Textbook Question
Chapter 2, Problem 70QTP
Calculate the major and minor pyramid angles for a Knoop indenter, and compare your results with those obtained from Vickers and Rockwell A indenters.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A circular specimen of MgO is loaded using a three-point bending mode. Compute the minimum possible radius of the specimen
without fracture, given that the applied load is 1000 N (225 lbf), the flexural strength is 105 MPa (15,000 psi), and the separation
between load points is 50.0 mm (1.97 in.).
i
mm
Sketch Figure 1.3, curve b (a ductile metal). Label it with the following terms, indicating from which location on the curve each quantity can be identified or extracted: elastic region, plastic region, proportional limit, tensile strength, onset of necking, fracture stress.
A sample of giant reed is shaped into a beam with
a square cross section of 15.5 mm by 15.5 mm.
Two supports placed 22.1 mm apart support the
sample and a load is applied halfway between the
support points in order to test the force required to
fracture the sample. If ultimate tensile strength is
912 MPa, what would be the force F (newtons)
required to cause failure?
Chapter 2 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 2 - Distinguish between engineering stress and true...Ch. 2 - In a stress-strain curve, what is the proportional...Ch. 2 - Describe the events that take place when a...Ch. 2 - What is ductility, and how is it measured?Ch. 2 - In the equation =Kn, which represents the true...Ch. 2 - What is strain-rate sensitivity, and how is it...Ch. 2 - What test can measure the properties of a material...Ch. 2 - What testing procedures can be used to measure the...Ch. 2 - Describe the differences between brittle and...Ch. 2 - What is hardness? Explain.
Ch. 2 - Describe the features of a Rockwell hardness test.Ch. 2 - What is a Leeb test? How is it different from a...Ch. 2 - Differentiate between stress relaxation and creep.Ch. 2 - Describe the difference between elastic and...Ch. 2 - Explain what uniform elongation means in tension...Ch. 2 - Describe the difference between deformation rate...Ch. 2 - Describe the difficulties involved in conducting a...Ch. 2 - What is Hookes law? Youngs modulus? Poissons...Ch. 2 - Describe the difference between transgranular and...Ch. 2 - What is the reason that yield strength is...Ch. 2 - Why does the fatigue strength of a specimen or...Ch. 2 - If striations are observed under microscopic...Ch. 2 - What is an Izod test? Why are Izod tests useful?Ch. 2 - Why does temperature increase during plastic...Ch. 2 - What is residual stress? How can residual stresses...Ch. 2 - On the same scale for stress, the tensile true...Ch. 2 - What are the similarities and differences between...Ch. 2 - Can a material have a negative Poissons ratio?...Ch. 2 - It has been stated that the higher the value of m,...Ch. 2 - Explain why materials with high m values, such as...Ch. 2 - With a simple sketch, explain whether it is...Ch. 2 - Explain why the difference between engineering...Ch. 2 - Consider an elastomer, such as a rubber band. This...Ch. 2 - If a material (such as aluminum) does not have an...Ch. 2 - What role, if any, does friction play in a...Ch. 2 - Which hardness tests and scales would you use for...Ch. 2 - Consider the circumstance where a Vickers hardness...Ch. 2 - Which of the two tests, tension or compression,...Ch. 2 - List and explain briefly the conditions that...Ch. 2 - List the factors that you would consider in...Ch. 2 - On the basis of Fig. 2.5, can you calculate the...Ch. 2 - If a metal tension-test specimen is rapidly pulled...Ch. 2 - Comment on your observations regarding the...Ch. 2 - Will the disk test be applicable to a ductile...Ch. 2 - What hardness test is suitable for determining the...Ch. 2 - Wire rope consists of many wires that bend and...Ch. 2 - A statistical sampling of Rockwell C hardness...Ch. 2 - In a Brinell hardness test, the resulting...Ch. 2 - Some coatings are extremely thinsome as thin as a...Ch. 2 - Select an appropriate hardness test for each of...Ch. 2 - A paper clip is made of wire 0.5 mm in diameter....Ch. 2 - A 250-mm-long strip of metal is stretched in two...Ch. 2 - Identify the two materials in Fig. 2.5 that have...Ch. 2 - Plot the ultimate strength vs. stiffness for the...Ch. 2 - If you remove the layer of material ad from the...Ch. 2 - Prove that the true strain at necking equals the...Ch. 2 - Percent elongation is always defined in terms of...Ch. 2 - You are given the K and n values of two different...Ch. 2 - A cable is made of two strands of different...Ch. 2 - On the basis of the information given in Fig. 2.5,...Ch. 2 - In a disk test performed on a specimen 1.00 in. in...Ch. 2 - A piece of steel has a hardness of 300 HB....Ch. 2 - A metal has the following properties: UTS = 70,000...Ch. 2 - Using only Fig. 2.5, calculate the maximum load in...Ch. 2 - Estimate the modulus of resilience for a highly...Ch. 2 - A metal has a strength coefficient K = 100,000 psi...Ch. 2 - Plot the true stresstrue strain curves for the...Ch. 2 - The design specification for a metal requires a...Ch. 2 - Calculate the major and minor pyramid angles for a...Ch. 2 - If a material has a target hardness of 300 HB,...Ch. 2 - A Rockwell A test was conducted on a material and...Ch. 2 - For a cold-drawn 0.5% carbon steel, will a...Ch. 2 - A material is tested in tension. Over a 1-in. gage...Ch. 2 - A horizontal rigid bar cc is subjecting specimen a...Ch. 2 - List and explain the desirable mechanical...Ch. 2 - When making a hamburger, you may have observed the...Ch. 2 - An inexpensive claylike material called Silly...Ch. 2 - In tension testing of specimens, mechanical and...Ch. 2 - Demonstrate the impact toughness of a piece of...Ch. 2 - Using a large rubber band and a set of weights,...Ch. 2 - Find or prepare some solid circular pieces of...Ch. 2 - Take several rubber bands and pull them at...Ch. 2 - Devise a simple fixture for conducting the bend...Ch. 2 - By pressing a small ball bearing against the top...Ch. 2 - Describe your observations regarding Fig. 2.14c.Ch. 2 - Embed a small steel ball in a soft block of...Ch. 2 - Devise a simple experiment, and perform tests on...Ch. 2 - Obtain some solid and some tubular metal pieces,...Ch. 2 - Explain how you would obtain an estimate of the...Ch. 2 - Without using the words stress or strain, define...Ch. 2 - We know that it is relatively easy to subject a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Write the analysis that assumes that the cross-section is constant andhas an axis of symmetry?arrow_forwardA sample of giant reed is shaped into a beam with a square cross section of 15.5 mm by 15.5 mm. Two supports placed 22.1 mm apart support thesample and a load is applied halfway between the support points in order to test the force required to fracture the sample. If ultimate tensile strength is912 MPa, what would be the force F (newtons) required to cause failure?arrow_forwardDraw a load vs. displacement curve as obtained from a homogeneous material using nanoindentation. Please explain how the elastic modulus is calculated using the curve.arrow_forward
- A 3.048 m annealed rod with a cross-sectional area of 555 mm2 was extruded from a 5083-0 aluminum alloy and axially loaded. Under load, the length of the rod increased to 3.0518 m. No plastic deformation occurred. (a) Find the modulus of elasticity of the material and calculate its allowable tensile stress, assuming it to be 50% of the tensile yield stress. (b) Calculate the tensile stress and the axial load applied to the rod. (c) Compare the calculated tensile stress with the allowable tensile stress, and find the absolute value of elongation of the rod for the allowable stress.arrow_forwardA steel rod (initial diameter: 3.2 mm, initial length: 42 mm) is extended by auniaxial tensile load of 4800 N in 120 seconds. At this load, the length of therod is measured as 49,2 mm. Calculate the followings:(a) Stress and strain occurred on the rod at this load.(b) Initial strain rate.(c) Diameter of the rod at this load.(Yield strength : 380 MPa, Ultimate Tensile Strength: 670 MPa,Modulus of Elasticity: 210000 MPa were given for this material)arrow_forwardA square specimen of is loaded using a three-point bend test. The load during the test is 419.6 N while the separation between the load points is 53.1mm. The flexural strength of MgO is equal to 103.4MPa . Compute the minimum possible thickness the specimen should have to avoid fractures during the bend test. Round your answer to three significant figures.arrow_forward
- A three-point bending test was performed on an aluminum oxide specimen having a circular cross section of radius = 5 mm, the specimen fractured at a load of 1400 N when the distance between the support points L = 100 mm. Another test is to be performed on a specimen of this same material, but one that has a square cross section of 12 mm on each edge. At what load would you expect this specimen to fracture if L = 50 mm? i need clear ans by hand and solve very very fast in 20 min and thank you DYBALARI |arrow_forwardSketch a graph of Hooke’s Law and label the elastic region, plastic region, yield tensile strength and ultimate tensile strength.arrow_forwardOrdinary sheets of borosilicate glass are tested in bending, and are found to fracture at an average stress of 72 MPa. After thermal tempering, the stress at failure increases by 90%. What are the sign and magnitude of the stress induced in the glass by the tempering operation?arrow_forward
- Explain why a maximum in stress occurs in the engineering stress—strain curve for a polycrystallinemetal deformed in tension. Why is there no maximum for the true stress— strain curve?arrow_forwardA high-strength steel has yield strength of 1165 MPa and fracture toughness of 95 MPavm. Calculate the size of an internal crack that will lead to catastrophic failure at an applied stress of 80% yield strength. (Y = 1.00 for internal crack, and Y=1.12 for surface crack)arrow_forwardA three-point transverse bending test was performed on a glass specimen having a square cross-section of 18.5 mm length on each edge. The specimen fractured at a load of 4530 N when the distance between support points was 42 mm. A second test is to be performed on another specimen of this same glass material, but one that has a circular cross-section. What minimum specimen diameter is required to ensure that fracture will not occur when a load of 3480 N is applied? Assume that the support separation is maintained at 42 mm. mmarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY