig. 10.9 illustrates...Ch. 10 - Utilizing the equipment and materials available in...Ch. 10 - One method of relieving stress concentrations in a...Ch. 10 - Describe the effects on mold design, including the...Ch. 10 - Small amounts of slag often persist after skimming...Ch. 10 - Design an experiment to measure the constants C...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Can someone please help me to answer the following question completely. PLEASE AND THANK YOU!!!arrow_forwardA machinist was tasked to insert an aluminum piston into a steel cylinder. The inside diameters of the cylinder and of the piston are 0.500 m and 0.4998 m, respectively, at 25OC. To what temperature must they be heated to obtain a perfect fit?arrow_forwardthis cylinder has a rod inside, around the rod there is paraffin wax that will expand, I want to know how to reduce the thickness of this cylinder. However, I don't know what formulas I need to be able to do this and how to do the calculations. Please can you make an example with the data you choose to have an example of how to do this step by step? Thank you Also keep in mind that the wax is expanding by an induction coil, and the heat is happening around the cylinder. And the thickness of the stainless steel cylinder has to be thin but not so thin that it causes a pressure problem.arrow_forward
- Can i get help with these questionsarrow_forwarda riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.arrow_forwardA riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.arrow_forward
- Step by step solution pleasearrow_forwardAn open, clean glass tube, having a diameter of 3 mm, is inserted vertically into a dish of mercury. How far (the magnitude in mm) will the column of mercury in the tube be depressed? Use Table 2-4 from the Fluid Properties – Part III. Assume wetting angle for mercury-glass in contact with air to be 130°. Take specific gravity of mercury as 13.6.arrow_forwardA riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 100 mm, width = 50 mm, and thickness = 10 mm. If the total solidification time of the casting itself is known to be 2.5 min, determine the diameter of the riser so that it will take 20% longer for the riser to solidify. %3D %3!arrow_forward
- A mould having dimensions 100 mm x 90 mm x 20 mm is filled with molten metal through a gate with height h and CS area A, the mould filling time is t1. The height is now quadrupled and the crosssectional area is halved. The corresponding filling time is t2 . What is the ratio t2/t1 ?arrow_forwardisufficient amount of pure copper is to be heated for casting a large plate in an open mold. The plate has dimensions: length = 20 in, width 10 in, and thickness 3 in. Compute the amount of heat that must be added to the metal to heat it to a temperature of 2150°F for pouring. Assume that the amount of metal heated will be 10% more than what is needed to fill the mold cavity. Properties of the metal are: density = 0.324 lbm/in3, melting point = 1981°F, specific heat of the metal = 0.093 Btu/lbm-F in the solid state and 0.090 Btu/lbm-F in the liquid state, and heat of fusion = 80 Btu/lbmarrow_forward-450.76 for parts (c) and (d) are incorrect.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Properties of Fluids: The Basics; Author: Swanson Flo;https://www.youtube.com/watch?v=TgD3nEO1iCA;License: Standard YouTube License, CC-BY
Fluid Mechanics-Lecture-1_Introduction & Basic Concepts; Author: OOkul - UPSC & SSC Exams;https://www.youtube.com/watch?v=6bZodDnmE0o;License: Standard Youtube License