Question
Chapter 13, Problem 39RQ
To determine
The undesirable consequences results from turbulence of the metal in the gating system and mold cavity.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Suggest the optimum parameter setting or methods to obtain high quality moulded parts.
لانقطة واحدة
of Warm working
The advantages
over cold working are: 1) forces and
power are higher,2) more intricate
work geometries possible, and 3)
need for annealing may be reduced
.or eliminated
T
F
Blow molding is an important
industrial process for making one-
piece hollow plastic parts with thick
.walls
T
Sly The sequence of the Blow Molding
is automated and often integrated
with downstream operations such
.as bottle filling and labeling
T
لنقطة واحدة
What is the typical industrial reduction ratio for an ingot while being processed into a forging?
Group of answer choices
7:2
3:1
2:1
10:1
How are oxides removed from the melt pool during a casting process?
Group of answer choices
Machined after solidification
Collected in slag
Allowed to diffuse out into the air
Vacuum degassing
Chapter 13 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 13 - What are the six activities that are conducted on...Ch. 13 - What is materials processing?Ch. 13 - What are the five basic families of...Ch. 13 - Describe the capabilities of the casting process...Ch. 13 - What are some of the various mold materials and...Ch. 13 - How might the desired production quantity...Ch. 13 - Why is it important to provide a means of venting...Ch. 13 - What types of problem or defect can occur if the...Ch. 13 - Why might product removal be less of a problem...Ch. 13 - What is a casting pattern? Flask? Core? Mold...
Ch. 13 - In a horizontally parted two-part mold, what is...Ch. 13 - What are some of the components that combine to...Ch. 13 - What is a parting line or parting surface?Ch. 13 - What is draft, and why is it used?Ch. 13 - Why is it important to control the solidification...Ch. 13 - What are the two stages of solidification, and...Ch. 13 - Why is it that most solidification does not begin...Ch. 13 - Why might it be desirable to promote nucleation in...Ch. 13 - Nucleation generally begins at preferred sites...Ch. 13 - Why might directional solidification be desirable...Ch. 13 - Describe some of the key features observed in the...Ch. 13 - What is superheat?Ch. 13 - Prob. 23RQCh. 13 - What is a liquidus temperature? A solidus...Ch. 13 - What is the freezing range for a metal or alloy?Ch. 13 - Discuss the roles of casting volume and surface...Ch. 13 - What characteristics of a specific casting process...Ch. 13 - What is the correlation between cooling rate and...Ch. 13 - What is the chill zone of a casting, and why does...Ch. 13 - Which of the three regions of a cast structure is...Ch. 13 - What is dross or slag, and how can it be prevented...Ch. 13 - What are some of the possible approaches that can...Ch. 13 - What is a misrun or cold shut, and what causes...Ch. 13 - What is fluidity, and how can it be measured?Ch. 13 - What is the most important factor controlling the...Ch. 13 - What defect can form in sand castings if the...Ch. 13 - Why is it important to design the geometry of the...Ch. 13 - Why might it be preferable to attach gates to the...Ch. 13 - Prob. 39RQCh. 13 - What are some desirable features in the sprue...Ch. 13 - What is a choke, and how does its placement affect...Ch. 13 - What features can be incorporated into the gating...Ch. 13 - What are some of the materials and designs of...Ch. 13 - What factors might influence the positioning of...Ch. 13 - What features of the metal being cast tend to...Ch. 13 - What are the three stages of contraction or...Ch. 13 - Why is it more difficult to prevent shrinkage...Ch. 13 - What steps can be taken to compensate for the...Ch. 13 - During what stage of shrinkage might hot tears...Ch. 13 - What is the role of a riser?Ch. 13 - Why is it desirable to design a casting to have...Ch. 13 - What is yield, and how does it relate to the...Ch. 13 - Based on Chvorinovs rule, what would be an ideal...Ch. 13 - Define the following riser-related terms: top...Ch. 13 - What assumptions were made when using Chvorinovs...Ch. 13 - Discuss aspects relating to the connection between...Ch. 13 - What is the purpose of a chill? Of an insulating...Ch. 13 - What are some materials that are commonly used to...Ch. 13 - What types of modifications or allowances are...Ch. 13 - Prob. 60RQCh. 13 - What is the purpose of a draft or taper on pattern...Ch. 13 - Why is it desirable to make the pattern allowances...Ch. 13 - What additional adjustment or correction must be...Ch. 13 - What are some of the features of the casting...Ch. 13 - Prob. 65RQCh. 13 - What are some design recommendations for inside...Ch. 13 - What are some appearance considerations in parting...Ch. 13 - Prob. 68RQCh. 13 - Prob. 69RQCh. 13 - Using Chvorinovs rule as presented in the text...Ch. 13 - Reposition the riser in Problem 1 so that it sits...Ch. 13 - A rectangular casting having the dimensions 3 in....Ch. 13 - A cylinder with a diameter of 2.5 in. and a height...Ch. 13 - Figure 13.Ashows the wall profile of a cast iron...Ch. 13 - Investigate various experimental techniques to...Ch. 13 - Porosity within a casting can be either...Ch. 13 - The chapter text describes various materials that...Ch. 13 - What is the most likely source of the gas bubbles?...Ch. 13 - What factors may have caused the penetration...Ch. 13 - Prob. 3CSCh. 13 - Prob. 4CSCh. 13 - Prob. 5CS
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- requirement : a good understandable handwriting and answer in step by step procedure with good arrangementarrow_forwardWhich of the following manufacturing methods could be economical for a batch size of 100.000 units?arrow_forward3) What are the means of elastic and plastic deformations? List the passageway (gating system) elements in sand casting moulds and show them with drawing?arrow_forward
- Describe the defects found on the injection/ compression moulded parts with different temperatures or time setting. Discuss the possible causes for each case.arrow_forwardWhy the chills are used in moulds in casting?arrow_forwardConverging passage is used for feeding the liquid molten metal into the mould to (a) increase the rate of feeding (b) quickly break off the protruding portion of the casting (c) decrease wastage of cast metal (d) avoid aspiration of airarrow_forward
- Calculate mould dimension for sprue runner and in-gate, the material using fluorothermoplastic and using injection molding. Question: 1. explain the steps for making a mold 2. If possible, use a simulation of the position where the defect will occur 3. Calculate to make mold male and female, the shape is near net shape product and determine material for dies, the liquid materials is 167°C Guidelines Sprue Gate Guidelines L 50% W1 A1 2-3° W1 20- 100% of W2 R1 > 1.5 mm T2 75-100% T1 (part thickness) D1 125-400% T1 (part thickness) D1 100-300% T1 (part thickness) Part Thickness 1.6 mm R > 1 mm (0.040") % Shrinkage Parallel to Flow 4.0-4.5 % Shrinkage Perpendicular to Flow 4.3-4.8 T3 100-200 % (part thickness)arrow_forwardanswer quicklyarrow_forward4) List the passageway (gating system) elements in sand casting moulds and show them with drawing? Draw the stress-strain curve and gives the stress and strain equations for both Engineering and True stress-strainarrow_forward
- i need the answer quicklyarrow_forwardQuestion 3 3.1 Briefly explain the Casting and Molding processes and define their basic requirements. 3.2 If a manufacturer was asked to produce a set of plastic bottles, which method would you suggest? Justify your answer. 3.3 What is the Forging process? Explain the process including two forged products. 3.4 Briefly explain the heat treatment processing techniques using a phase diagram.arrow_forwardno hurry ............. a very good handwriting with every step to be mentioned to understand the answer easily step to follow given requirement solution result if not followed the above steps , ready for consequences i want the solution with a very good handwritingarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY