Textbook Question
Chapter 8.15, Problem 46SEP
In the Pb–Sn phase diagram (Fig. 8.12), answer the following questions:
- a. What is α? (Explain in detail including atomic structure.) What is β?
- b. What is the maximum solubility of Sn in α? At what temperature?
- c. What happens to the α in part b if it is cooled to room temperature?
- d. What is the maximum solubility of Sn in liquid metal at the lowest possible temperature? What is that temperature?
- e. What is the solubility limit of Sn in α when liquid is present? (This will be a range.)
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A lead-tin (Pb-Sn) alloy of composition 30 wt % Sn and 70 wt % Pb is slowly heated from a temperature of 140 OC. Refer to the phase diagram provided in Figure 1 and answer the following.
(i) At what temperature does the first liquid phase form?
(ii) What is the composition of this liquid phase?
(iii) At what temperature does complete melting of the alloy occur?
(iv) What is the composition of the last solid remaining prior to complete melting?
The Al-Si phase diagram is given below.
Consider 1 kg of an Al-Si alloy with 80 wt % silicon. The sample is slowly heated up from room temperature to 1400 oC. Upon cooling,
(i) At what temperature will the liquid start to solidify and what is the composition of the first solid formed?
(ii) At what temperature will you have an equal amount of solid and liquid phase? And what is the composition of the liquid phase at this temperature?
The Al-Si phase diagram is given below.
Consider 1 kg of an Al-Si alloy with 80 wt % silicon. The sample is slowly heated up from room temperature to 1400 oC. Upon cooling,
(a) At what temperature will the liquid start to solidify and what is the composition of the first solid formed?
(b) At what temperature will you have an equal amount of solid and liquid phase? And what is the composition of the liquid phase at this temperature?
Chapter 8 Solutions
Foundations of Materials Science and Engineering
Ch. 8.15 - Define (a) a phase in a material and (b) a phase...Ch. 8.15 - In the pure water pressure-temperature equilibrium...Ch. 8.15 - How many triple points are there in the pure iron...Ch. 8.15 - Write the equation for the Gibbs phase rule and...Ch. 8.15 - Refer to the pressuretemperature equilibrium phase...Ch. 8.15 - (a) What is a cooling curve? (b) What type of...Ch. 8.15 - Prob. 7KCPCh. 8.15 - What is an alloy? What is the difference between...Ch. 8.15 - Prob. 9KCPCh. 8.15 - What is the significance of the liquidus curve?...
Ch. 8.15 - Prob. 11KCPCh. 8.15 - Prob. 12KCPCh. 8.15 - Prob. 13KCPCh. 8.15 - Describe the mechanism that produces the...Ch. 8.15 - Can coring and surrounding occur in a...Ch. 8.15 - What is a monotectic invariant reaction? How is...Ch. 8.15 - Write equations for the following invariant...Ch. 8.15 - How are eutectic and eutectoid reactions similar?...Ch. 8.15 - Distinguish between (a) a terminal phase and (b)...Ch. 8.15 - Distinguish between (a) an intermediate phase and...Ch. 8.15 - What is the difference between a congruently...Ch. 8.15 - Consider an alloy containing 70 wt% Ni and 30 wt%...Ch. 8.15 - Consider the binary eutectic coppersilver phase...Ch. 8.15 - If 500 g of a 40 wt% Ag60 wt% Cu alloy is slowly...Ch. 8.15 - A lead-tin (PbSn) alloy consists of 60 wt%...Ch. 8.15 - A PbSn alloy (Fig. 8.12) contains 40 wt% and 60...Ch. 8.15 - An alloy of 30 wt% Pb70 wt% Sn is slowly cooled...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - In the copperlead (CuPb) system (Fig. 8.24) for an...Ch. 8.15 - For an alloy of Cu70 wt% Pb (Fig. 8.24), determine...Ch. 8.15 - What is the average composition (weight percent)...Ch. 8.15 - Consider an Fe4.2 wt% Ni alloy (Fig. 8.17) that is...Ch. 8.15 - Consider an Fe5.0 wt% Ni alloy (Fig. 8.17) that is...Ch. 8.15 - Determine the weight percent and composition in...Ch. 8.15 - Determine the composition in weight percent of the...Ch. 8.15 - Draw, schematically, the liquidus and the solidus...Ch. 8.15 - Consider the CuZn phase diagram of Figure 8.26. a....Ch. 8.15 - Consider the nickelvanadium phase diagram of...Ch. 8.15 - Consider the titaniumaluminum phase diagram of...Ch. 8.15 - What is the composition of point y in Figure...Ch. 8.15 - In Figure 8.12, determine the degree of freedom,...Ch. 8.15 - The cooling curve of an unknown metal shows a...Ch. 8.15 - In the PbSn phase diagram (Fig. 8.12), answer the...Ch. 8.15 - Based on the CuAg phase diagram in Figure P8.23,...Ch. 8.15 - Based on the PdAg phase diagram in Figure EP 8.3,...Ch. 8.15 - Prob. 49SEPCh. 8.15 - Derive the lever rule for the amount in weight...Ch. 8.15 - Based on the AlNi phase diagram given in Figure...Ch. 8.15 - Prob. 52SEPCh. 8.15 - Based on the Al2O3SiO2 phase diagram in Figure...Ch. 8.15 - (a) Design a CuNi alloy that will be completely...Ch. 8.15 - Prob. 55SEPCh. 8.15 - Given that Pb and Sn have similar tensile...Ch. 8.15 - Consider the sugarwater phase diagram shown in...Ch. 8.15 - In Figure P8.57, if 60 g of water and 140 g of...Ch. 8.15 - In Figure P8.57, if 30 g of water and 170 g of...Ch. 8.15 - At 80C, if the wt% of sugar is 80%, (a) what...Ch. 8.15 - (a) Based on the phase diagram in Figure P8.61,...Ch. 8.15 - Referring to Figure P8.61. explain what happens as...Ch. 8.15 - Referring to Figure P8.61, (a) explain what...Ch. 8.15 - Using Figure P8.40, explain what the phase diagram...Ch. 8.15 - Using Figure P8.40. explain why, according to the...Ch. 8.15 - (a) In the TiAl phase diagram. Figure P8.42, what...Ch. 8.15 - Draw an approximate hypothetical phase diagram for...Ch. 8.15 - Draw the hypothetical phase diagram for a binary...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- BINARY PHASE DIAGRAMS Please only answer parts d and e as the rest have been solved. Show full detailed explanation to answers with diagrams if necessary a)(i) What is the melting point of pure Mg?(ii) What is the maximum solubility of Mg in Pb and at what temperaturedoes this occur? (b) A 50 wt.% Pb-50wt% Mg alloy is slowly cooled from 700 °C to 400 °C.(i) At what temperature does the first solid phase form?(ii) What is the composition of this solid phase?(iii) At what temperature does all the liquid solidify?(iv) What is the composition of the last remaining liquid phase?(v) What is the freezing range? (c) What is the mass fraction of solid and liquid of a 60 wt.% Mg alloy at atemperature of 500 °C.(d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A Mg-Pb alloy of mass 5.5 kg has a composition just slightly below thesolubility limit of 200 °C.(i) What mass of lead is in the alloy?(ii) If the alloy is heated to 350 °C how much more lead can be dissolvedin…arrow_forwardPlease helparrow_forwardAccording to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105arrow_forward
- Question: Construct the hypothetical phase diagram for metals A and B between room temperature (20°C) and 700°C given the following information: The melting temperature of metal A is 480°C. The maximum solubility of B in A is 4 wt% B, which occurs at 420°C. The solubility of B in A at room temperature is 0 wt% B. One eutectic occurs at 420°C and 18 wt% B–82 wt% A. A second eutectic occurs at 475°C and 42 wt% B–58 wt% A. The intermetallic compound AB exists at a composition of 30 wt% B–70 wt% A, and melts congruently at 525°C. The melting temperature of metal B is 600°C. The maximum solubility of A in B is 13 wt% A, which occurs at 475°C. ● The solubility of A in B at room temperature is 3 wt% A.arrow_forwardAn alloy consisting of completely soluble cadmium (Cd) and zinc (Zn) in the liquid state, but neither of them dissolves in each other in the solid state. the table shown below shows the solidification temperatures for various alloys of cadmium and zinc. 1. Draw the equilibrium diagram according to the information given and data in the table and indicating all important temperature and phases. 2. Find the percentage of each phases and percentage of constituents of the alloy that contain 60 % Zn and at a temperature 300 °C. 3. Find the melting point for the following alloys 20 % Cd, 80% Cd 4. Draw the internal structure, noting the phases of the following alloys A) 30 % Cd at 290 °C b) 60 % Cd at room temperature. % of Zinc in alloy Start of solidification ("C) End of solidification ("C) 0 10 14 20 30 40 50 60 321 290 266 275 293 310 328 345 70 80 90 100 362 390 401 419 266 266 266 266 266 266 266 266 266 266 266 266arrow_forwardIn Figure 1 (phase diagram), an alloy composition of 95 wt% Mg and 5 wt% Al is cooled from 700 C to 475 C. An analysis of the resulting ε solid-phase composition reveals that it has a higher Mg content than is anticipated by the phase diagram.a) Explain why this might be the case and how your reasoning results in the higher-than-expected Mg content.b) Provide a sketch showing the likely distribution of Mg content within the volume of ε solid-phase.arrow_forward
- I need neat and clean handwritten solution. Don't give typed solution. Correct answer will be upvoted only.do rememberarrow_forwardA 50 wt% Ni–50 wt% Cu alloy is heated to a temperature within the a liquid-phase region. If the composition of the alpha phase is 58 wt% Ni, determine (b) the composition of the liquid phase in wt% Niarrow_forwardIn the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! TOCL (liquid) 20 (a, solid) 30 A BCD E E 40 OOOOO 50 wt% Ni www CL= Ca= CL= Ca= CL= Ca= CL= Cu= C₁= Ca= W₁= Wa= WL= WQ= W₁= Wa= W₁= Wa= W₁= Wa= A B C D Earrow_forward
- 5. For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, ii. Calculate the composition(s) of the phase(s) present. iii. Calculate the amount of each phase present in terms of mass fraction. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 80 100 (Pb) (Sn) Composition (wt% Sn) Temperature ("C) Temperat ure ("F)arrow_forwardDraw thermal equilibrium diagram for the binary alloy system (Si-Au), from the following data:- a- Silicon melts at 1414 °C, and gold melts at 1064 °C. b-Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au, and identify all phases are present in the diagram c-Determine the amount of each phase for the alloy which consist of 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?arrow_forwardThe figure is shown here.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Intro to Ceramics and Glasses — Lesson 2, Part 1; Author: Ansys Learning;https://www.youtube.com/watch?v=ArDFnBWH-8w;License: Standard Youtube License