Question
Chapter 4, Problem 4.18QP
(a)
To determine
The percent change in yield strength of aluminum when temperature increases from
(b)
To determine
The percent change in ultimate strength of aluminum when temperature increases from
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
1. The tensile strength vs. temperature curves of aluminum are plotted
below. Explain the meaning of these two curves.
400
Ultimate strength
300
Yield strength
200
100
-200 -150 -100
-50
50
100
150
200
250
Temperature, °C
Strength, kPa
The stress-strain diagram for a steel alloy having an original
diameter of 0.4 in. and a gage length of 4 in. is shown in the
figure below. (Figure 1)
Part A
Determine the modulus of resilience.
Express your answer to three significant figures.
vec
?
(u, )approx =
in-lb
in
Figure
Submit
Request Answer
o (ksi)
80
70
60
Part B
50
Determine the modulus of toughness.
40
30
Express your answer to three significant figures.
20
10
Vol AEO It vec
?
e (in./in.)
0 0.04 0.08 0.12 0.16 0.20 0.24 0.28
0 0.0005 0.0010.0015 0.002 0.0025 0.0030.0035
in-kip
(4)approx =
in
The stress–strain diagram for a steel alloy having an original diameter of 0.5 in. and a gage length of 2 in. is given in the figure. Determine approximately the modulus of resilience and the modulus of toughness for the material.
Chapter 4 Solutions
Materials for Civil and Construction Engineers (4th Edition)
Ch. 4 - Name the two primary factors that make aluminum an...Ch. 4 - Prob. 4.2QPCh. 4 - An aluminum alloy specimen with a radius of 0.28...Ch. 4 - An aluminum alloy bar with a radius of 7 mm was...Ch. 4 - Decode the characteristics of a 6063 T831...Ch. 4 - A round aluminum alloy bar with a 0.6 in. diameter...Ch. 4 - An aluminum alloy bar with a rectangular cross...Ch. 4 - A round aluminum alloy bar with a 0.25-in....Ch. 4 - An aluminum alloy rod has a circular cross section...Ch. 4 - An aluminum alloy cylinder with a diameter of 3...
Ch. 4 - A 3003-H14 aluminum alloy rod with 0.5 in....Ch. 4 - The stressstrain relation of an aluminum alloy bar...Ch. 4 - An aluminum specimen originally 300 mm long is...Ch. 4 - A tension stress of 40 ksi was applied on a 12-in....Ch. 4 - A tension test was performed on an aluminum alloy...Ch. 4 - In Problem 4.15, plot the stressstrain...Ch. 4 - Referring to Figure 4.5, determine approximate...Ch. 4 - Prob. 4.18QPCh. 4 - A tensile stress is applied along the long axis of...Ch. 4 - A cylindrical aluminum alloy rod with a 0.5 in....Ch. 4 - Prob. 4.21QPCh. 4 - Discuss galvanic corrosion of aluminum. How can...
Knowledge Booster
Similar questions
- The following figure shows the tensile stress-strain curve for a plain-carbon steel. 600 80 500 MPa 600 10 psi 60 80 400 400 60- 300 40 40 200 200 20 20 100 0.005 0.05 0.10 0.15 Strain (a) What is this alloy's tensile strength? MPа (b) What is its modulus of elasticity? GPa (c) What is the yield strength? i MPa Stress (MPa) Stress (10 psi)arrow_forwardAnswer the following questions based on the given information in the table and further calculation (if needed for any missing parameter, e.g. strain at yield point). Assume all metals started with the same shape and size before the tensile tests occurred. Material A B C D E Yield Strength (MPa) 105 600 430 355 The material that experienced the greatest percent reduction in area is material The hardest material is material The hardest material has Tensile Strength (MPa) The material that experienced the greatest percent reduction in area has 135 850 The material that experienced the largest change in shape before plastic deformation occurred is material The stiffest material is material The stiffest material has 535 365 Fracture before yielding The material that experienced the largest change in shape before plastic deformation occurred has Strain at Fracture [Choose ] [Choose ] [Choose ] [Choose ] [Choose ] [Choose ] [Choose ] [Choose ] 0.45 0.15 0.20 0.25 Fracture Strength (MPa)…arrow_forwardUse the engineering stress strain diagram provided below to answer parts (A) to (H) below (the stress-strain diagram has already been drawn for you): stress strain diagram 400 350 0 300 0 250 0 200 0 150.0 100.0 50.0 O 05 0 1 0.15 strain A. Determine the tensile strength of this alloy. B. show the elastic, plastic and total strain on the diagram stress (Mpa)arrow_forward
- The stress-strain diagram for a steel alloy having an original diameter of 0.5 in. and a gage length of 2 in. is given in the figure. If the specimen is loaded until it is stressed to 70 ksi, determine the approximate amount of elastic recovery and the increase in the gage length after it is unloaded. o (ksi) 80 70 60 50 40 30 20 10 e (in./in.) 0 04 0.08 0.12 0.16 0.20 0.24 0.28 0 0005 0.0010.0015 0.002 0.0025 0.0030.0035arrow_forwardAn aluminum alloy bar with a radius of 7 mm was subjected to tension until fracture and produced results shown in Table P4.3. a. Using a spreadsheet program, plot the stress–strain relationship. b. Calculate the modulus of elasticity of the aluminum alloy. c. Determine the proportional limit. d. What is the maximum load if the stress in the bar is not to exceed the proportional limit? e. Determine the 0.2% offset yield strength. f. Determine the tensile strength. g. Determine the percent of elongation at failure.arrow_forwardAn aluminum alloy bar with a radius of 7 mm was subjected to tension until fracture and produced results shown in Table P4 a. Using a spreadsheet program, plot the stress–strain relationship. b. Calculate the modulus of elasticity of the aluminum alloy. c. Determine the proportional limit. d. What is the maximum load if the stress in the bar is not to exceed the proportional limit? e. Determine the 0.2% offset yield strength. f. Determine the tensile strength. g. Determine the percent of elongation at failure.arrow_forward
- The graphs in figure 5 show how tensile stress varies with tensile strain for two metallic wires copper and steel. Study the two graphs and answer the questions that follow. The stress is applied until the material breaks, in each case. stress/GPa STEEL COPPER 10 strain/% Figure 5 (i) Write down the breaking tensile stress of each of the materials.arrow_forwardi need the answer quicklyarrow_forwardI need the answer as soon as possiblearrow_forward
- 1.19 A brass alloy has a yield strength of 280 MPa, a tensile strength of 390 MPa, and an elastic modulus of 105 GPa. A cylindrical specimen of this alloy 12.7 mm in diameter and 250 mm long is stressed in tension and found to elongate 7.6 mm. On the basis of the information given, is it possible to compute the magnitude of the load that is necessary to produce this change in length? If so, calculate the load. If not, explain why.arrow_forwardQuestion No.2 Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 000 -Metal A S 600 -Metal B 300 0.00 a.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, mim FIGURE P1.16 Stress, MPaarrow_forwardS Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 900 Metal A 600 Metal B 300 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, m/m FIGURE P1.16 Stress, MPaarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning