Question
Chapter 5, Problem 5.19P
(a)
To determine
The temperature at which the single phase start to separate into two phases.
(b)
To determine
The number of phases present at
(c)
To determine
The composition of each phase at
(d)
To determine
The volume fraction of each phase at
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
1. A 65 wt% Ni -35 wt% Cu alloy is heated to a temperature within the a + liquid phase
region. If the composition of the a phase is 70 wt % Ni, determine
i.
The temperature of the alloy
ii.
The composition of the liquid phase
iii.
The mass fraction of both phases
Composition (at% Ni)
20
40
60
80
100
1600
H 2800
1500
Liquid
1453°C
2600
1400
Solidus line
Liquidus line
2400
1300
a +L
1200
2200
1100
A
2000
1085°C
1000
20
40
60
80
100
(Cu)
Composition (wt% Ni)
(Ni)
Temperature (°C)
Temperature (F)
subject: Material Engineering
Using the given sheet for the Ni-Ti Phase diagram, how many phase fields appear in the diagram and write down the weight fraction of gamma phase for an alloy containing 43% wt of Ti at 1000 C
34 If the following diagram represents the sintering of the ceramic MgO, what could the curves x and y refer to?
increase in property
X
1000
1200
1600
sintering temperature (°C)
(A) = grain size; y porosity
(B) x grain size; y = strength
O(C) x porosity; y-grain size
1400
O (D) x strength; y grain size
1800
Chapter 5 Solutions
Materials Science And Engineering Properties
Ch. 5 - Prob. 1CQCh. 5 - Prob. 2CQCh. 5 - Prob. 3CQCh. 5 - Prob. 4CQCh. 5 - Prob. 5CQCh. 5 - Prob. 6CQCh. 5 - Prob. 7CQCh. 5 - Prob. 8CQCh. 5 - Prob. 9CQCh. 5 - Prob. 10CQ
Ch. 5 - Prob. 11CQCh. 5 - Prob. 12CQCh. 5 - Prob. 13CQCh. 5 - Prob. 14CQCh. 5 - Prob. 15CQCh. 5 - Prob. 16CQCh. 5 - Prob. 17CQCh. 5 - Prob. 18CQCh. 5 - Prob. 19CQCh. 5 - Prob. 20CQCh. 5 - Prob. 21CQCh. 5 - Prob. 22CQCh. 5 - Prob. 23CQCh. 5 - Prob. 24CQCh. 5 - Prob. 25CQCh. 5 - Prob. 26CQCh. 5 - Prob. 27CQCh. 5 - Prob. 28CQCh. 5 - Prob. 29CQCh. 5 - Prob. 30CQCh. 5 - Prob. 31CQCh. 5 - Prob. 32CQCh. 5 - Prob. 33CQCh. 5 - Prob. 34CQCh. 5 - Prob. 35CQCh. 5 - Prob. 36CQCh. 5 - Prob. 1ETSQCh. 5 - Prob. 2ETSQCh. 5 - Prob. 3ETSQCh. 5 - Prob. 4ETSQCh. 5 - Prob. 5ETSQCh. 5 - Prob. 6ETSQCh. 5 - Prob. 7ETSQCh. 5 - Prob. 8ETSQCh. 5 - Prob. 9ETSQCh. 5 - Prob. 10ETSQCh. 5 - Prob. 11ETSQCh. 5 - Prob. 12ETSQCh. 5 - Prob. 1DRQCh. 5 - Prob. 2DRQCh. 5 - Prob. 3DRQCh. 5 - Prob. 5.1PCh. 5 - Prob. 5.2PCh. 5 - Prob. 5.3PCh. 5 - Prob. 5.4PCh. 5 - Prob. 5.5PCh. 5 - Prob. 5.6PCh. 5 - Prob. 5.7PCh. 5 - Prob. 5.8PCh. 5 - Prob. 5.9PCh. 5 - Prob. 5.10PCh. 5 - Prob. 5.11PCh. 5 - Prob. 5.12PCh. 5 - Prob. 5.13PCh. 5 - Prob. 5.14PCh. 5 - Prob. 5.15PCh. 5 - Prob. 5.16PCh. 5 - Prob. 5.17PCh. 5 - Prob. 5.18PCh. 5 - Prob. 5.19P
Knowledge Booster
Similar questions
- Given a Cu-Ag alloy with a bulk composition of 30wt% Ag, answer the following: a. At what temperature does the first solid start to form? units: units: units: b. What is the elemental composition of this solid phase when it first appears? c. At what temperature does the material become fully solid? d. What is the elemental composition of the very last portion of liquid that is present just before the system fully transforms to solid? Temperature (°C) 1200 1000 800 A α B 8.0 (CE) units: Composition (at% Ag) 20 40 60 80 100 2200 -Liquidus Liquid 2000 -Solidus a +L 1800 F 1600 779°C (TE) B+L E G 71.9 91.2 1400 β (CE) (CBE) 600 Solvus α + β 400 C 200 0 20 40 (Cu) 1200 1000 800 600 H 400 60 80 100 (Ag) Composition (wt% Ag) Temperature (°F)arrow_forwardQ.1. For hypereutectoid plain carbon steel (select %C content yourself), determine the phases that are present, the compositions of these phases, and the percentages or fractions of the phases. Make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: a) Just above the austenite transformation temperature b) The austenite transformation temperature 10°C c) The eutectoid transformation temperature +10°C d) The eutectoid transformation temperature 10°Carrow_forwardI need answer within 20 minutes please please with my best wishesarrow_forward
- What are the various parameters that affect the viscosity of a polymer melt, and how do they affect its propertiesarrow_forwardThe following information is given for n-pentane at 1 atm:boiling point = 36.20°C ΔHvap (36.20°C) = 357.6 J/g melting point = − 129.7°C ΔHfus (−129.7°C) = 116.7 J/g specific heat gas = 1.650 J/g ⋅ °C specific heat liquid = 2.280 J/g ⋅ °C A 26.10-g sample of liquid n-pentane is initially at −51.40°C. If the sample is heated at constant pressure (P = 1 atm), how many kJ of energy are needed to raise the temperature of the sample to 65.30°C?arrow_forwardView Policies Current Attempt in Progress Using the Animated Figure 10.40, the isothermal transformation diagram for a 0.45 wt% C steel alloy, specify the nature of the final microstructure (in terms of the microconstituents present) of a small specimen that has been subjected to the following temperature treatments. In each case assume that the specimen begins at 845 °C and that it has been held at this temperature long enough to have achieved a complete and homogeneous austenitic structure. a) Rapidly cool to 700 degrees C, hold for 100,000 s, then quench to room temperature. b) Rapidly cool to 450 degrees C, hold for 10 s, then quench to room temperature. proeutectoid ferrite + pearlite proeutectoid ferrite + martensite proeutectoid ferrite + pearlite + martensite eT proeutectoid ferrite + pearlite + bainite + martensite all spheroidite Save all bainite Attempts: 0 of 5 used Submit Answer all martensite bainite + martensitearrow_forward
- Example: Cast iron contains 5% carbon, its structure at 1131°C consists of leadpurite and elemental cementite, find the percentage of these two components?arrow_forwardI need the answer at 20 minutearrow_forwardAn aluminum pipe has a length of 54 m at a temperature of 10°C. An adjacent steel pipe at the same temperature is 8 mm longer. At what temperature will the aluminum pipe be 24 mm longer than the steel pipe? Assume that the coefficient of thermal expansion for the aluminum is 22.5x10-6/°C and that the coefficient of thermal expansion for the steel is 12.5×10-6/°C.arrow_forward
- A hypothetical metal alloy has a grain diameter of 2.4 x 10-2 mm. After a heat treatment at 575°C for 500 min, the grain diameter has increased to 9.0 × 10-2 mm. Compute the time required for a specimen of this same material (i.e., do = 2.4 × 10-2 mm) to achieve a grain diameter of 5.5 × 10-2 mm while being heated at 575°C. Assume the n grain diameter exponent has a value of 2.2. i minarrow_forwardEnter your answer in the box provided. What is the ee for the following mixture of enantiomers A and B? 89% A and 11% B % eearrow_forwardAn aluminum cup of 150 cm3 capacity is completely filled with glycerin at 16°C. How much glycerin will spill out of the cup if the temperature of both the cup and glycerin is increased to 39°C? (The linear expansion coefficient of aluminum is 23 x 10-6 1/CO. The coefficient of volume expansion of glycerin is 5.1 x 104 1/C°) loth prob Number i Unitsarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage LearningConstruction Materials, Methods and Techniques (M...Civil EngineeringISBN:9781305086272Author:William P. Spence, Eva KultermannPublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
Construction Materials, Methods and Techniques (M...
Civil Engineering
ISBN:9781305086272
Author:William P. Spence, Eva Kultermann
Publisher:Cengage Learning