Textbook Question
Chapter 10, Problem 49QTP
The constant C in Chvorinov’s rule is given as 2.5 s/mm2, and is used to produce a cylindrical casting with a diameter of 50 mm and height of 125 mm. Estimate the time for the casting to fully solidify. The mold can be broken safely when the solidified shell is at least 20 mm. Assuming that the cylinder cools evenly, how much time must transpire after pouring the molten metal before the mold can be broken?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate,
with length = 100 mm, width = 50 mm, and thickness = 10 mm. If the total solidification time of the casting
itself is known to be 2.5 min, determine the diameter of the riser so that it will take 20% longer for the riser
to solidify.
%3D
%3!
I am in a hurry, I need the answer as soon as possible, please help.
A flat plate is to be cast in an open mold
whose bottom has a square shape that is 200
mm by 200 mm. The mold is 40 mm deep. A
total of 106 mm3 of molten aluminum is
poured into the mold. Solidification
shrinkage is known to be 6.0%. The linear
shrinkage due to thermal contraction after
solidification is 1.3%. If the availability of
molten metal in the mold allows the square
shape of the cast plate to maintain its 200
mm by 200 mm dimensions until
solidification is completed, determine the
final dimensions of the plate.
Chapter 10 Solutions
Manufacturing Engineering & Technology
Ch. 10 - Explain why casting is an important manufacturing...Ch. 10 - Why do most metals shrink when they are cast?Ch. 10 - What are the differences between the...Ch. 10 - What are dendrites? Why are they called so?Ch. 10 - Describe the difference between short and long...Ch. 10 - What is superheat? Is it important? What are the...Ch. 10 - Define shrinkage and porosity. How can you tell...Ch. 10 - What is the function of chills? What are they made...Ch. 10 - Why is the Reynolds number important in casting?Ch. 10 - What is a sprue? What shape should a sprue have if...
Ch. 10 - How is fluidity defined? Why is it important?Ch. 10 - Explain the reasons for hot tearing in castings.Ch. 10 - Why is it important to remove dross or slag during...Ch. 10 - Why is Bernoullis equation important in casting?Ch. 10 - Describe thixocasting and rheocasting.Ch. 10 - What is Chvorinovs Rule?Ch. 10 - How is a blister related to a scab?Ch. 10 - Is there porosity in a chocolate bar? In an ice...Ch. 10 - Describe the stages involved in the contraction of...Ch. 10 - Explain the effects of mold materials on fluid...Ch. 10 - It is known that pouring metal at a high rate into...Ch. 10 - Describe the events depicted in Fig. 10.5.Ch. 10 - Would you be concerned about the fact that...Ch. 10 - Review Fig. 10.8 and make a summary, explaining...Ch. 10 - Make a sketch of volume vs. temperature for a...Ch. 10 - What practical demonstrations can you suggest to...Ch. 10 - Explain why a casting may have to be subjected to...Ch. 10 - List and explain the reasons why porosity can...Ch. 10 - Why does porosity have detrimental effects on the...Ch. 10 - A spoked handwheel is to be cast in gray iron. In...Ch. 10 - Which of the following considerations are...Ch. 10 - Explain why the constant C in Eq. (10.7) depends...Ch. 10 - Are external chills as effective as internal...Ch. 10 - Explain why, as shown in Table 10.1, gray cast...Ch. 10 - Referring to Fig. 10.11, explain why internal...Ch. 10 - Note the shape of the two risers shown in Fig....Ch. 10 - Is there any difference in the tendency for...Ch. 10 - What is the influence of the cross-sectional area...Ch. 10 - It has long been observed that (a) low pouring...Ch. 10 - In casting metal alloys, what would you expect to...Ch. 10 - If you inspect a typical cube of ice, you are...Ch. 10 - How can you tell whether cavities in a casting are...Ch. 10 - Describe the drawbacks to having a riser that is...Ch. 10 - Reproduce Fig. 10.2 for a casting that is...Ch. 10 - List the process variables that affect the...Ch. 10 - Assume that you have a method of measuring...Ch. 10 - A round casting is 0.2 m (7.9 in.) in diameter and...Ch. 10 - A cylinder with a diameter of 2.0 in. and a height...Ch. 10 - The constant C in Chvorinovs rule is given as 2.5...Ch. 10 - Pure copper is poured into a sand mold. The metal...Ch. 10 - For the sprue described in Problem 10.58, what...Ch. 10 - When designing patterns for casting, pattern...Ch. 10 - Can you devise fluidity tests other than that...Ch. 10 - Figure P10.55 indicates various defects and...Ch. 10 - The fluidity test shown in Fig. 10.9 illustrates...Ch. 10 - Utilizing the equipment and materials available in...Ch. 10 - One method of relieving stress concentrations in a...Ch. 10 - Describe the effects on mold design, including the...Ch. 10 - Small amounts of slag often persist after skimming...Ch. 10 - Design an experiment to measure the constants C...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.arrow_forwardManufacturing Processesarrow_forwardParvinbhaiarrow_forward
- (9,00 Puanlar) 36 - A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 25 cm, width = 15 cm, and thickness = 2,5 cm. If the total solidification time of the casting itself is known to be 4,5 min, determine the diameter of the riser so that it will take 2596 longer for the riser to solidify. Riser volume: V-(nD³/6 (D=diameter) Riser area: A-TD2 Casting volume: V-L-W-t (L-Length, W=width, t=thickness)arrow_forward(9,00 Puanlar) A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with 8- length 50 cm, width = 35 cm, and thickness = 4 cm. If the total solidification time of the casting itself is known to be 7,5 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify. %3D Riser volume: V3(TD3)/6(D%3Ddiameter) Riser area: A=TD2 Casting volume: V-L-Wt (L-Length, W=width, t-thickness) a) 8,41 cm b) O 7,34 cm c) 6.62 cm 11,46 cm Boş bırak KÖnceki 8/43 Sonraki> Каpatarrow_forwardAnswer this broadly.arrow_forward
- Doarrow_forwardFor sand-casting a steel rectangular plate with dimensions 80mm×120mm×20mm, a cylindrical riser has to be designed. The height of the riser is equal to its diameter. The total solidification time for the casting is 2 minutes. In Chvorinov‟s law for the estimation of the total solidification time, exponent is to be taken as 2. For a solidification time of 3 minutes in the riser, the diameter (in mm) of the riser is ____arrow_forwardA flat plate is to be cast in an open mold whose bottom has a square shape of 12.5 cm by 12.5 cm. The mold is 7.0 cm deep. A total of 350 cm³ of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.25%, which is a volumetric contraction, not a linear contraction. Table 7.1 lists the linear shrinkage due to thermal contraction after solidification. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its square dimension until solidification is completed, determine the final dimensions (width and height) of the plate.arrow_forward
- TYPED ANSWERarrow_forwardI am in a hurry, I need the answer as soon as possible, please help.arrow_forward2. A 10-inch x 10-inch x 0.75-inch plate casting is produced with a steel alloy with p = 0.28 lb/in³ (= 7.75 g/cm³). Two third of the steel plate casting volume should be added more into the original one, and all molten metal should be poured in 10 seconds. The cylindrical, tapered sprue height is 4 inches. The sprue has a cylindrical base and is connected to two runners. Each runner with a square vertical cross-section is connected to two gates. The gate has a rectangular vertical cross-section, and its width is three times the height. 0.75 inch Cylindrical Square Rectangular sprue base gate runner Steel alloy casting Note that drawings are not to actual scale or ratios. Area of a sprue base's horizontal cross-section The ratio of the cylindrical sprue base's horizontal cross-sectional area to the sum of two runners' vertical cross-sectional areas to the sum of four gates' vertical cross-sectional areas is 1:2:3. The sum of areas of two runners' vertical cross-sections 1 2 Note that…arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Casting Metal: the Basics; Author: Casting the Future;https://www.youtube.com/watch?v=2CIcvB72dmk;License: Standard youtube license