Materials Science And Engineering Properties
1st Edition
ISBN: 9781111988609
Author: Charles Gilmore
Publisher: Cengage Learning
expand_more
expand_more
format_list_bulleted
Question
Chapter 4, Problem 4.25P
To determine
(a)
The entropy of mixing.
To determine
(b)
The enthalpy of the mixture at 373 K.
To determine
(c)
The change in Gibbs free energy.
To determine
(d)
The mixing condition of the two polymers.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
2. In a copper-nickel system as shown in figure, an alloy composition of 35 wt% Ni was
cooled down from the temperature of 1300°C. Sketch the expected microstructures at
the point a, b, c, d and e and briefly describe the development of these microstructures
in the equilibrium cooling.
L.
L
(35 Ni)
1300
L (32 Ni)
a (46 Ni)
a(43 Ni)
L (24 Ni)
d
1200
1100
20
30
40
50
Composition (wt% Ni)
Temperature (°C))
At 170°C, what is the maximum solubility (a) of Pb in Sn and (b) of Sn in Pb?
The lead-tin phase diagram is shown in the Animated Figure 9.8.
(a)
wt% Pb
(b)
i
wt% Sn
For alloys of two hypothetical metals A and B, there exist an a, A-rich phase and a ß, B-rich phase.
From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine
the composition of the phase boundary (or solubility limit) for the following:
Fraction Fraction
Alloy Composition
a Phase
B Phase
60 wt% A - 40 wt% B
0.59
0.41
30 wt% A - 70 wt% B
0.13
0.87
(a) a phase
wt% A
(b) B phase
wt% A
Chapter 4 Solutions
Materials Science And Engineering Properties
Ch. 4 - Prob. 1CQCh. 4 - Prob. 2CQCh. 4 - Prob. 3CQCh. 4 - Prob. 4CQCh. 4 - Prob. 5CQCh. 4 - Prob. 6CQCh. 4 - Prob. 7CQCh. 4 - Prob. 8CQCh. 4 - Prob. 9CQCh. 4 - Prob. 10CQ
Ch. 4 - Prob. 11CQCh. 4 - Prob. 12CQCh. 4 - Prob. 13CQCh. 4 - Prob. 14CQCh. 4 - Prob. 15CQCh. 4 - Prob. 16CQCh. 4 - Prob. 17CQCh. 4 - Prob. 18CQCh. 4 - Prob. 19CQCh. 4 - Prob. 20CQCh. 4 - Prob. 21CQCh. 4 - Prob. 22CQCh. 4 - Prob. 23CQCh. 4 - Prob. 24CQCh. 4 - Prob. 25CQCh. 4 - Prob. 26CQCh. 4 - Prob. 27CQCh. 4 - Prob. 28CQCh. 4 - Prob. 29CQCh. 4 - Prob. 30CQCh. 4 - Prob. 31CQCh. 4 - Prob. 32CQCh. 4 - Prob. 33CQCh. 4 - Prob. 34CQCh. 4 - Prob. 35CQCh. 4 - Prob. 36CQCh. 4 - Prob. 37CQCh. 4 - Prob. 38CQCh. 4 - Prob. 39CQCh. 4 - Prob. 40CQCh. 4 - Prob. 41CQCh. 4 - Prob. 42CQCh. 4 - Prob. 43CQCh. 4 - Prob. 1ETSQCh. 4 - Prob. 2ETSQCh. 4 - Prob. 3ETSQCh. 4 - Prob. 4ETSQCh. 4 - Prob. 5ETSQCh. 4 - Prob. 6ETSQCh. 4 - Prob. 7ETSQCh. 4 - Prob. 1DRQCh. 4 - Prob. 4.1PCh. 4 - Prob. 4.2PCh. 4 - Prob. 4.3PCh. 4 - Prob. 4.4PCh. 4 - Prob. 4.5PCh. 4 - Prob. 4.6PCh. 4 - Prob. 4.7PCh. 4 - Prob. 4.8PCh. 4 - Prob. 4.9PCh. 4 - Prob. 4.10PCh. 4 - Prob. 4.11PCh. 4 - Prob. 4.12PCh. 4 - Prob. 4.13PCh. 4 - Prob. 4.14PCh. 4 - Prob. 4.15PCh. 4 - Prob. 4.16PCh. 4 - Prob. 4.17PCh. 4 - Prob. 4.18PCh. 4 - Prob. 4.19PCh. 4 - Prob. 4.20PCh. 4 - Prob. 4.21PCh. 4 - Prob. 4.22PCh. 4 - Prob. 4.23PCh. 4 - Prob. 4.24PCh. 4 - Prob. 4.25P
Knowledge Booster
Similar questions
- TRUE OR FALSE The viscosity of liquids will increase if the temperature is increased.arrow_forwardA sheet of BCC iron 1 mm thick was exposed to a carburizing gas atmosphere on one side and a decarburizing atmosphere on the other side at 725°C. After having reached steady state, the iron was quickly cooled to room temperature. The carbon concentrations at the two surfaces of the sheet were determined to be 0.012 and 0.0075 wt%. Compute the diffusion coefficient if the diffusion flux is 1.4 × 10-8 kg/m2 -s.arrow_forwardCa+2 = 36.8mg/L Mg+2 = 2.9mg/L HCO3 = 98mg/L pH = 7.53 Temp = 9C Calculate the following: a. Hardness in units of mg/L as CaCO3 b. Ionic strength (be sure to include H++ and OH--) c. PCO2 in equilibrium with the sample d. Saturation index with respect to calcite (SIC) e. Saturation index with respect to dolomite (SID)arrow_forward
- If the Ksp of Sn(OH)2 (s) is 5.33 x 10-27, what is the solubility of it in the unit of mg/L?arrow_forwardAn aluminum pipe has a length of 53 m at a temperature of 7°C. An adjacent steel pipe at the same temperature is 7 mm longer. At what temperature will the aluminum pipe be 21 mm longer than the steel pipe? Assume that the coefficient of thermal expansion for the aluminum is 22.5x10-6/°C and that the coefficient of thermal expansion for the steel is 12.5×106/°C. Answer: Tf = i °Carrow_forwardA magnesium-lead alloy of mass 6.4 kg consists of a solid a phase that has a composition just slightly below the solubility limit at 300°C (570°F). The magnesium-lead phase diagram is shown in Animated Figure 9.20. (a) What mass of lead is in the alloy? i kg (b) If the alloy is heated to 400°C (750°F), how much more lead may be dissolved in the a phase without exceeding the solubility limit of this phase? kgarrow_forward
- Assumptions: • Density of Al Cu phase is 4.34 g/cm3 • Density of alpha phase is 2.8 g/cm3 • Assume composition of alpha is 5 wt% Cu • Assume composition of AlCu phase is 53 wt% Cu To-do: • What is the bulk composition of the unknown sample? • Use the lever rule method and the help of the phase diagram to determine this.arrow_forwardPlease help me in 6. Thank you!!!arrow_forwardQ.1. For hypereutectoid plain carbon steel (select %C content yourself), determine the phases that are present, the compositions of these phases, and the percentages or fractions of the phases. Make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: a) Just above the austenite transformation temperature b) The austenite transformation temperature 10°C c) The eutectoid transformation temperature +10°C d) The eutectoid transformation temperature 10°Carrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning