Question
Chapter 5, Problem 5.4P
(a)
To determine
The temperature when the first solid start to form and the chemical composition of it.
(b)
To determine
The phases present at
(c)
To determine
The temperature at which entire alloy become solid at slow cooling and the chemical composition of solid.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A magnesium-lead alloy of mass 6.4 kg consists of a solid a phase that has a composition just slightly below the solubility limit
at 300°C (570°F). The magnesium-lead phase diagram is shown in Animated Figure 9.20.
(a) What mass of lead is in the alloy?
i
kg
(b) If the alloy is heated to 400°C (750°F), how much more lead may be dissolved in the a phase without exceeding the
solubility limit of this phase?
kg
For alloys of two hypothetical metals A and B, there exist an a, A-rich phase and a ß, B-rich phase.
From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine
the composition of the phase boundary (or solubility limit) for the following:
Fraction Fraction
Alloy Composition
a Phase
B Phase
60 wt% A - 40 wt% B
0.59
0.41
30 wt% A - 70 wt% B
0.13
0.87
(a) a phase
wt% A
(b) B phase
wt% A
1. A 65 wt% Ni -35 wt% Cu alloy is heated to a temperature within the a + liquid phase
region. If the composition of the a phase is 70 wt % Ni, determine
i.
The temperature of the alloy
ii.
The composition of the liquid phase
iii.
The mass fraction of both phases
Composition (at% Ni)
20
40
60
80
100
1600
H 2800
1500
Liquid
1453°C
2600
1400
Solidus line
Liquidus line
2400
1300
a +L
1200
2200
1100
A
2000
1085°C
1000
20
40
60
80
100
(Cu)
Composition (wt% Ni)
(Ni)
Temperature (°C)
Temperature (F)
Chapter 5 Solutions
Materials Science And Engineering Properties
Ch. 5 - Prob. 1CQCh. 5 - Prob. 2CQCh. 5 - Prob. 3CQCh. 5 - Prob. 4CQCh. 5 - Prob. 5CQCh. 5 - Prob. 6CQCh. 5 - Prob. 7CQCh. 5 - Prob. 8CQCh. 5 - Prob. 9CQCh. 5 - Prob. 10CQ
Ch. 5 - Prob. 11CQCh. 5 - Prob. 12CQCh. 5 - Prob. 13CQCh. 5 - Prob. 14CQCh. 5 - Prob. 15CQCh. 5 - Prob. 16CQCh. 5 - Prob. 17CQCh. 5 - Prob. 18CQCh. 5 - Prob. 19CQCh. 5 - Prob. 20CQCh. 5 - Prob. 21CQCh. 5 - Prob. 22CQCh. 5 - Prob. 23CQCh. 5 - Prob. 24CQCh. 5 - Prob. 25CQCh. 5 - Prob. 26CQCh. 5 - Prob. 27CQCh. 5 - Prob. 28CQCh. 5 - Prob. 29CQCh. 5 - Prob. 30CQCh. 5 - Prob. 31CQCh. 5 - Prob. 32CQCh. 5 - Prob. 33CQCh. 5 - Prob. 34CQCh. 5 - Prob. 35CQCh. 5 - Prob. 36CQCh. 5 - Prob. 1ETSQCh. 5 - Prob. 2ETSQCh. 5 - Prob. 3ETSQCh. 5 - Prob. 4ETSQCh. 5 - Prob. 5ETSQCh. 5 - Prob. 6ETSQCh. 5 - Prob. 7ETSQCh. 5 - Prob. 8ETSQCh. 5 - Prob. 9ETSQCh. 5 - Prob. 10ETSQCh. 5 - Prob. 11ETSQCh. 5 - Prob. 12ETSQCh. 5 - Prob. 1DRQCh. 5 - Prob. 2DRQCh. 5 - Prob. 3DRQCh. 5 - Prob. 5.1PCh. 5 - Prob. 5.2PCh. 5 - Prob. 5.3PCh. 5 - Prob. 5.4PCh. 5 - Prob. 5.5PCh. 5 - Prob. 5.6PCh. 5 - Prob. 5.7PCh. 5 - Prob. 5.8PCh. 5 - Prob. 5.9PCh. 5 - Prob. 5.10PCh. 5 - Prob. 5.11PCh. 5 - Prob. 5.12PCh. 5 - Prob. 5.13PCh. 5 - Prob. 5.14PCh. 5 - Prob. 5.15PCh. 5 - Prob. 5.16PCh. 5 - Prob. 5.17PCh. 5 - Prob. 5.18PCh. 5 - Prob. 5.19P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- Given a Cu-Ag alloy with a bulk composition of 30wt% Ag, answer the following: a. At what temperature does the first solid start to form? units: units: units: b. What is the elemental composition of this solid phase when it first appears? c. At what temperature does the material become fully solid? d. What is the elemental composition of the very last portion of liquid that is present just before the system fully transforms to