Degarmo's Materials And Processes In Manufacturing
13th Edition
ISBN: 9781119492825
Author: Black, J. Temple, Kohser, Ronald A., Author.
Publisher: Wiley,
expand_more
expand_more
format_list_bulleted
Concept explainers
Textbook Question
Chapter 17, Problem 44RQ
If the deformed grains recrystallize during hot working, how can hot deformation impart an oriented or flow structure (and directionally dependent properties)?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
I need the answer as soon as possible
3) Which advantages, disadvantages and characteristic properties does hot working
Lelative to cold working have?(
Explain basic operations in bulk deformation.
shortly (with using figures)(
A cylindrical brass rod with a minimum tensile strength of 450 MPa, a ductility of at least 13% EL (elongation), and a final diameter of 12.7mm is required. You have in your inventory some 19.0mm diameter brass stock that has been cold worked to 35%. Assuming that the cross section of the rod is still circular after being cold worked, and that brass experiences cracking at 65% CW, describe the necessary working steps in order to achieve the final product. Take the expression for % cold work to be = (Ao - Af)/ Ao x 100%, where Ao and Af are the original and final circular cross-sectional areas of the rod.
Chapter 17 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 17 - What is plasticity?Ch. 17 - What are some of the general assets of the...Ch. 17 - Why might large production quantities be necessary...Ch. 17 - What types of deformation may occur in forming...Ch. 17 - What is an independent variable in a...Ch. 17 - What are some considerations regarding selection...Ch. 17 - What is the significance of tool and die geometry...Ch. 17 - Why is lubrication often a major concern in metal...Ch. 17 - What are some of the secondary effects that may...Ch. 17 - Prob. 10RQ
Ch. 17 - Why is it important to be able to predict the...Ch. 17 - Prob. 12RQCh. 17 - Prob. 13RQCh. 17 - Prob. 14RQCh. 17 - Prob. 15RQCh. 17 - Prob. 16RQCh. 17 - Prob. 17RQCh. 17 - What are some of the features that may be...Ch. 17 - What features have contributed to the expanded use...Ch. 17 - What are some of the uses or applications of...Ch. 17 - Prob. 21RQCh. 17 - Prob. 22RQCh. 17 - Prob. 23RQCh. 17 - What type of information about the material being...Ch. 17 - Prob. 25RQCh. 17 - Why is friction such an important parameter in...Ch. 17 - Why are friction effects in metalworking difficult...Ch. 17 - Prob. 28RQCh. 17 - Prob. 29RQCh. 17 - Prob. 30RQCh. 17 - Prob. 31RQCh. 17 - Discuss the significance of wear in metal forming:...Ch. 17 - Lubricants are often selected for properties in...Ch. 17 - What is tribology?Ch. 17 - What are some of the common types of metal forming...Ch. 17 - What is hydrodynamic lubrication? What are some of...Ch. 17 - If the temperature of a material is increased,...Ch. 17 - Define the various regimes of cold working, warm...Ch. 17 - What is an acceptable definition of hot working?...Ch. 17 - What are some of the attractive manufacturing and...Ch. 17 - What are some of the negative aspects of hot...Ch. 17 - Prob. 42RQCh. 17 - Prob. 43RQCh. 17 - If the deformed grains recrystallize during hot...Ch. 17 - Why might a rolled thread offer improved strength...Ch. 17 - How might the temperature of a deforming workpiece...Ch. 17 - Why are heated dies or tools often employed in...Ch. 17 - What generally restricts the upper temperature to...Ch. 17 - What is the primary cause of residual stresses in...Ch. 17 - What is cold working?Ch. 17 - Compared to hot working, what are some of the...Ch. 17 - What are some of the disadvantages of...Ch. 17 - How could cold working be used to reduce the cost...Ch. 17 - Why are cold�forming processes best suited for...Ch. 17 - How can the tensile test properties of a metal be...Ch. 17 - Why is elastic springback an important...Ch. 17 - What is pickling, and how does it remove surface...Ch. 17 - Prob. 58RQCh. 17 - What engineering properties are likely to decline...Ch. 17 - Prob. 60RQCh. 17 - Prob. 61RQCh. 17 - Prob. 62RQCh. 17 - What are some of the advantages of warm forming...Ch. 17 - Prob. 64RQCh. 17 - What material feature is considered to be the...Ch. 17 - Why is isothermal forming considerably more...Ch. 17 - Prob. 67RQCh. 17 - Prob. 1PCh. 17 - Prob. 2PCh. 17 - List and discuss the various economic factors that...Ch. 17 - Prob. 4PCh. 17 - Prob. 5PCh. 17 - Prob. 6PCh. 17 - Prob. 1.1CSCh. 17 - Prob. 1.2CSCh. 17 - Which stainless steel would you recommend? Begin...Ch. 17 - Prob. 1.4CSCh. 17 - Prob. 1.5CSCh. 17 - After drawing and perforating, the residual...Ch. 17 - One of the blades has struck a rock and is badly...Ch. 17 - A second propeller, identical to the one above,...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Why is heat treatment typically an integral part of the process flow for bulk deformation of metal?.arrow_forwardThis is a True or false question that has been bothersome please helparrow_forward1) Chapter 2: How do grain boundaries contribute to strain hardening in metals? 2) Chapter 3: Review question 3.6: What is work hardening? 3) Chapter 3: Review question 3.10: Under what circumstances does the strength coefficient have the same value as the yield strength? 4) Chapter 3: Review question 3.11: What is the complicating factor that occurs in a compression test that might be considered analogous to necking in a tensile test?arrow_forward
- What is a consequence of strain hardening?arrow_forwardQuestion-2 If it takes 12.0 min to 50% recrystallize a piece of high-purity copper sheet at 140°C and 200 min at 88°C, how many minutes are required to recrystallize the sheet 50% percent at 100°C? Assume an Arrhenius-type rate behavior.arrow_forwardBriefly cite the differences between the recovery and recrystallization processes.arrow_forward
- MENG364 MANUFACTURING TECHNOLOGY please solve the question very quicklyarrow_forwardRegarding annealing, choose the right answer (One or more): The actual annealing time must be long enough to allow for any necessary transformation reactions that may occur Annealing can be performed to release internal stresses of the material The main purpose of annealing is to decrease or restore material's ductility Time isn't a significant parameter in annealing process If the rate of temperature change is too great, temperature gradients and internal stresses may be induced that may lead to warping or even crackingarrow_forwardThe same alloy is used to fabricate two different components, both of which result in identical mechanical properties. Cold working yields a microstructure with a much higher incidence of symmetrical grain boundaries for Component 1 as compared with that of Component 2. Which item will most likely have a higher resistance to dynamic embrittlement?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Types of Manufacturing Process | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=koULXptaBTs;License: Standard Youtube License