Materials Science And Engineering Properties
1st Edition
ISBN: 9781111988609
Author: Charles Gilmore
Publisher: Cengage Learning
expand_more
expand_more
format_list_bulleted
Concept explainers
Question
Chapter 12, Problem 12.11P
(a)
To determine
The strain where the first change in elastic modulus occur.
(b)
To determine
Composite stress where change in elastic modulus occurs.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
An element representative of a composite comprising an isotropic fiber
enveloped by the isotropic resin is shown in Figure 1. Note that the two materials
stick together perfectly and that the external surface of the element is free of
stress. Calculate the axial stress in the fiber (of) and that in the resin (om) in the
middle of the axis longitudinal fiber (L/ 2) using the material strength approach in
the case where the element is exposed to a change in temperature AT, depending
on following variables
The thermal expansion coefficients af and am
• The Af and Am sections
• The moduli of elasticity Ef and Em
• AT
Guide:
There is no external force
• Relations to consider: balance, geometric compatibility and relation
stress-strain.
Fibre :
At, Er,
Of, af
Matrice :
Am, Em,
Ớm, đm
A 1500 mm long composite bar consists of aluminum and steel as shown. The cross-sectional area of the aluminum bar is twice that of the steel bar. If the assembly is exposed to an axial tensile load of 250 kN, determine the lengths of each of the components if the elongation of the aluminum is the same with that of the steel. The modulus of elasticity of steel E = 200 GPa and for the aluminum is one-third of the steel.
for a fiber reinforced composite material, assume Fibre's volume fraction is 0.3. what is the effective tensile strength of the composite if the strength of fiber is 150GPa and that of matrix is 16GPa
Chapter 12 Solutions
Materials Science And Engineering Properties
Ch. 12 - Prob. 1CQCh. 12 - Prob. 2CQCh. 12 - Prob. 3CQCh. 12 - Prob. 4CQCh. 12 - Prob. 5CQCh. 12 - Prob. 6CQCh. 12 - Prob. 7CQCh. 12 - Prob. 8CQCh. 12 - Composite _________ is produced by laying fibers...Ch. 12 - Prob. 10CQ
Ch. 12 - Prob. 11CQCh. 12 - Prob. 12CQCh. 12 - Prob. 13CQCh. 12 - Prob. 14CQCh. 12 - Prob. 15CQCh. 12 - Prob. 16CQCh. 12 - Prob. 17CQCh. 12 - Prob. 18CQCh. 12 - Prob. 19CQCh. 12 - Prob. 20CQCh. 12 - Prob. 21CQCh. 12 - Prob. 22CQCh. 12 - Prob. 23CQCh. 12 - Prob. 24CQCh. 12 - Prob. 25CQCh. 12 - Prob. 26CQCh. 12 - Prob. 27CQCh. 12 - Prob. 28CQCh. 12 - Prob. 1ETSQCh. 12 - Prob. 2ETSQCh. 12 - Prob. 3ETSQCh. 12 - Prob. 4ETSQCh. 12 - Prob. 5ETSQCh. 12 - Prob. 6ETSQCh. 12 - Prob. 7ETSQCh. 12 - Prob. 8ETSQCh. 12 - Prob. 9ETSQCh. 12 - Prob. 10ETSQCh. 12 - In Example Problem 12.1, a uniaxial composite...Ch. 12 - Prob. 12.2PCh. 12 - Prob. 12.3PCh. 12 - Prob. 12.4PCh. 12 - Prob. 12.5PCh. 12 - Prob. 12.6PCh. 12 - Estimate the transverse tensile strength of the...Ch. 12 - Prob. 12.8PCh. 12 - Prob. 12.9PCh. 12 - Prob. 12.10PCh. 12 - Prob. 12.11PCh. 12 - Prob. 12.12PCh. 12 - Prob. 12.13PCh. 12 - Prob. 12.14PCh. 12 - Prob. 12.15PCh. 12 - Prob. 12.16PCh. 12 - Prob. 12.17P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- In Example Problem 12.1, a uniaxial composite material is made into a circular rod Vbith a 1.27-cm diameter from 70 volume percent continuous carbon fibers and 30 volume percent epoxy. The rod is subject to an axial force of 100,000 N. The composite matcrial in Example Problem 12.1 is to be replaced with a less expensive composite made of 70 volume percent continuous E-glass fibers and 30 volume percent epoxy. The elastic moduli are 5 GPa for the epoxy resin and 72.4 GPa fos the E-glass. (a) Compare the elastic modulus, composite strain, fiber and matrix stresses, and density of this composite with the carbon epoxy composite in Example Problem 12.1. Usc the density of UHM carbon, and assume the density of the epoxy is 1.2g/cm3 . (b) Can both the E-glass fiber and matrix withstand the applied force?arrow_forward4. For the composite block shown, determine (a) the value of h if the portion of the load carried by the aluminum plates is half the portion of the load carried by the brass core, (b) the total load if the stress in the brass is 80 Mpa. P Rigid end plate Aluminum Plates (E=70 GPa) Brass Core (E=105 GPa) 40 mm I h 60 mm 300 mmarrow_forwardA composite beam made of steel and bronze has the cross section shown. The cross-sectional dimensions are b, - 0.9 in, b2 - 2.7 in., and d- 1.8 in. The elastic modulus of the steel is E, - 30,000 ksi, and its allowable bending stress is 17 ksi. The elastic modulus of the bronze is E2 - 15,000 ksi, and its allowable bending stress is 14 ksi. Calculate the allowable bending moment that can be applied about the z centroidal axis. Bronze (2) d Steel (1) b2 Part 1 Your answer has been saved. See score details after the due date. Determine the modular ratio in order to transform the steel into an equivalent amount of bronze. Answer: n- Attempts: 1 of 1 used Part 2 Determine the area moment of inertia of the transformed section about the z-axis. Answer: in.4arrow_forward
- A discontinuous fibre reinforced composite consists of 20mm long carbon fibres in a polymer matrix. The volume fraction of the composite is 0.5, interfacial shear strength 5MPa and the critical fibre length 2.5mm. The fibre modulus is 250GPA and strain to failure 1.5%. The matrix modulus is 3.5GPa and failure strain 10%. If the ultimate fibre strength = 3500MPa, calculate the average failure stress in the composite.arrow_forwardCalculate the modulus of elasticity of fiberglass under isostrain condition if the fiberglass consists of 70% E-glass fibers and 30% epoxy by volume. Also, calculate the percentage of load carried by the glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70.5 and 6.9 GPa, respectively. If a longitudinal stress of 60 MPa is applied on the composite with a cross-sectional area ofm300 mm2, what is the load carried by each of the fiber and the matrix phases? What is the strain sustained by each of the fiber and the matrix phases?arrow_forwardA composite sample of carbon reinforced epoxy has dimensions of in 20 in x 20 in x 0.135 in and mass of 3 lb. The carbon fibres have a modulus of elasticity of 80(106) lb/in2 and a density of 0.15 lb/in3. The epoxy matrix has modulus of elasticity of 0.90(106) lb/in2 and a density of 0.05 lb/in3. Assume there are no voids in the sample, calculate the volume fraction of: (i) The carbon fibres (ii) The epoxy matrix in the sample.arrow_forward
- When looking up data for composite materials, it is important to: a.)Make sure the volume fraction of the fibres is specified b.)The orientation of each fibre layer is specified c.)The type of resin/matric is specified d.)All of the abovearrow_forwardA solid rod of bronze 20 mm in diameter is surrounded by a fitting steel cylinder of external diameter 28 mm. If the permissible bending stress in bronze and steel are 100 and 150 N/mm², find the moment of resistance of the composite section. The Young's modulus for steel may be taken as 1.75 times that of bronze.arrow_forwardA bar having the cross section shown has been formed by securely bonding brass and aluminum stock. Using the data given below, determine the largest permissible bending moment when the composite bar is bent about a horizontal axis.Modulus of elasticity 70 GPa,105 GPa Allowable stress100 MPa,160 MPaarrow_forward
- A composite beam made of steel and bronze has the cross section shown. The cross-sectional dimensions are bz - 0.9 in, b2 - 2.7 in., and d- 1.8 in. The elastic modulus of the steel is E1 - 30,000 ksi, and its allowable bending stress is 17 ksi. The elastic modulus of the bronze is Ez - 15,000 ksi, and its allowable bending stress is 14 ksi. Calculate the allowable bending moment that can be applied about the z centroidal axis. Bronze (2) d Steel (1) b2 Part 1 Determine the modular ratio in order to transform the steel into an equivalent amount of bronze. Answer: n - iarrow_forwardIV- It is necessary to design a continuous and aligned glass fiber-reinforced polyester having a tensile strength of at least 1400 MPa in the longitudinal direction. The maximum possible specific gravity is 1.65. Using the following data, determine whether such a composite is possible. Justify. Assume a value of 15 MPa for the stress on the matrix when the fibers fail. Material Glass fiber Polyester Specific gravity 2.5 1.35 Tensile strength (MPa) 3500 50arrow_forwardCalculate the modulus of elasticity of fiberglass under isostrain condition if the fiberglass consists of 70% E-glass fibers and 30% epoxy by volume. Also, calculate the percentage of load carried by the glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70.5 and 6.9 GPa, respectively. If a longitudinal stress of 60 MPa is applied on the composite with a cross-sectional area of 300 mm2, what is the load carried by each of the fiber and the matrix phases?What is the strain sustained by each of the fiber and the matrix phases?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
The History of Composite Materials, From Brick to Bakelite to Biomimetic Hybrids; Author: Autodesk;https://www.youtube.com/watch?v=VS_Kg-VEvzE;License: Standard YouTube License, CC-BY