solid? Temperature (°C) 1200 1000 800 A α B 8.0 (CE) units: Composition (at% Ag) 20 40 60 80 100 2200 -Liquidus Liquid 2000 -Solidus a +L 1800 F 1600 779°C (TE) B+L E G 71.9 91.2 1400 β (CE) (CBE) 600 Solvus α + β 400 C 200 0 20 40 (Cu) 1200 1000 800 600 H 400 60 80 100 (Ag) Composition (wt% Ag) Temperature (°F)arrow_forwardNeed help with this question. Thank you :)arrow_forward2. In a copper-nickel system as shown in figure, an alloy composition of 35 wt% Ni was cooled down from the temperature of 1300°C. Sketch the expected microstructures at the point a, b, c, d and e and briefly describe the development of these microstructures in the equilibrium cooling. L. L (35 Ni) 1300 L (32 Ni) a (46 Ni) a(43 Ni) L (24 Ni) d 1200 1100 20 30 40 50 Composition (wt% Ni) Temperature (°C))arrow_forward
- Metal X has an atomic weight of 43.1 g/mol, theoretical density of 6.40 g/cm^3, and atomic radius of 122 pm. Determine whether the crystal structure of Metal X is BCC, FCC, or simple cubic. Provide your complete solution.arrow_forward3.11 Each of the following statements describes a silicate mineral or mineral group. In each case, provide the appropriate name. a- The most common member of the amphibole group. b- The most common non ferromagnesian member of the mica family. c- The only silicate mineral made entirely of silicon and oxygen. d- A high-temperature silicate with a name that is based on its color. e-Characterized by striations. f- Originates as a product of chemical weathering.arrow_forward18 Material Science and Engineeringarrow_forward
- Q.1. For hypereutectoid plain carbon steel (select %C content yourself), determine the phases that are present, the compositions of these phases, and the percentages or fractions of the phases. Make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: a) Just above the austenite transformation temperature b) The austenite transformation temperature 10°C c) The eutectoid transformation temperature +10°C d) The eutectoid transformation temperature 10°Carrow_forwardView Policies Current Attempt in Progress Using the Animated Figure 10.40, the isothermal transformation diagram for a 0.45 wt% C steel alloy, specify the nature of the final microstructure (in terms of the microconstituents present) of a small specimen that has been subjected to the following temperature treatments. In each case assume that the specimen begins at 845 °C and that it has been held at this temperature long enough to have achieved a complete and homogeneous austenitic structure. a) Rapidly cool to 700 degrees C, hold for 100,000 s, then quench to room temperature. b) Rapidly cool to 450 degrees C, hold for 10 s, then quench to room temperature. proeutectoid ferrite + pearlite proeutectoid ferrite + martensite proeutectoid ferrite + pearlite + martensite eT proeutectoid ferrite + pearlite + bainite + martensite all spheroidite Save all bainite Attempts: 0 of 5 used Submit Answer all martensite bainite + martensitearrow_forwardWhich of the following alloys would form a complete substitutional solid solution? Metal 1 is BCC, metal 2 is FCC, and atomic radíus difference is 12%. Metal 1 is FCC, metal 2 is FCC, and atomic radius difference is 12%. Metal 1 is FCC, metal 2 is FCC, and atomic radíus difference is 15%. Metal 1 is HCP, metal 2 is FCC, and atomic radius differene is less than 15%. Metal 1 is BCC, metal 2 is BCC, and atomic radius difference is at least 15%.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning