Question
Chapter 1, Problem 32QLP
To determine
Explain the difference that it was mentioned that twinning usually occurs in HCP materials, but Fig. 1.6b shows twinning in a rectangular array of atoms.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
The mechanical properties of cobalt may be improved by incorporating fine particles of tungsten carbide (WC). Given that the modulus of elasticity of these materials is 200 GPa and
700 GP, respectively. Plot modulus of elasticity versus the volume percent of WC in Co from 0 to 100 vol%, using both upper- and lower-bound expressions.
1. In engineering, why is the density of a particular engineering substance so crucial? Clearly explain.
2. What do the terms "single crystal" and "polycrystalline substance" mean? Briefly compare and contrast them.
3. Describe how x-ray diffraction is used to quantify elastic strain.
Please answer all with full detail, Thank you
The mechanical properties of cobalt may be improved by incorporating fine particles of tungsten carbide (WC). Given that the modulus of elasticity of these materials is 200 GPa and 700 GP, respectively. Plot modulus of elasticity versus the volume percent of WC in Co from 0 to 100 vol%, using both upper- and lower-bound expressions.
And explain what you have plotted.
Chapter 1 Solutions
Manufacturing Engineering & Technology
Ch. 1 - What is the difference between an atom and a...Ch. 1 - Prob. 2RQCh. 1 - Prob. 3RQCh. 1 - Prob. 4RQCh. 1 - Define anisotropy. What is its significance?Ch. 1 - What effects does recrystallization have on the...Ch. 1 - What is strain hardening, and what effects does it...Ch. 1 - Explain what is meant by structure-sensitive and...Ch. 1 - Prob. 9RQCh. 1 - What influence does grain size have on the...
Ch. 1 - What is the relationship between the nucleation...Ch. 1 - What is a slip system, and what is its...Ch. 1 - Explain the difference between recovery and...Ch. 1 - What is hot shortness, and what is its...Ch. 1 - Explain the advantages and limitations of cold,...Ch. 1 - Describe what the orange peel effect is. Explain...Ch. 1 - Some metals, such as lead, do not become stronger...Ch. 1 - Describe the difference between preferred...Ch. 1 - Differentiate between stress relaxation and stress...Ch. 1 - What is twinning? How does it differ from slip?Ch. 1 - Prob. 21QLPCh. 1 - What is the significance of the fact that some...Ch. 1 - Is it possible for two pieces of the same metal to...Ch. 1 - Prob. 24QLPCh. 1 - A cold-worked piece of metal has been...Ch. 1 - What materials and structures can you think of...Ch. 1 - Two parts have been made of the same material, but...Ch. 1 - Do you think it might be important to know whether...Ch. 1 - Explain why the strength of a polycrystalline...Ch. 1 - Describe the technique you would use to reduce the...Ch. 1 - What is the significance of the fact that such...Ch. 1 - Prob. 32QLPCh. 1 - It has been noted that the more a metal has been...Ch. 1 - Is it possible to cold work a metal at...Ch. 1 - Comment on your observations regarding Fig. 1.14.Ch. 1 - Is it possible for a metal to be completely...Ch. 1 - Prob. 37QTPCh. 1 - Prob. 38QTPCh. 1 - Plot the data given in Table 1.1 in terms of...Ch. 1 - A strip of metal is reduced from 30 mm in...Ch. 1 - Prob. 41QTPCh. 1 - How many grains are there on the surface of the...Ch. 1 - Prob. 43QTPCh. 1 - Prob. 44QTPCh. 1 - Prob. 45QTPCh. 1 - A technician determines that the grain size of a...Ch. 1 - If the diameter of the aluminum atom is 0.28 nm,...Ch. 1 - The following data are obtained in tension tests...Ch. 1 - Prob. 50QTPCh. 1 - Prob. 51QTPCh. 1 - Prob. 52QTPCh. 1 - Same as Prob. 1.39, but ASTM no. versus...Ch. 1 - By stretching a thin strip of polished metal, as...Ch. 1 - Draw some analogies to mechanical fiberingfor...Ch. 1 - Draw some analogies to the phenomenon of hot...Ch. 1 - Take a deck of playing cards, place a rubber band...Ch. 1 - Give examples in which anisotropy is scale...Ch. 1 - The movement of an edge dislocation was described...
