Question
Chapter 4, Problem 17CQ
To determine
The value of the coefficient of thermal expansion, when a material with an interatomic potential is symmetric about the equilibrium interatomic separation.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
2. In a copper-nickel system as shown in figure, an alloy composition of 35 wt% Ni was
cooled down from the temperature of 1300°C. Sketch the expected microstructures at
the point a, b, c, d and e and briefly describe the development of these microstructures
in the equilibrium cooling.
L.
L
(35 Ni)
1300
L (32 Ni)
a (46 Ni)
a(43 Ni)
L (24 Ni)
d
1200
1100
20
30
40
50
Composition (wt% Ni)
Temperature (°C))
topic- solid mech.
A square high-density polyethylene [a = 158 × 10-6/°C] plate has a width of 295 mm. A 177 mm diameter circular hole is located at the
center of the plate. If the temperature of the plate increases by 45°C, determine:
(a) the change in width of the plate.
(b) the change in diameter of the hole.
Answer:
(a) Aw=
(b) Ad = i
i
mm
mm
Chapter 4 Solutions
Materials Science And Engineering Properties
Ch. 4 - Prob. 1CQCh. 4 - Prob. 2CQCh. 4 - Prob. 3CQCh. 4 - Prob. 4CQCh. 4 - Prob. 5CQCh. 4 - Prob. 6CQCh. 4 - Prob. 7CQCh. 4 - Prob. 8CQCh. 4 - Prob. 9CQCh. 4 - Prob. 10CQ
Ch. 4 - Prob. 11CQCh. 4 - Prob. 12CQCh. 4 - Prob. 13CQCh. 4 - Prob. 14CQCh. 4 - Prob. 15CQCh. 4 - Prob. 16CQCh. 4 - Prob. 17CQCh. 4 - Prob. 18CQCh. 4 - Prob. 19CQCh. 4 - Prob. 20CQCh. 4 - Prob. 21CQCh. 4 - Prob. 22CQCh. 4 - Prob. 23CQCh. 4 - Prob. 24CQCh. 4 - Prob. 25CQCh. 4 - Prob. 26CQCh. 4 - Prob. 27CQCh. 4 - Prob. 28CQCh. 4 - Prob. 29CQCh. 4 - Prob. 30CQCh. 4 - Prob. 31CQCh. 4 - Prob. 32CQCh. 4 - Prob. 33CQCh. 4 - Prob. 34CQCh. 4 - Prob. 35CQCh. 4 - Prob. 36CQCh. 4 - Prob. 37CQCh. 4 - Prob. 38CQCh. 4 - Prob. 39CQCh. 4 - Prob. 40CQCh. 4 - Prob. 41CQCh. 4 - Prob. 42CQCh. 4 - Prob. 43CQCh. 4 - Prob. 1ETSQCh. 4 - Prob. 2ETSQCh. 4 - Prob. 3ETSQCh. 4 - Prob. 4ETSQCh. 4 - Prob. 5ETSQCh. 4 - Prob. 6ETSQCh. 4 - Prob. 7ETSQCh. 4 - Prob. 1DRQCh. 4 - Prob. 4.1PCh. 4 - Prob. 4.2PCh. 4 - Prob. 4.3PCh. 4 - Prob. 4.4PCh. 4 - Prob. 4.5PCh. 4 - Prob. 4.6PCh. 4 - Prob. 4.7PCh. 4 - Prob. 4.8PCh. 4 - Prob. 4.9PCh. 4 - Prob. 4.10PCh. 4 - Prob. 4.11PCh. 4 - Prob. 4.12PCh. 4 - Prob. 4.13PCh. 4 - Prob. 4.14PCh. 4 - Prob. 4.15PCh. 4 - Prob. 4.16PCh. 4 - Prob. 4.17PCh. 4 - Prob. 4.18PCh. 4 - Prob. 4.19PCh. 4 - Prob. 4.20PCh. 4 - Prob. 4.21PCh. 4 - Prob. 4.22PCh. 4 - Prob. 4.23PCh. 4 - Prob. 4.24PCh. 4 - Prob. 4.25P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- Which material has a higher linear coefficient of thermal expansion? A Teflon B Titanium ) Medium-carbon steel D Soda lime glassarrow_forwardRPSIIIarrow_forward26) Given the T-T-T curve below, select the process that will result in a microstructure of nearly all bainite. a. Cool to 400°C, hold for 20 seconds, then quench to room temperature b. Cool to 500°C, hold for 10 seconds, then quench to room temperature c. Quench to 125°C, hold for 10 seconds, then reheat to 600°C for more than 100 seconds d. Cool to 725°C, hold for 1,000 seconds, then quench to 125°C e. Cool to 600°C, hold for 1 second, the quench to room temperature Temperature (°C) f. none of the above 900 800 H A+C 1600 1400 700- 1200 A+P 600 P 1000 500H A+B 800 400- Temperature (°F) 4 A 300- M(start) 200 M(50%) 100- M(90%) 600 50% T 0 1 10 102 103 10 105 106 Time (s) 400 200 27) Fatigue failure situations are typically dependent upon which combination of the following factors? a. Slip plane, slip direction, and orientation of the applied load b. Yield strength, elastic modulus, and ductility of the material c. Temperature, time, and applied stress d. Stress amplitude, frequency of…arrow_forward
- What is the Henry’s law constant in dimensionless form and atmospheres for a compound that has a Henry’s law constant of 2.0 atm/ (mol/L)? What is the dimensionless Henry’s law constant for a compound that has a value of 200 atm? Assume the temperature is 10? C.arrow_forward26) Given the T-T-T curve below, select the process that will result in a microstructure of nearly all bainite. C. Cool to 400°C, hold for 20 seconds, then quench to room temperature Cool to 500°C, hold for 10 seconds, then quench to room temperature Quench to 125°C, hold for 10 seconds, then reheat to 600°C for more than 100 seconds d. Cool to 725°C, hold for 1,000 seconds, then quench to 125°C Cool to 600°C, hold for 1 second, the quench to room temperature f. none of the above 900 Temperature (°C) 800 A+C 700 A+P 600 500 A+B 400 A 300 200 M(start) M(50%) 100 M(90%) TT 1600 1400 1200 1000 800 600 50% 0 1 10 102 103 104 105 106 Time(s) 400 200 Temperature (°F) 27) Fatigue failure situations are typically dependent upon which combination of the following factors? Slip plane, slip direction, and orientation of the applied load b. Yield strength, elastic modulus, and ductility of the material c. Temperature, time, and applied stress d. Stress amplitude, frequency of loading, and number…arrow_forwardScission can be defined as. a. The loss of fragments from the surfaces of ceramic materials due to internal or residual stress b. An increase in the volume of a polymeric materials caused by the absorption of glass or liquid. c. The formation of crystalline regions in amorphous network ceramics. d. The fracture of long chain molecules in polymers subjected to neutron irradiation or radiation by ultraviolet lightarrow_forward
- A 0.35-m long steel rod with a round cross-section (25 mm) is resting on a frictionless surface.The rod temperature is measured to be at 10°C. The plate is then heated uniformly to 97°C.The steel has a coefficient of thermal expansion equal to 1.1*10-5 m/m/°C.a) What is the length of expansion?b) Is there a stress on the rod?c) If the rod is snugly fitted against two immovable non-conducting walls at atemperature of 15°C and the heated uniformly to 115°C, what is its length at 115°C ifthe elastic modulus of steel is 205 GPa, what is the stress induced in the bar? Tensionor compression?arrow_forwardPeriod 6 is unusual in several ways.(a) It is the longest period in the table. How many elements be-long to Period 6? How many metals?(b) It contains no metalloids. Where is the metal/nonmetal boundary in Period 6?arrow_forwardThe reciprocal of density isarrow_forward
arrow_back_ios
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning