Textbook Question
Chapter 3, Problem 2P
Brass is an alloy of copper with a certain amount of zinc dissolved and dispersed throughout the structure. Based on the material presented in this chapter:
- Would you expect brass to be stronger or weaker than pure copper? Why?
- Low brass (Copper alloy 240) contains 20% zinc. Cartridge brass (Copper alloy 260) contains 30% dissolved zinc. Which would you expect to be stronger? Why?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
I need the solution of this question please please please quickly
Thanks
Show complete work step by step.
You are an engineer for a steel plant. You are presented with a piece of steel from your rival plant. You
investigate the microstructure and find it to contain 60 % ferrite and 40% martensite, and the
martensite contains 0.5% carbon.
Based on this information, reverse engineer the nominal composition and starting temperature used by
your rival.
You may assume the composition of ferrite to be 0.022 %.
(Round the composition to 2 decimal places, and the temperature to the nearest 25 degrees Celsius)
O 0.31wt% C at 725 Celsius
O 0.21wt% C at 725 Celsius
0.26wt% C at 775 Celsius
O 0.26wt% Cat 725 Celsius
O 0.21wt% C at 775 Celsius
0.31wt% Cat 775 Celsius
Chapter 3 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 3 - What enables us to control the properties and...Ch. 3 - Â What are the next levels of structure that are...Ch. 3 - Prob. 3RQCh. 3 - Prob. 4RQCh. 3 - Prob. 5RQCh. 3 - Prob. 6RQCh. 3 - What are the three types of primary bonds, and...Ch. 3 - What are some general characteristics of...Ch. 3 - Prob. 9RQCh. 3 - Prob. 10RQ
Ch. 3 - Prob. 11RQCh. 3 - Prob. 12RQCh. 3 - Prob. 13RQCh. 3 - What are some unique property features of...Ch. 3 - Prob. 15RQCh. 3 - Prob. 16RQCh. 3 - Prob. 17RQCh. 3 - What are some of the general characteristics of...Ch. 3 - Prob. 19RQCh. 3 - Prob. 20RQCh. 3 - Prob. 21RQCh. 3 - Prob. 22RQCh. 3 - Prob. 23RQCh. 3 - Prob. 24RQCh. 3 - What is a grain? A grain boundary?Ch. 3 - Prob. 26RQCh. 3 - What is implied by a low ASTM grain�size number?...Ch. 3 - Prob. 28RQCh. 3 - What is Poissons ratio, and under what conditions...Ch. 3 - What is plastic deformation?Ch. 3 - Why do metals retain their strength during plastic...Ch. 3 - Prob. 32RQCh. 3 - Prob. 33RQCh. 3 - What is a dislocation? Using the carpet analogy,...Ch. 3 - What is the difference between an edge dislocation...Ch. 3 - What are some of the common barriers to...Ch. 3 - Prob. 37RQCh. 3 - What is the mechanism (or mechanisms) responsible...Ch. 3 - Why is a fine grain size often desired in an...Ch. 3 - What is an anisotropic property? Why might...Ch. 3 - What is the difference between brittle fracture...Ch. 3 - How does a metal increase its internal energy...Ch. 3 - What is required in order to drive the...Ch. 3 - How might the lowest recrystallization temperature...Ch. 3 - In what ways can recrystallization be used to...Ch. 3 - What is the major distinguishing feature between...Ch. 3 - What is warm working?Ch. 3 - How can deformation and recrystallization improve...Ch. 3 - Why is grain growth usually undesirable?Ch. 3 - Prob. 50RQCh. 3 - As a result of their ionic or covalent bonding,...Ch. 3 - Prob. 52RQCh. 3 - Prob. 53RQCh. 3 - What is the difference between an intrinsic...Ch. 3 - What is required for electrical conductivity in...Ch. 3 - What is required for electrical conductivity in...Ch. 3 - Brass is an alloy of copper with a certain amount...Ch. 3 - It is not uncommon for processing operations to...Ch. 3 - Polyethylene consists of fibrous molecules of...Ch. 3 - Prob. 5P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- 1. Calculate the density of a high-leaded brass with a composition of 64.5 wt% Cu, 33.5 wt% Zn, and 2 wt% Pb. Cu, Zn, and Pb have densities of 8.96 m, 7.133 g cm-3, and 11.29 g cm-3, respectively, at ambient temperature.arrow_forwardPlease don't provide handwritten solution .....arrow_forwardHelp with thisarrow_forward
- As a material scientist, you have been requested by an engineer to list down a possiblecylindrical rod alloy to be used in your next project. Each cylindrical rod having adimension of 100 mm long and a diameter of 10.0 mm is to be deformed using a tensileload of 27,500 N. It must not experience either plastic deformation or a diameterreduction of more than 7.5 × 10−3 mm. Based on materials listed in Table 2, which arepossible candidates? Justify your choice(s).arrow_forwardWe wish to produce an 0.3 inch plate of oxygen-free, high-conductivity (OFHC) copper that has a yield strength of at least 45 ksi and elongation of at least 10%. The original thickness of the plate is 3 inches. The width of the plate remains the same during processing. Which of the following procedures would give the correct final properties. More than one answer is possible. Group of answer choices Hot work from 3 to 0.5 inches; cold work from 0.5 to 0.3 inches Cold work from 3 to 1 inch; cold work from 1 to 0.5 inches; hot work from 0.5 to 0.3 inches Cold work from 3 to 1 inch; cold work from 1 to 0.4 inches; cold work from 0.4 to 0.3 inches Cold work from 3 to 1 inch; do full anneal; cold work from 1 to 0.5 inches; do full anneal; cold work from 0.5 to 0.3 inches Hot work from 3 to 0.4 inches; cold work from 0.4 to 0.3 inches None of the above will work Cold work from 3 to 0.3 inches Cold work from 3 to 1 inch; hot work from 1 to 0.4 inches; cold work from 0.4…arrow_forwardThe density of pure aluminum calculatedfrom crystallographic data is expected tobe 2.69955 g cm3.(a) Design an aluminum alloy that has adensity of 2.6450 g cm3(b) Design an aluminum alloy that has adensity of 2.7450 g cm3. The density of pure aluminum calculatedfrom crystallographic data is expected tobe 2.69955 g cm3.(a) Design an aluminum alloy that has adensity of 2.6450 g cm3.(b) Design an aluminum alloy that has adensity of 2.7450 g cm3.arrow_forward
- 1 Al-Li Aerospace Alloys When a small amount of Li is added into Al to create an Al-Li alloy, the two elements typically do not mix homogeneously. Instead, most of the material is nearly-pure Al, while some small regions are Li-rich.¹ (These small regions are called precipitates and they are responsible for giving Al-Li alloys much better properties for aerospace applications relative to pure Al. We'll learn more about the alloying process and about precipitates later in the course.) The Li-rich regions have the chemical formula Al3Li and belong to the cubic crystal system.² In the unit cell, the Li atoms are located at 000, while the Al atoms are located at 110, 101, and 01121. (a) Draw the unit cell of Al3Li. (b) Which of the crystal structures from Callister Chapter 3 does this resemble? Why do we not call it that structure? (c) Given that the lattice parameter is 0.401 nm, what is the density of Al3Li?arrow_forwardIn the Ni-base superalloys used to make turbine blades, which of the following statements are true? Select one or more: U a. There is an atom at each corner of each cube face and one in the centre of each cube face U b. There are two types of phases, with essentially identical crystalline arrangement and different strength O c. The underlying atomic structure is a cubic crystalline type Od. There are two types of phases, with very different crystalline arrangement and different strength There are two types of phases, with essentially identical crystalline arrangement and same strength An atom is present only at each corner of each cube face e. O f.arrow_forwardPlease answer all questionsarrow_forward
- You are given three metal test samples, with the same chemical composition and differing grain sizes: A: 5.0, B: 10.0 and C: 20.0 microns. Samples A and B have been tested and have yield stresses of 142.4 MPa and 135.8 MPa (all numbers are rounded off to the 1st decimal point). Based on this information, which of the following values do you think will be the closest to the yield stress of Sample C? In calculating the answer, use the Hall-Petch relation between yield stress of a metal o vield and the grain size of the metal d, which is Oyield = 00 + kd¬1/2 where k and og are constants. (This question has only one correct answer) а. 100.6 MPa b. 131.1 MPa С. 152.4 MPa O d. 115.8 MPa е. 128.1 MPaarrow_forwardYou are given three metal test samples, with the same chemical composition and differing grain sizes: A: 5.0, B: 10.0 and C: 20.0 microns. Samples A and B have been tested and have yield stresses of 142.4 MPa and 135.8 MPa (all numbers are rounded off to the 1st decimal point). Based on this information, which of the following values do you think will be the closest to the yield stress of Sample C? In calculating the answer, use the Hall-Petch relation between yield stress of a metal ovield and the grain size of the metal d, which is Oyield = 00 + kd¯1/2 where k and og are constants. (This question has only one correct answer) a. 128.1 MPa O b. 115.8 MPa О с. 100.6 MPa O d. 131.1 MPa Ое. 152.4 MPaarrow_forwardThis is the microstructure of astm a 128 a high magnesease steel. This microstructure was taken after etching the samples. After etching why did it turn the microstructure colors. What can be determined when looking at the microstructure of this samplearrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Intro to Ceramics and Glasses — Lesson 2, Part 1; Author: Ansys Learning;https://www.youtube.com/watch?v=ArDFnBWH-8w;License: Standard Youtube License