Knowledge Booster
Similar questions
- Calculate the residual molar entropy for molecular crystals of 1,3,5-Trichlorobenzenearrow_forward1. Calculate the shear stress of aluminum material with shear modulus of 24 GPa, displace 0.2 cm along the x-direction. www The interatomic spacing between the atoms is 3.2 mm. (arrow_forwardCeramics materials have high temperature .. . resistance due to إجابتك The attraction force of the metallic bonds is depended on إجابتك the principal regions of a .. . macrostructure are إجابتك A substitutional defect is introduced when إجابتك The solubility of carbon in austenite is greater than to that of ferrite is due to إجابتكarrow_forward
- Nylon 6,6 is a thermoplastic polymer with high mechanical strength, high resistance to chemical environments, and good stability under heat. Therefore, it is well suited to be used in 3D structural objects. A cylindrical nylon 6,6 pipe is made by injection molding. The pipe is 1 m long with an outer diameter of 8cm, and a thickness of 2mm. The crystallinity of the pipe is 25%. The density and associated percent crystallinity for two nylon 6,6 samples are measured as below: ρ(g/cm3) crystallinity (%) 1.190 67 1.155 44 Calculate the density of this pipe, which has 25% crystallinity.arrow_forwardNylon 6,6 is a thermoplastic polymer with high mechanical strength, high resistance to chemical environments, and good stability under heat. Therefore, it is well suited to be used in 3D structural objects. A cylindrical nylon 6,6 pipe is made by injection molding. The pipe is 1 m long with an outer diameter of 8cm, and a thickness of 2mm. The crystallinity of the pipe is 25%. The density and associated percent crystallinity for two nylon 6,6 samples are measured as below: ρ(g/cm3) crystallinity (%) 1.190 67 1.155 44 If the degree of polymerization is 500, calculate the number of chains in the pipe. (Assume the chains are equal in length).arrow_forward(a) At the atomic level, how deformation process occurs/proceeds? (b) If we have the same materials in two different forms as a single crystal and as a polycrystalline sample, which one would have higher internal energy? Why? (c) Determine miller indices for the plane shown in red. Show your work to clarify how you came up with your answer.arrow_forward
- Metallic Crystal Structures1. For the HCP crystal structure, show that the ideal c/a ratio is 1.633. 2. Show that the atomic packing factor for HCP is 0.74.arrow_forwardZinc crystallizes in HCP structure. Geometrically the height of the unit cell is 43.4378 x10^-8 cm 4.34378x 10^-8 cm 2.1718 x10^-8cm data insufficientarrow_forward(a). Graphite and diamond are both made from carbon atoms. Kedua-dua grafit dan intan adalah diperbuat dari atom-atom karbon. (). List TWO physical characteristic of each material. Senaraikan DUA sifat-sifat fizikal bagi kedua-dua bahan tersebut (ii) Give ONE application for graphite and ONE for diamond Berikan SATU penggunaan bagi grafit dan SATU penggunaan bagi intan (ii). If both materials are made of carbon, why does such a difference in properties exist? Jika kedua-dua bahan tersebut diperbuat daripada karbon. jelaskan kenapa perbezaan ke atas sifat-sifat ini wujud?arrow_forward
- Metals and their alloys possess crystalline structures that may be altered to change their mechanical properties. Illustrate, with the aid of a diagram, substitutional ANDarrow_forwardTwo processes are used to produce polycrystalline Al2O3. In the first process the grain size is 10 μm, and in the second case it is 40 μm. Compute the ASTM grain size for each of these structuresarrow_forwardCommon aluminum foil for household use is nearly pure aluminum. A box of this product at a local supermarket is advertised as giving 75 ft°of material (in a roll 304 mm wide by 22.8 m long). If the foil is 0.5 mil (12.7 µm) thick, calculate the number of atoms of aluminum in the roll. Given: Density of Aluminum: p= 2.7 Mg/m³ Molar mass of Aluminum: MAI= 26.98 g/mol Avogadro's Number: AN = 0.6203 (10)²ªarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY