Question
Chapter 4, Problem 4.9P
To determine
The density of nickel at
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
2. In a copper-nickel system as shown in figure, an alloy composition of 35 wt% Ni was
cooled down from the temperature of 1300°C. Sketch the expected microstructures at
the point a, b, c, d and e and briefly describe the development of these microstructures
in the equilibrium cooling.
L.
L
(35 Ni)
1300
L (32 Ni)
a (46 Ni)
a(43 Ni)
L (24 Ni)
d
1200
1100
20
30
40
50
Composition (wt% Ni)
Temperature (°C))
(9A metal rod made of some alloy is to be used as a thermometer. At OoC its length is
40000cm, and at 1000C its length is 40060cm. (a) What is the linear expansion
coefficient of the alloy? (b) what is the temperature when its length is 39975cm?
1 If the particle formed at the sine of the liquid were a cylinder whose diameter is equal to its height, obtain the optimal height and then the critical Gibbs free energy
Explain all steps
Chapter 4 Solutions
Materials Science And Engineering Properties
Ch. 4 - Prob. 1CQCh. 4 - Prob. 2CQCh. 4 - Prob. 3CQCh. 4 - Prob. 4CQCh. 4 - Prob. 5CQCh. 4 - Prob. 6CQCh. 4 - Prob. 7CQCh. 4 - Prob. 8CQCh. 4 - Prob. 9CQCh. 4 - Prob. 10CQ
Ch. 4 - Prob. 11CQCh. 4 - Prob. 12CQCh. 4 - Prob. 13CQCh. 4 - Prob. 14CQCh. 4 - Prob. 15CQCh. 4 - Prob. 16CQCh. 4 - Prob. 17CQCh. 4 - Prob. 18CQCh. 4 - Prob. 19CQCh. 4 - Prob. 20CQCh. 4 - Prob. 21CQCh. 4 - Prob. 22CQCh. 4 - Prob. 23CQCh. 4 - Prob. 24CQCh. 4 - Prob. 25CQCh. 4 - Prob. 26CQCh. 4 - Prob. 27CQCh. 4 - Prob. 28CQCh. 4 - Prob. 29CQCh. 4 - Prob. 30CQCh. 4 - Prob. 31CQCh. 4 - Prob. 32CQCh. 4 - Prob. 33CQCh. 4 - Prob. 34CQCh. 4 - Prob. 35CQCh. 4 - Prob. 36CQCh. 4 - Prob. 37CQCh. 4 - Prob. 38CQCh. 4 - Prob. 39CQCh. 4 - Prob. 40CQCh. 4 - Prob. 41CQCh. 4 - Prob. 42CQCh. 4 - Prob. 43CQCh. 4 - Prob. 1ETSQCh. 4 - Prob. 2ETSQCh. 4 - Prob. 3ETSQCh. 4 - Prob. 4ETSQCh. 4 - Prob. 5ETSQCh. 4 - Prob. 6ETSQCh. 4 - Prob. 7ETSQCh. 4 - Prob. 1DRQCh. 4 - Prob. 4.1PCh. 4 - Prob. 4.2PCh. 4 - Prob. 4.3PCh. 4 - Prob. 4.4PCh. 4 - Prob. 4.5PCh. 4 - Prob. 4.6PCh. 4 - Prob. 4.7PCh. 4 - Prob. 4.8PCh. 4 - Prob. 4.9PCh. 4 - Prob. 4.10PCh. 4 - Prob. 4.11PCh. 4 - Prob. 4.12PCh. 4 - Prob. 4.13PCh. 4 - Prob. 4.14PCh. 4 - Prob. 4.15PCh. 4 - Prob. 4.16PCh. 4 - Prob. 4.17PCh. 4 - Prob. 4.18PCh. 4 - Prob. 4.19PCh. 4 - Prob. 4.20PCh. 4 - Prob. 4.21PCh. 4 - Prob. 4.22PCh. 4 - Prob. 4.23PCh. 4 - Prob. 4.24PCh. 4 - Prob. 4.25P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- H.W3: Predict the ideal solubility of lead in bismuth at 280°C given that its melting point is 327°C and its enthalpy of fusion is 5.2 kJ mol-1, M.wt Bi=209 g/mol, M.wt Pb=209 g/mol.arrow_forwardRPSIIIarrow_forward26) Given the T-T-T curve below, select the process that will result in a microstructure of nearly all bainite. a. Cool to 400°C, hold for 20 seconds, then quench to room temperature b. Cool to 500°C, hold for 10 seconds, then quench to room temperature c. Quench to 125°C, hold for 10 seconds, then reheat to 600°C for more than 100 seconds d. Cool to 725°C, hold for 1,000 seconds, then quench to 125°C e. Cool to 600°C, hold for 1 second, the quench to room temperature Temperature (°C) f. none of the above 900 800 H A+C 1600 1400 700- 1200 A+P 600 P 1000 500H A+B 800 400- Temperature (°F) 4 A 300- M(start) 200 M(50%) 100- M(90%) 600 50% T 0 1 10 102 103 10 105 106 Time (s) 400 200 27) Fatigue failure situations are typically dependent upon which combination of the following factors? a. Slip plane, slip direction, and orientation of the applied load b. Yield strength, elastic modulus, and ductility of the material c. Temperature, time, and applied stress d. Stress amplitude, frequency of…arrow_forward
- 26) Given the T-T-T curve below, select the process that will result in a microstructure of nearly all bainite. C. Cool to 400°C, hold for 20 seconds, then quench to room temperature Cool to 500°C, hold for 10 seconds, then quench to room temperature Quench to 125°C, hold for 10 seconds, then reheat to 600°C for more than 100 seconds d. Cool to 725°C, hold for 1,000 seconds, then quench to 125°C Cool to 600°C, hold for 1 second, the quench to room temperature f. none of the above 900 Temperature (°C) 800 A+C 700 A+P 600 500 A+B 400 A 300 200 M(start) M(50%) 100 M(90%) TT 1600 1400 1200 1000 800 600 50% 0 1 10 102 103 104 105 106 Time(s) 400 200 Temperature (°F) 27) Fatigue failure situations are typically dependent upon which combination of the following factors? Slip plane, slip direction, and orientation of the applied load b. Yield strength, elastic modulus, and ductility of the material c. Temperature, time, and applied stress d. Stress amplitude, frequency of loading, and number…arrow_forwardAn aluminum pipe has a length of 69 m at a temperature of 8°C. An adjacent steel pipe at the same temperature is 5 mm longer. At what temperature will the aluminum pipe be 15 mm longer than the steel pipe? Assume that the coefficient of thermal expansion for the aluminum is 22.5×10-6/°C and that the coefficient of thermal expansion for the steel is 12.5×10-6/°C.arrow_forwardWhich material has a higher linear coefficient of thermal expansion? A Teflon B Titanium ) Medium-carbon steel D Soda lime glassarrow_forward
- I need the answer as soon as possiblearrow_forward-A rod 3 m long is heated from (10 to 90) °C, if the modulus of elasticity equal to 10000O MN/m2, and coefficient of thermal expansion = 0.000012 per °C, the new long of rod after expansion is 0.168 cm 0.288 cm 0.208 cm 0.348 cm 0.388 cm Other:arrow_forwardAn aluminum pipe has a length of 60 m at a temperature of 10° C. An adjacent steel pipe at the same temperature is 5 mm longer than the aluminum pipe. At what temperature (degrees Celsius) will the aluminum pipe be 15 mm longer than the steel pipe? (Assume that the coefficients of thermal expansion of aluminum and steel are aAL=23x 10^-6°C and as=12x10^-6° C respectively)arrow_forward
- An aluminum pipe with a length of 60 m at a temperature of 10°C rests freely on the ground. An adjacent steel pipe at the same temperature is 5 mm longer than the aluminum pipe. (a) At what temperature (degrees Celsius) will the aluminum pipe be 15 mm longer than the steel pipe? (Assume that the coefficients of thermal expansion of aluminum and steel are ca=23x10-6/°C and as=12x10-6/°C, respectively.) (b) What is the axial stress developed in the aluminum pipe when the temperature was increased? Aluminun Steel Figure No. 1 5 mmarrow_forwardAn aluminum pipe has a length of 75 m at a temperature of 18°C. An adjacent steel pipe at the same temperature is 0.005 m longer than the aluminum pipe. At what temperature (0C) will the aluminum pipe be 0.015 mm longer than the steel pipe? (Assume that the coefficients of thermal expansion of aluminum and steel are aa = 23 x 10–6/°C and as = 12 x 10–6/°C, respectively.)arrow_forwardAn aluminum pipe with a length of 60 m at a temperature of 10°C rests freely on the ground. An adjacent steel pipe at the same temperature is 5 mm longer than the aluminum pipe. (a) At what temperature (degrees Celsius) will the aluminum pipe be 15 mm longer than the steel pipe? (Assume that the coefficients of thermal expansion of aluminum and steel are a=23x10-6/°C and as-12x10-6/ c, respectively.) (b) What is the axial stress developed in the aluminum pipe when the temperature was increased? 5 mm Aluminun Steel Figure No. 1arrow_forward
arrow_back_ios
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning