Textbook Question
Chapter 2, Problem 59QTP
You are given the K and n values of two different metals. Is this information sufficient to determine which metal is tougher? If not, what additional information do you need?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Based on the stress-strain plots, which materials tested are stiff and which are tough? How can you tell the difference?
* we tested (Steel HR250)and (Aluminium 5251)in this experiment
Figure 2 shows the results of tensile tests performed on Alloys A and B. Interpret from
the curves shown the significant mechanical property difference between Alloys A and B.
A
Figure 2
What is the material used for the wire BC? Justify your answer
Chapter 2 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 2 - Distinguish between engineering stress and true...Ch. 2 - In a stress-strain curve, what is the proportional...Ch. 2 - Describe the events that take place when a...Ch. 2 - What is ductility, and how is it measured?Ch. 2 - In the equation =Kn, which represents the true...Ch. 2 - What is strain-rate sensitivity, and how is it...Ch. 2 - What test can measure the properties of a material...Ch. 2 - What testing procedures can be used to measure the...Ch. 2 - Describe the differences between brittle and...Ch. 2 - What is hardness? Explain.
Ch. 2 - Describe the features of a Rockwell hardness test.Ch. 2 - What is a Leeb test? How is it different from a...Ch. 2 - Differentiate between stress relaxation and creep.Ch. 2 - Describe the difference between elastic and...Ch. 2 - Explain what uniform elongation means in tension...Ch. 2 - Describe the difference between deformation rate...Ch. 2 - Describe the difficulties involved in conducting a...Ch. 2 - What is Hookes law? Youngs modulus? Poissons...Ch. 2 - Describe the difference between transgranular and...Ch. 2 - What is the reason that yield strength is...Ch. 2 - Why does the fatigue strength of a specimen or...Ch. 2 - If striations are observed under microscopic...Ch. 2 - What is an Izod test? Why are Izod tests useful?Ch. 2 - Why does temperature increase during plastic...Ch. 2 - What is residual stress? How can residual stresses...Ch. 2 - On the same scale for stress, the tensile true...Ch. 2 - What are the similarities and differences between...Ch. 2 - Can a material have a negative Poissons ratio?...Ch. 2 - It has been stated that the higher the value of m,...Ch. 2 - Explain why materials with high m values, such as...Ch. 2 - With a simple sketch, explain whether it is...Ch. 2 - Explain why the difference between engineering...Ch. 2 - Consider an elastomer, such as a rubber band. This...Ch. 2 - If a material (such as aluminum) does not have an...Ch. 2 - What role, if any, does friction play in a...Ch. 2 - Which hardness tests and scales would you use for...Ch. 2 - Consider the circumstance where a Vickers hardness...Ch. 2 - Which of the two tests, tension or compression,...Ch. 2 - List and explain briefly the conditions that...Ch. 2 - List the factors that you would consider in...Ch. 2 - On the basis of Fig. 2.5, can you calculate the...Ch. 2 - If a metal tension-test specimen is rapidly pulled...Ch. 2 - Comment on your observations regarding the...Ch. 2 - Will the disk test be applicable to a ductile...Ch. 2 - What hardness test is suitable for determining the...Ch. 2 - Wire rope consists of many wires that bend and...Ch. 2 - A statistical sampling of Rockwell C hardness...Ch. 2 - In a Brinell hardness test, the resulting...Ch. 2 - Some coatings are extremely thinsome as thin as a...Ch. 2 - Select an appropriate hardness test for each of...Ch. 2 - A paper clip is made of wire 0.5 mm in diameter....Ch. 2 - A 250-mm-long strip of metal is stretched in two...Ch. 2 - Identify the two materials in Fig. 2.5 that have...Ch. 2 - Plot the ultimate strength vs. stiffness for the...Ch. 2 - If you remove the layer of material ad from the...Ch. 2 - Prove that the true strain at necking equals the...Ch. 2 - Percent elongation is always defined in terms of...Ch. 2 - You are given the K and n values of two different...Ch. 2 - A cable is made of two strands of different...Ch. 2 - On the basis of the information given in Fig. 2.5,...Ch. 2 - In a disk test performed on a specimen 1.00 in. in...Ch. 2 - A piece of steel has a hardness of 300 HB....Ch. 2 - A metal has the following properties: UTS = 70,000...Ch. 2 - Using only Fig. 2.5, calculate the maximum load in...Ch. 2 - Estimate the modulus of resilience for a highly...Ch. 2 - A metal has a strength coefficient K = 100,000 psi...Ch. 2 - Plot the true stresstrue strain curves for the...Ch. 2 - The design specification for a metal requires a...Ch. 2 - Calculate the major and minor pyramid angles for a...Ch. 2 - If a material has a target hardness of 300 HB,...Ch. 2 - A Rockwell A test was conducted on a material and...Ch. 2 - For a cold-drawn 0.5% carbon steel, will a...Ch. 2 - A material is tested in tension. Over a 1-in. gage...Ch. 2 - A horizontal rigid bar cc is subjecting specimen a...Ch. 2 - List and explain the desirable mechanical...Ch. 2 - When making a hamburger, you may have observed the...Ch. 2 - An inexpensive claylike material called Silly...Ch. 2 - In tension testing of specimens, mechanical and...Ch. 2 - Demonstrate the impact toughness of a piece of...Ch. 2 - Using a large rubber band and a set of weights,...Ch. 2 - Find or prepare some solid circular pieces of...Ch. 2 - Take several rubber bands and pull them at...Ch. 2 - Devise a simple fixture for conducting the bend...Ch. 2 - By pressing a small ball bearing against the top...Ch. 2 - Describe your observations regarding Fig. 2.14c.Ch. 2 - Embed a small steel ball in a soft block of...Ch. 2 - Devise a simple experiment, and perform tests on...Ch. 2 - Obtain some solid and some tubular metal pieces,...Ch. 2 - Explain how you would obtain an estimate of the...Ch. 2 - Without using the words stress or strain, define...Ch. 2 - We know that it is relatively easy to subject a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Qustions 1,2,3arrow_forwardA 0.013 m diameter, 0.5 m long cylindrical metal bar is subjected to a compressive force of 8,500 N. This load does not exceed the yield strength of the material. Determine its diameter under this load. You will need some of the following properties of the metal to solve the problem: modulus of elasticity = 207 GPa, Poisson’s ratio = 0.30, yield strength = 180 MPa, tensile strength = 380 MPa, ductility = 23% elongation.arrow_forwardA tensile force of 200 KN is applied on a 0.02-m diameter and.2-m long rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. Assuming no permanent deformation occurs in that material, the modulus of elasticity (GPa) is?arrow_forward
- A titanium tube with an outside diameter of 25 mm and inside diameter of 20 mm and a length of 200 mm. When an elastic uniaxial tensile force of 30 kN is applied to this tube along its length, what is the final length of that tube? (Modulus of elasticity of Titanium is 105 GPa)arrow_forwardChoose correct answer: Rigid material Rigid plastic material Elastic plastic material Elastic perfectly plastic materialarrow_forwardshort Answer with Explaining all parts of the Question pleasearrow_forward
- Note: for tackling parts of this question, you will need to use the K-calculator; i have provided a screenshot of the K calculator and i am inly looking for input vales for this. A new grade of steel with enhanced corrosion resistance is proposed for use in the nuclear industry; however, little is known about the fracture toughness and an engineer is asked to investigate. Bend samples are fatigue cracked and then loaded to failure. The engineer tested three samples and the results are summarised below. Test results Sample W (mm) B (mm) a (mm) Load at failure (kN) 1 20 5 9.8 2.3 2 20 10 9.4 4.4 3 20 20 10.1 8.6 For the geometry used, the stress at failure is calculated from the equation added below. where P is in newtons and B is in metres. (Note that this is an empirical formula so the units do not balance.) i.Use the ‘Beam in pure bending - through-thickness edge crack’ geometry in the K-calculator to calculate the value of K at failure for the three…arrow_forwardWhich material/metal is the stiffest based on the following data provided and why?arrow_forwardA tensile force of 120 kN is applied on a 0.02-m diameter and 2-m long rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. The engineering stress on that rod is?arrow_forward
- A cylindrical rod 500 mm long, having a diameter of 12.7 mm, is to be subjected to a tensile load. If the rod is to experience neither plastic deformation nor an elongation of more than 1.3 mm when the applied load is 29,000 N, which of the four metals or alloys listed below are possible candidates? Justify your choice(s).Material Modulus of Elasticity (GPa ) Yield Strength (MPa) Tensile Strength (MPa)Aluminum alloy 70 225 420Brass alloy 100 325 420Copper 110 210 275Steel alloy 207 450 550arrow_forwardYou have been given the following test sample data following mechanical testing of 15 test pieces of a transformation toughened zirconia. What is the Weibull modulus of this material? Would you advise the use of this material over one with a Weibull Modulus of 25.4 and a mean failure stress of 235 MPa, if you anticipate that the peak stress on the material could be 220 MPa? (Since this question has two parts, you must select the two correct options from the list below) Test Sample Failure Stress (MPa) 1 255 2 271 3 260 4 223 5 257 6. 267 7 242 8 230 9. 245 10 225 11 254 12 236 13 238 14 251 15 264 O a. 27.3 O b. 4.5 O c. 6.9 O d. Yes е. 15.2 O f. 18.3 O g. No O O O O O O Oarrow_forwardA cylindrical specimen of a brass alloy having a length of 104 mm (4.094 in.) must elongate only 5.20 mm (0.2047 in.) when a tensile load of 95000 N (21360 lbf) is applied. Under these circumstances what must be the radius of the specimen? Consider this brass alloy to have the stress-strain behavior shown in the Animated Figure 7.12.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY