Question
Chapter 5, Problem 6CQ
To determine
The line in phase diagram which used to evaluate the temperature where the first liquid formed upon heating an alloy.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Which material has a higher linear coefficient of thermal expansion?
A Teflon
B Titanium
) Medium-carbon steel
D Soda lime glass
2. In a copper-nickel system as shown in figure, an alloy composition of 35 wt% Ni was
cooled down from the temperature of 1300°C. Sketch the expected microstructures at
the point a, b, c, d and e and briefly describe the development of these microstructures
in the equilibrium cooling.
L.
L
(35 Ni)
1300
L (32 Ni)
a (46 Ni)
a(43 Ni)
L (24 Ni)
d
1200
1100
20
30
40
50
Composition (wt% Ni)
Temperature (°C))
A magnesium-lead alloy of mass 6.4 kg consists of a solid a phase that has a composition just slightly below the solubility limit
at 300°C (570°F). The magnesium-lead phase diagram is shown in Animated Figure 9.20.
(a) What mass of lead is in the alloy?
i
kg
(b) If the alloy is heated to 400°C (750°F), how much more lead may be dissolved in the a phase without exceeding the
solubility limit of this phase?
kg
Chapter 5 Solutions
Materials Science And Engineering Properties
Ch. 5 - Prob. 1CQCh. 5 - Prob. 2CQCh. 5 - Prob. 3CQCh. 5 - Prob. 4CQCh. 5 - Prob. 5CQCh. 5 - Prob. 6CQCh. 5 - Prob. 7CQCh. 5 - Prob. 8CQCh. 5 - Prob. 9CQCh. 5 - Prob. 10CQ
Ch. 5 - Prob. 11CQCh. 5 - Prob. 12CQCh. 5 - Prob. 13CQCh. 5 - Prob. 14CQCh. 5 - Prob. 15CQCh. 5 - Prob. 16CQCh. 5 - Prob. 17CQCh. 5 - Prob. 18CQCh. 5 - Prob. 19CQCh. 5 - Prob. 20CQCh. 5 - Prob. 21CQCh. 5 - Prob. 22CQCh. 5 - Prob. 23CQCh. 5 - Prob. 24CQCh. 5 - Prob. 25CQCh. 5 - Prob. 26CQCh. 5 - Prob. 27CQCh. 5 - Prob. 28CQCh. 5 - Prob. 29CQCh. 5 - Prob. 30CQCh. 5 - Prob. 31CQCh. 5 - Prob. 32CQCh. 5 - Prob. 33CQCh. 5 - Prob. 34CQCh. 5 - Prob. 35CQCh. 5 - Prob. 36CQCh. 5 - Prob. 1ETSQCh. 5 - Prob. 2ETSQCh. 5 - Prob. 3ETSQCh. 5 - Prob. 4ETSQCh. 5 - Prob. 5ETSQCh. 5 - Prob. 6ETSQCh. 5 - Prob. 7ETSQCh. 5 - Prob. 8ETSQCh. 5 - Prob. 9ETSQCh. 5 - Prob. 10ETSQCh. 5 - Prob. 11ETSQCh. 5 - Prob. 12ETSQCh. 5 - Prob. 1DRQCh. 5 - Prob. 2DRQCh. 5 - Prob. 3DRQCh. 5 - Prob. 5.1PCh. 5 - Prob. 5.2PCh. 5 - Prob. 5.3PCh. 5 - Prob. 5.4PCh. 5 - Prob. 5.5PCh. 5 - Prob. 5.6PCh. 5 - Prob. 5.7PCh. 5 - Prob. 5.8PCh. 5 - Prob. 5.9PCh. 5 - Prob. 5.10PCh. 5 - Prob. 5.11PCh. 5 - Prob. 5.12PCh. 5 - Prob. 5.13PCh. 5 - Prob. 5.14PCh. 5 - Prob. 5.15PCh. 5 - Prob. 5.16PCh. 5 - Prob. 5.17PCh. 5 - Prob. 5.18PCh. 5 - Prob. 5.19P
Knowledge Booster
Similar questions
- Q.1. For hypereutectoid plain carbon steel (select %C content yourself), determine the phases that are present, the compositions of these phases, and the percentages or fractions of the phases. Make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: a) Just above the austenite transformation temperature b) The austenite transformation temperature 10°C c) The eutectoid transformation temperature +10°C d) The eutectoid transformation temperature 10°Carrow_forwardFor alloys of two hypothetical metals A and B, there exist an a, A-rich phase and a ß, B-rich phase. From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine the composition of the phase boundary (or solubility limit) for the following: Fraction Fraction Alloy Composition a Phase B Phase 60 wt% A - 40 wt% B 0.59 0.41 30 wt% A - 70 wt% B 0.13 0.87 (a) a phase wt% A (b) B phase wt% Aarrow_forward[14] Electrolysis process is based on : * O thermal effect of current O chemical effect of current O luminous effect of current magnetic effect of currentarrow_forward
- Calculate the unit cell edge length for an 57 wt% Ag- 43 wt% Pd alloy. All of the palladium is in solid solution, and the crystal structure for this alloy is FCC. Room temperature densities for Ag and Pd are 10.49 g/cm3 and 12.02 g/cm3, respectively, and their respective atomic weights are 107.87 g/mol and 106.4 g/mol. Report your answer in nanometers.arrow_forwardWhich compound is liberates higher heat at 3 days from the hydration * Tetra calcium Aluminoferrite Tricalcium silicate Tricalcium aluminate Dicalcium silicatearrow_forwardA niobium alloy is produced by introducing tungsten substitutional atoms in the BCC structure. The lattice parameter and density of the alloy is 0.3285 nm and 12.25 g/cm3, respectively. Calculate the fraction of tungsten alloys. (AW = 183.85 g/mol, ANb =92.91 g/mol).arrow_forward
- The following information is given for cadmium at 1atm: boiling point = 765 °C Hvap(765 °C) = 100 kJ/mol melting point = 321 °C Hfus(321 °C) = 6.11 kJ/mol specific heat solid= 0.230 J/g°C specific heat liquid = 0.264 J/g°C __________kJ are required to melt a 31.0 g sample of solid cadmium, Cd, at its normal melting point.arrow_forwardFor a 99.65 wt% Fe-0.35 wt% C alloy at a temperature just up the eutectoid teamperature, determine the following: (a) The fractions of each phases. (b) The Cooling curve for the specific alloy. (C) Descript the phases for this alloy. Subject: Metallurgyarrow_forward
arrow_back_ios
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning