Question
Chapter 4, Problem 16CQ
To determine
The nature of the linear coefficient of thermal expansion for a polymer filament that is to be expected in the axial direction than in the transverse direction.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Give me right solution with clear calculations
Scission can be defined as.
a. The loss of fragments from the surfaces of ceramic materials due to
internal or residual stress
b. An increase in the volume of a polymeric materials caused by the
absorption of glass or liquid.
c. The formation of crystalline regions in amorphous network ceramics.
d. The fracture of long chain molecules in polymers subjected to neutron
irradiation or radiation by ultraviolet light
The assembly consists of a brass shell (1) fully bonded to a solid ceramic core (2).
The brass shell [E = 115 GPa, a = 18.7 × 10-6/°C] has dout 50mm. and din
= 35mm.
The ceramic core [E = 290 GPa, α = 3.1 x 10-6/°C] has a diameter dout = 35mm.
At a temperature of 15°C, the assembly is unstressed. AT = 60°C.
Find the internal stress in the brass.
=
200 mm
Brass shell (1)
(2) Ceramic core
Chapter 4 Solutions
Materials Science And Engineering Properties
Ch. 4 - Prob. 1CQCh. 4 - Prob. 2CQCh. 4 - Prob. 3CQCh. 4 - Prob. 4CQCh. 4 - Prob. 5CQCh. 4 - Prob. 6CQCh. 4 - Prob. 7CQCh. 4 - Prob. 8CQCh. 4 - Prob. 9CQCh. 4 - Prob. 10CQ
Ch. 4 - Prob. 11CQCh. 4 - Prob. 12CQCh. 4 - Prob. 13CQCh. 4 - Prob. 14CQCh. 4 - Prob. 15CQCh. 4 - Prob. 16CQCh. 4 - Prob. 17CQCh. 4 - Prob. 18CQCh. 4 - Prob. 19CQCh. 4 - Prob. 20CQCh. 4 - Prob. 21CQCh. 4 - Prob. 22CQCh. 4 - Prob. 23CQCh. 4 - Prob. 24CQCh. 4 - Prob. 25CQCh. 4 - Prob. 26CQCh. 4 - Prob. 27CQCh. 4 - Prob. 28CQCh. 4 - Prob. 29CQCh. 4 - Prob. 30CQCh. 4 - Prob. 31CQCh. 4 - Prob. 32CQCh. 4 - Prob. 33CQCh. 4 - Prob. 34CQCh. 4 - Prob. 35CQCh. 4 - Prob. 36CQCh. 4 - Prob. 37CQCh. 4 - Prob. 38CQCh. 4 - Prob. 39CQCh. 4 - Prob. 40CQCh. 4 - Prob. 41CQCh. 4 - Prob. 42CQCh. 4 - Prob. 43CQCh. 4 - Prob. 1ETSQCh. 4 - Prob. 2ETSQCh. 4 - Prob. 3ETSQCh. 4 - Prob. 4ETSQCh. 4 - Prob. 5ETSQCh. 4 - Prob. 6ETSQCh. 4 - Prob. 7ETSQCh. 4 - Prob. 1DRQCh. 4 - Prob. 4.1PCh. 4 - Prob. 4.2PCh. 4 - Prob. 4.3PCh. 4 - Prob. 4.4PCh. 4 - Prob. 4.5PCh. 4 - Prob. 4.6PCh. 4 - Prob. 4.7PCh. 4 - Prob. 4.8PCh. 4 - Prob. 4.9PCh. 4 - Prob. 4.10PCh. 4 - Prob. 4.11PCh. 4 - Prob. 4.12PCh. 4 - Prob. 4.13PCh. 4 - Prob. 4.14PCh. 4 - Prob. 4.15PCh. 4 - Prob. 4.16PCh. 4 - Prob. 4.17PCh. 4 - Prob. 4.18PCh. 4 - Prob. 4.19PCh. 4 - Prob. 4.20PCh. 4 - Prob. 4.21PCh. 4 - Prob. 4.22PCh. 4 - Prob. 4.23PCh. 4 - Prob. 4.24PCh. 4 - Prob. 4.25P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- An aluminum pipe has a length of 53 m at a temperature of 7°C. An adjacent steel pipe at the same temperature is 7 mm longer. At what temperature will the aluminum pipe be 21 mm longer than the steel pipe? Assume that the coefficient of thermal expansion for the aluminum is 22.5x10-6/°C and that the coefficient of thermal expansion for the steel is 12.5×106/°C. Answer: Tf = i °Carrow_forwardState two applications where single crystals are used as well as two applications of amorphous silicate glasses.arrow_forwardWhich material has a higher linear coefficient of thermal expansion? A Teflon B Titanium ) Medium-carbon steel D Soda lime glassarrow_forward
- ASK YOUR TEACHER PRACTICE ANOTHER Thin strips of copper and brass of equal length are used to construct a bimetallic strip. When the strip is heated, due to the difference in the coefficient of linear expansion of the two metals, the brass strip will have a greater increase in length than the copper strip, causing them to bend into an arc with the brass on the outside of the curve. When the temperature of the bimetallic strip increases by 25.0°C, the angle subtended by the two ends of the curved strip is 30.3° and the difference in the radius of curvature of the two strips is 1.55 x 103 cm. Determine the original length of the strip. The coefficients of linear expansion of copper and brass are 17 x 10-6/°C and 19 x 10-6/°C respectively. cm Savearrow_forwardthe cross-sectional area of the bar 1 of the two bars supported on the left and right sides is 1.2 cm^2, the coefficient of thermal expansion is 20.9 10^(-6)/K; The cross-sectional area of bar 2 is 3 cm^2 and its coefficient of thermal expansion is 25.4 10^(-6)/K. Since the modulus of elasticity of the material is 207 GPa, these two bars are heated to 99 °C.a) What will be the change in length (mm) of bar 1?b) What is the stress in bar 1 in MPa?c) What is the stress in bar 2 in MPa?arrow_forward9.5 The following thermal bimorph is made of Silicon with a thermal conductivity k = 130 W/(m°C), Young's modulus E = 200 GPa, Poisson's ratio v = 0.27, and ther- mal expansion coefficient a = 2.6 × 10-6/°C. It is 1 mm thick with fixed tempera- tures of 60°C and 10°C, respectively, at the leftmost ends of its hot arm and cold arm, as shown below. Suppose the bimorph has a uniform internal heat genera- tion at 100 W/m³, and ignore the effects of convective heat transfer. (1) Determine the steady-state temperature distribution in the thermal bimorph. (2) Determine the thermally induced deformation and stresses in the bimorph if the two arms are fixed on their left ends. Hot arm Thot = 60°C Cold arm Tcold = 10°C All dimensions are in millimeters. 6.000- 3.000 2.000 2.000 200 12.000 5.000 3.000arrow_forward
- At a temperature of 60°F, a 0.04-in. gap exists between the ends of the two bars shown. Bar (1) is an aluminum alloy [E = 10,000 ksi; v = 0.32; a = 12.3 × 106/°F] bar with a width of 3 in. and a thickness of 0.75 in. Bar (2) is a stainless steel [E = 28,000 ksi; v = 0.12; a = 8.9 x 10-6/°F] bar with a width of 2 in. and a thickness of 0.75 in. The supports at A and C are rigid. Determine the lowest temperature at which the two bars contact each other. (1) 3 in. 32 in. O 80.1°F O 118.6°F O 150.7°F O 132.9°F O 110.9°F B 2 in. 44 in. 0.04-in. gaparrow_forwardTwo similar bars of Steel and Aluminium are heated to a same temperature. Forces are applied at the ends of the bars to maintain their lengths unaltered. If the ratio of Young's moduli of Steel and Aluminium is 3, and the ratio of the coefficients of thermal expansion of Steel to that of Aluminium is 0.5, what is the stress on the Aluminium bar if the stress on the Steel bar is 100 MPa?arrow_forwardList the 12 slip systems for fec. which of these will not be active if a load is applied in [100] direction for a single crystal?arrow_forward
- At a temperature of 60°F, a 0.04-in. gap exists between the ends of the two bars shown in the figure. Bar (1) is an aluminum alloy (E-10,000 ksi; u= 0,32; a= 12.5 x10°/°F] bar with a width of 3 in, and a thickness of 0.75 in. Bar (2) is a stainless steel |E-28,000 ksi; u=0.12; a=9.6x10°/°F] bar with a width of 2 in. and a thickness of 0.75 in. The supports at A and C are rigid. Determine the normal stress in bar (1) at a temperature of 450°Farrow_forwardA 0.35-m long steel rod with a round cross-section (25 mm) is resting on a frictionless surface.The rod temperature is measured to be at 10°C. The plate is then heated uniformly to 97°C.The steel has a coefficient of thermal expansion equal to 1.1*10-5 m/m/°C.a) What is the length of expansion?b) Is there a stress on the rod?c) If the rod is snugly fitted against two immovable non-conducting walls at atemperature of 15°C and the heated uniformly to 115°C, what is its length at 115°C ifthe elastic modulus of steel is 205 GPa, what is the stress induced in the bar? Tensionor compression?arrow_forward6 A steel pipe with a 50 mm outside diameter and a 43.75 'mm inside diameter surrounds a solid brass rod 37.5 mm in diameter as shown. Both materials are joined to a rigid cover plate at each end. The assembly is free to expand longitudinally. The assembly is stress free at a temperature of 27°C. For steel, Young's modulus is 200 GN/m², and the coefficient of linear thermal expansion is 11.7x10-6 1/°C. For brass, Young's modulus is 93.33 GN/m², and the coefficient of linear thermal expansion is 1.872 x 10-5 1/°C. What is the stress in the steel tube when the temperature is raised to 121°C? brass rod (solid) 37.5 mm diameter steel tube 50 mm outside diameter 43.75 mm inside diameterarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY