What characteristics of a specific casting process are incorporated into the mold constant, B, of Chvorinov’s rule?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
In casting experiments performed during a certain alloy and
type of sand mould it took 155 second for a cube shaped
casting to solidify. The cube was 50 mm on a side.
(i)
Determine the value of the mould constant in
Chvorinov's Rule.
(ii)
If the same alloy and mould type were used, find the
total solidification time for cylindrical casting in which
the diameter D = 30 mm and length L = 50 mm.
%3D
Answer this broadly.
what solidification time is required for a casting of 9.5 cm3 and a mold contact area of 10 cm2? The mold constant is 838 s/cm2.
Chapter 13 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 13 - What are the six activities that are conducted on...Ch. 13 - What is materials processing?Ch. 13 - What are the five basic families of...Ch. 13 - Describe the capabilities of the casting process...Ch. 13 - What are some of the various mold materials and...Ch. 13 - How might the desired production quantity...Ch. 13 - Why is it important to provide a means of venting...Ch. 13 - What types of problem or defect can occur if the...Ch. 13 - Why might product removal be less of a problem...Ch. 13 - What is a casting pattern? Flask? Core? Mold...
Ch. 13 - In a horizontally parted two-part mold, what is...Ch. 13 - What are some of the components that combine to...Ch. 13 - What is a parting line or parting surface?Ch. 13 - What is draft, and why is it used?Ch. 13 - Why is it important to control the solidification...Ch. 13 - What are the two stages of solidification, and...Ch. 13 - Why is it that most solidification does not begin...Ch. 13 - Why might it be desirable to promote nucleation in...Ch. 13 - Nucleation generally begins at preferred sites...Ch. 13 - Why might directional solidification be desirable...Ch. 13 - Describe some of the key features observed in the...Ch. 13 - What is superheat?Ch. 13 - Prob. 23RQCh. 13 - What is a liquidus temperature? A solidus...Ch. 13 - What is the freezing range for a metal or alloy?Ch. 13 - Discuss the roles of casting volume and surface...Ch. 13 - What characteristics of a specific casting process...Ch. 13 - What is the correlation between cooling rate and...Ch. 13 - What is the chill zone of a casting, and why does...Ch. 13 - Which of the three regions of a cast structure is...Ch. 13 - What is dross or slag, and how can it be prevented...Ch. 13 - What are some of the possible approaches that can...Ch. 13 - What is a misrun or cold shut, and what causes...Ch. 13 - What is fluidity, and how can it be measured?Ch. 13 - What is the most important factor controlling the...Ch. 13 - What defect can form in sand castings if the...Ch. 13 - Why is it important to design the geometry of the...Ch. 13 - Why might it be preferable to attach gates to the...Ch. 13 - Prob. 39RQCh. 13 - What are some desirable features in the sprue...Ch. 13 - What is a choke, and how does its placement affect...Ch. 13 - What features can be incorporated into the gating...Ch. 13 - What are some of the materials and designs of...Ch. 13 - What factors might influence the positioning of...Ch. 13 - What features of the metal being cast tend to...Ch. 13 - What are the three stages of contraction or...Ch. 13 - Why is it more difficult to prevent shrinkage...Ch. 13 - What steps can be taken to compensate for the...Ch. 13 - During what stage of shrinkage might hot tears...Ch. 13 - What is the role of a riser?Ch. 13 - Why is it desirable to design a casting to have...Ch. 13 - What is yield, and how does it relate to the...Ch. 13 - Based on Chvorinovs rule, what would be an ideal...Ch. 13 - Define the following riser-related terms: top...Ch. 13 - What assumptions were made when using Chvorinovs...Ch. 13 - Discuss aspects relating to the connection between...Ch. 13 - What is the purpose of a chill? Of an insulating...Ch. 13 - What are some materials that are commonly used to...Ch. 13 - What types of modifications or allowances are...Ch. 13 - Prob. 60RQCh. 13 - What is the purpose of a draft or taper on pattern...Ch. 13 - Why is it desirable to make the pattern allowances...Ch. 13 - What additional adjustment or correction must be...Ch. 13 - What are some of the features of the casting...Ch. 13 - Prob. 65RQCh. 13 - What are some design recommendations for inside...Ch. 13 - What are some appearance considerations in parting...Ch. 13 - Prob. 68RQCh. 13 - Prob. 69RQCh. 13 - Using Chvorinovs rule as presented in the text...Ch. 13 - Reposition the riser in Problem 1 so that it sits...Ch. 13 - A rectangular casting having the dimensions 3 in....Ch. 13 - A cylinder with a diameter of 2.5 in. and a height...Ch. 13 - Figure 13.Ashows the wall profile of a cast iron...Ch. 13 - Investigate various experimental techniques to...Ch. 13 - Porosity within a casting can be either...Ch. 13 - The chapter text describes various materials that...Ch. 13 - What is the most likely source of the gas bubbles?...Ch. 13 - What factors may have caused the penetration...Ch. 13 - Prob. 3CSCh. 13 - Prob. 4CSCh. 13 - Prob. 5CS
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- (9,00 Puanlar) A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with 8- length 50 cm, width = 35 cm, and thickness = 4 cm. If the total solidification time of the casting itself is known to be 7,5 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify. %3D Riser volume: V3(TD3)/6(D%3Ddiameter) Riser area: A=TD2 Casting volume: V-L-Wt (L-Length, W=width, t-thickness) a) 8,41 cm b) O 7,34 cm c) 6.62 cm 11,46 cm Boş bırak KÖnceki 8/43 Sonraki> Каpatarrow_forwardPlease show all of your work, thank you!arrow_forwardA flat plate is to be cast in an open mold whose bottom has a square shape that is 200 mm by 200 mm. The mold is 40 mm deep. A total of 106 mm3 of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.0%. The linear shrinkage due to thermal contraction after solidification is 1.3%. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its 200 mm by 200 mm dimensions until solidification is completed, determine the final dimensions of the plate.arrow_forward
- Q. Solidification patterns of steel, with different composition of carbon, in sand and metal molds by time elapse are represented in the following images. Briefly explain the differences observed between the microstructure that develop from mold walls in each case.arrow_forwardMENG364 MANUFACTURING TECHNOLOGYarrow_forwardA riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 100 mm, width = 50 mm, and thickness = 10 mm. If the total solidification time of the casting itself is known to be 2.5 min, determine the diameter of the riser so that it will take 20% longer for the riser to solidify. %3D %3!arrow_forward
- Q#3:(b) Explain in detail different components of a gating system in sand mold casting. Answer:arrow_forwardDoarrow_forward(c) A square casting has a volume and surface area equal to 1000 mm³ and 600 mm² respectively, and a cylindrical riser through which the molten metal is poured has a volume and surface area equal to 282 mm³ and 244 mm² respectively. Using Chvorinov's rule, determine whether such a design would avoid shrinkage cavities.arrow_forward
- State the steps that must be taken to correct the following casting defects: 1. Formation of discontinuity in the casting.- 2. Cast surface consisting of a mixture of sand and metal. 3. Casting with balloon-shaped gas cavity near the surface. 4. Formation of hot tearing in expandable and permanent mold casungs. 5. Metal splatters during pouring and solid globules form and become entrapped in casting.arrow_forwardA 5 cm cube solidifies in 4.6 min. Assume n=2. Calculate (a) the mold constant in Chvorinov’s rule and (b) the solidification time for a 1.25 cm X 12.5 cm X 15 cm bar cast under the same conditionsarrow_forwardWhat is a pattern? What are the consideration necessary while designing pattern in casting?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Casting Metal: the Basics; Author: Casting the Future;https://www.youtube.com/watch?v=2CIcvB72dmk;License: Standard youtube license