Textbook Question
Chapter 1, Problem 46QTP
A technician determines that the grain size of a certain etched specimen is 8. Upon further checking, it is found that the magnification used was 125 x, instead of the 100 x that is required by the ASTM standards. Determine the correct grain size.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
If a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force direction) at a tensile stress of 50 MPa, slip will occur in the [0 1 1] direction on the (1 1 -1) plane. Use this information to answer the following questions.
Which of the following is the critical resolved shear stress on the slip plane in the slip direction?
Group of answer choices
24.49 MPa
34.65 MPa
12.25 MPa
102 MPa
You are called as an expert witness to analyze the fracture of a sintered silicon carbide plate that was fractured in bending when a blunt load was applied to the plate center. Measurement of the distance between the fracture origin and the mirror/mist boundary on the fracture surface gives a radius of 0.796 mm. You are given three pieces of the same SiC to test, and you determine that the mirror radius is 0.603, 0.203, and 0.162 mm for bending failure stress levels of 225, 368, and 442 MPa, respectively. What is your estimate of the stress present at the time of fracture for the original plate?
which is correct?
53.2 mm , 1.1 mm , 121.4 mm, 22.2 mm ,11.1 mm
Chapter 1 Solutions
Manufacturing Engineering & Technology
Ch. 1 - What is the difference between an atom and a...Ch. 1 - Prob. 2RQCh. 1 - Prob. 3RQCh. 1 - Prob. 4RQCh. 1 - Define anisotropy. What is its significance?Ch. 1 - What effects does recrystallization have on the...Ch. 1 - What is strain hardening, and what effects does it...Ch. 1 - Explain what is meant by structure-sensitive and...Ch. 1 - Prob. 9RQCh. 1 - What influence does grain size have on the...
Ch. 1 - What is the relationship between the nucleation...Ch. 1 - What is a slip system, and what is its...Ch. 1 - Explain the difference between recovery and...Ch. 1 - What is hot shortness, and what is its...Ch. 1 - Explain the advantages and limitations of cold,...Ch. 1 - Describe what the orange peel effect is. Explain...Ch. 1 - Some metals, such as lead, do not become stronger...Ch. 1 - Describe the difference between preferred...Ch. 1 - Differentiate between stress relaxation and stress...Ch. 1 - What is twinning? How does it differ from slip?Ch. 1 - Prob. 21QLPCh. 1 - What is the significance of the fact that some...Ch. 1 - Is it possible for two pieces of the same metal to...Ch. 1 - Prob. 24QLPCh. 1 - A cold-worked piece of metal has been...Ch. 1 - What materials and structures can you think of...Ch. 1 - Two parts have been made of the same material, but...Ch. 1 - Do you think it might be important to know whether...Ch. 1 - Explain why the strength of a polycrystalline...Ch. 1 - Describe the technique you would use to reduce the...Ch. 1 - What is the significance of the fact that such...Ch. 1 - Prob. 32QLPCh. 1 - It has been noted that the more a metal has been...Ch. 1 - Is it possible to cold work a metal at...Ch. 1 - Comment on your observations regarding Fig. 1.14.Ch. 1 - Is it possible for a metal to be completely...Ch. 1 - Prob. 37QTPCh. 1 - Prob. 38QTPCh. 1 - Plot the data given in Table 1.1 in terms of...Ch. 1 - A strip of metal is reduced from 30 mm in...Ch. 1 - Prob. 41QTPCh. 1 - How many grains are there on the surface of the...Ch. 1 - Prob. 43QTPCh. 1 - Prob. 44QTPCh. 1 - Prob. 45QTPCh. 1 - A technician determines that the grain size of a...Ch. 1 - If the diameter of the aluminum atom is 0.28 nm,...Ch. 1 - The following data are obtained in tension tests...Ch. 1 - Prob. 50QTPCh. 1 - Prob. 51QTPCh. 1 - Prob. 52QTPCh. 1 - Same as Prob. 1.39, but ASTM no. versus...Ch. 1 - By stretching a thin strip of polished metal, as...Ch. 1 - Draw some analogies to mechanical fiberingfor...Ch. 1 - Draw some analogies to the phenomenon of hot...Ch. 1 - Take a deck of playing cards, place a rubber band...Ch. 1 - Give examples in which anisotropy is scale...Ch. 1 - The movement of an edge dislocation was described...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- The fine grains have lower toughness than coarse grains. Select one: True Falsearrow_forwardFrom the grain distribution curve, D60 = 1.45 mm, D30 = 0.75 mm and D10 = 0.45 mm. Determine the coefficient of gradation.arrow_forwardanswer must be in handwritten format or you can use Ms word but please do not typearrow_forward
- Do not answer in image format. Answer completely.arrow_forwardDetermine the ASTM grain size number of a metal specimen if 25 grains per square inch are measured at a magnification of 100x Solution please. Thankyouarrow_forwardQUESTION 8 A small component is made from aluminium 7475 where Kc = 35.2 MPa m 1/2 Non-destructive testing by micro-computed tomography showed the component to contain cracks of up to 2a = 0.05 mm in length. Laboratory tests showed the crack growth rate under cyclic loading is given by: Where A= 1.10x10-13 Assuming that: da dN = ΑΔΚΑ (MN m-2)-4 m-1 and the component is subjected to an alternating stress of range A = 180 MPa about a mean tensile stress of 40/2. ΔΚ = Δονπα Calculate the number of cycles to failure, give your answer in number of 1000s of cycles to 3 significant figures (e.g. 101,000 cycles would be inputted as 101)arrow_forward
- Request: Can you please help me with answering the following question? Thank you. Question: A specimen of a ceramic material having an elastic modulus of 250 GPa (36.3 x 106 psi) is pulled in tension with a stress of 750 MPa (109,000 psi). Will the specimen fail if its “most severe flaw” is an internal crack that has a length of 0.20 mm (7.87 x 10-3 in.) and a tip radius of curvature of 0.001 mm (3.94 x 10-5 in.)? Why or why not?arrow_forward2.) Two previously undeformed specimens of the same metal are to be plastically deformed by reducing their cross-sectional areas. One has a circular cross section, and the other is rectangular; during deformation the circular cross section is to remain circular, and the rectangular is to remain as such. Their original and deformed dimensions are as follows: Circular Rectangular (diameter, mm) (тm) Original dimensions Deformed dimensions 18.0 20 x 50 15.9 13.7 × 55.1 Which of these specimens will be the hardest after the plastic deformation? a) The deformed circular specimen will be harder b) The deformed rectangular specimen will be harder c) Both will have the same hardness d) Both would brake e) No estimation can be made for such processarrow_forwardNeed help on this Qarrow_forward
- Q2:- The part of the vehicle is production from an magnesium alloy .if KIC 40 MPavm. The fracture occurred at a pressure of 195 MPa when the maximum edge crack length was 3.0 mm. Calculate the value Y. If a stress levelis increased to 275 MPa and the maximum edge crack length is reduced to 2.3 mm, predict whether any fracture will occur. Compare your answer with existing data. Justify your answer.arrow_forwardPlease show all the work. Material science question, Don't use chatgpt for this question.arrow_forwardThe following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 158 kN. - Length of the specimen is 26 mm. - The yield strength is 75 kN/mm?. - The percentage of elongation is 40 %. Determine the following (v) Final diameter if the percentage of reduction in area is 21 %. Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Explanation of Solidification of Metals & Alloys | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=G5z9KknF_s8;License: Standard Youtube License