Manufacturing Engineering & Technology
7th Edition
ISBN: 9780133128741
Author: Serope Kalpakjian, Steven Schmid
Publisher: Prentice Hall
expand_more
expand_more
format_list_bulleted
Concept explainers
Videos
Textbook Question
Chapter 11, Problem 37QLP
In shell-mold casting, the curing process is critical to the quality of the finished mold. In this stage of the process, the shell-mold assembly and cores are placed in an oven for a short period of time to complete the curing of the resin binder. List probable causes of unevenly cured cores or of uneven core thicknesses.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
State the steps that must be taken to correct the following casting defects:
1. Formation of discontinuity in the casting.-
2. Cast surface consisting of a mixture of sand and metal.
3. Casting with balloon-shaped gas cavity near the surface.
4. Formation of hot tearing in expandable and permanent mold casungs.
5. Metal splatters during pouring and solid globules form and become entrapped in
casting.
2. What do the various elements that comprise the gating system? what are the
pouring basin in a sand casting?
3. Explain why a sprue should be tapered?
4. What are the disadvantages of die casting?
5. Explain the various kinds of patterns in use. What are the allowances provided
How do the patterns differ from the casting required?
6. Define Expendable-mold, Expendable-pattern Casting Processes
Manufacturing Processes
Chapter 11 Solutions
Manufacturing Engineering & Technology
Ch. 11 - Describe the differences between expendable and...Ch. 11 - Name the important factors in selecting sand for...Ch. 11 - What are the major types of sand molds? What are...Ch. 11 - List important considerations when selecting...Ch. 11 - What is the function of a core?Ch. 11 - What is the difference between sand-mold and...Ch. 11 - What are composite molds? Why are they used?Ch. 11 - Describe the features of plaster-mold casting.Ch. 11 - Name the type of materials typically used for...Ch. 11 - What are the advantages of pressure casting over...
Ch. 11 - List the advantages and limitations of die...Ch. 11 - What is the purpose of a riser? What is a blind...Ch. 11 - Explain the purpose of a vent and a runner in a...Ch. 11 - How are shell molds produced?Ch. 11 - What keeps the mold together in vacuum casting?Ch. 11 - What is squeeze casting? What are its advantages?Ch. 11 - What are the advantages of the lost-foam casting...Ch. 11 - Prob. 18RQCh. 11 - What are the reasons for the large variety of...Ch. 11 - Why are risers not as useful in die casting as...Ch. 11 - Describe the drawbacks to having a riser that is...Ch. 11 - Why can blind risers be smaller than open-top...Ch. 11 - Why does die casting produce the smallest cast...Ch. 11 - Why is the investment-casting process capable of...Ch. 11 - What differences, if any, would you expect in the...Ch. 11 - Recently, cores for sand casting have been...Ch. 11 - Would you recommend preheating the molds used in...Ch. 11 - Give reasons for, and examples of, using die...Ch. 11 - Referring to Fig. 11.3, do you think it is...Ch. 11 - Explain why squeeze casting produces parts with...Ch. 11 - How are the individual wax patterns attached on a...Ch. 11 - Describe the measures that you would take to...Ch. 11 - You have seen that, even though die casting...Ch. 11 - How are hollow parts with various cavities made by...Ch. 11 - It was stated that the strength-to-weight ratio of...Ch. 11 - How are risers and sprues placed in sand molds?...Ch. 11 - In shell-mold casting, the curing process is...Ch. 11 - Why does the die-casting machine shown in Fig....Ch. 11 - Prob. 39QLPCh. 11 - What are the benefits to heating the mold in...Ch. 11 - The slushy state of alloys refers to that state...Ch. 11 - Can a chaplet also act as a chill? Explain.Ch. 11 - Rank the casting processes described in this...Ch. 11 - Estimate the clamping force for a die-casting...Ch. 11 - In sand casting, it is important that the...Ch. 11 - If an acceleration of 100 g is necessary to...Ch. 11 - A jeweler wishes to produce 24 gold rings in one...Ch. 11 - Describe the procedures that would be involved in...Ch. 11 - The optimum shape of a riser is spherical to...Ch. 11 - Sketch and describe a casting line consisting of...Ch. 11 - Outline the casting processes that would be most...Ch. 11 - Make a list of the mold and die materials used in...Ch. 11 - Write a brief paper on the permeability of molds...Ch. 11 - Light metals commonly are cast in vulcanized...Ch. 11 - It sometimes is desirable to cool metals more...Ch. 11 - The part shown in Fig. P11.59 is a hemispherical...Ch. 11 - Porosity that has developed in the boss of a...Ch. 11 - In Fig. II.1b the gemstones have been cast in...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Which of these factors causes more porosity to form toward the interior of a casting rather than toward the outside? (a) Gasses are less soluble in the solid metal than the liquid, so solidified areas push dissolved gasses toward the interior. (b) Casting under a vacuum causes gasses near the liquid metal surface to be drawn out of the liquid during solidification. (c) The feeding structures of the mold are designed to force entrapped air into the center of the casting. (d) Draft on the mold wall forces air bubbles toward the interior of the solidifying metal. (e) None of the above Non-eutectic alloys (most commercial alloys) solidify over a temperature range. Which of the following statements explains how this affects the casting process. (a) Solidified non-eutectic alloys are especially difficult to remove from metal dies (b) Non-eutectic alloys have significantly less fluidity than pure metals or eutectic alloys. (c) Non-eutectic alloys solidify starting from the outside of the…arrow_forwardA flat plate is to be cast in an open mold whose bottom has a square shape that is 200 mm by 200 mm. The mold is 40 mm deep. A total of 106 mm3 of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.0%. The linear shrinkage due to thermal contraction after solidification is 1.3%. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its 200 mm by 200 mm dimensions until solidification is completed, determine the final dimensions of the plate.arrow_forwardIn turbine blade casting, how is a single-crystal structure achieved? Select one or more: a. By using a curving coil-like channel in the casting mould b. By removing grain boundaries by hot working and recrystallisation c. By careful control of the temperatures of the mould d. By introducing impurities into the molten alloy in the mouldarrow_forward
- 1-In hot forming processes, the strain rate is important since deformation resistance of w.p. increases as is increased. ****** 2-The coating of interior surfaces of casting molds can aid....... 3- Based on nature of use, the cores can be classified into: 1. and 2. ..... and 4-In centrifugal casting, fine grain microstructure (resisting to corrosion, better mechanical properties) castings can be obtained because of...... 5-During manufacturing processes, the residual stresses can be arising due to three major reasons: 1......, 2...... and 3...... 6- The wheels, pulleys and flywheels can be manufacturing by...... casting. 7- The ...... of casting molds can help removing impurities and facilitating metal flow inside the molds. 8-In horizontal true centrifugal casting, a tubular products having uniform wall thickness can be obtained when...... is greater than ......arrow_forward3. (Slow or Fast, which one? – Circle one) cooling rates results in coarse dendritic structures. 4. The higher the viscosity of the melt, the . its fluidity? 5. Name 3 defects in casting: 6. Internal or external are an effective means of reducing shrinkage porosity during solidification. 7. Is green-sand molding expensive? 8. .... are inserts placed in the molds to form the hollow regions in casting. 9. The method of casting turbine blades: Sample A 10. Which one has higher stiffness? Sample A or Sample B Sample B 11. Which one has higher toughness? Sample A or Sample B 12. Which one has higher strength? Sample A or Sample B 13. Which one has higher ductility? Sample A or Sample 14. Higher ......... means more rigidity. Strain 15. Before the no-slip point, the velocity is (higher or lower, which one? - Circle one) 16. In flat-rolling process, using smaller diameter rolls (increases or decreases, which one? - Circle one) the roll force. 17. Balls for ball bearings can be made by rolling…arrow_forwardI am in a hurry, I need the answer as soon as possible, please help.arrow_forward
- A flat plate is to be cast in an open mold whose bottom has a square shape of 12.5 cm by 12.5 cm. The mold is 7.0 cm deep. A total of 350 cm³ of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.25%, which is a volumetric contraction, not a linear contraction. Table 7.1 lists the linear shrinkage due to thermal contraction after solidification. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its square dimension until solidification is completed, determine the final dimensions (width and height) of the plate.arrow_forward(9,00 Puanlar) A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with 8- length 50 cm, width = 35 cm, and thickness = 4 cm. If the total solidification time of the casting itself is known to be 7,5 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify. %3D Riser volume: V3(TD3)/6(D%3Ddiameter) Riser area: A=TD2 Casting volume: V-L-Wt (L-Length, W=width, t-thickness) a) 8,41 cm b) O 7,34 cm c) 6.62 cm 11,46 cm Boş bırak KÖnceki 8/43 Sonraki> Каpatarrow_forwardEX.3//A cylindrical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 7.5 cm x 12.5 cm x 2.0 cm. Previous observations have indicated that the total solidification time (TTs) for this casting =1.6 min. The cylinder for the riser will have a diameter-to-height ratio=1.0. Determine the dimensions of the riser so that its TTS = 2.0 min.arrow_forward
- Parvinbhaiarrow_forwardA riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 100 mm, width = 50 mm, and thickness = 10 mm. If the total solidification time of the casting itself is known to be 2.5 min, determine the diameter of the riser so that it will take 20% longer for the riser to solidify. %3D %3!arrow_forwarda riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Casting Metal: the Basics; Author: Casting the Future;https://www.youtube.com/watch?v=2CIcvB72dmk;License: Standard youtube license