Textbook Question
Chapter 19, Problem 29QLP
An injection-molded nylon gear is found to contain small pores. It is recommended that the material be dried before molding it. Explain why drying will solve this problem.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Regarding amorphous plastics, explain why they tend to have higher tensile strength when deformed compared to when not. please include an illustration
Identify which is typically tougher: a semicrystalline or an amorphous polymer.
May I have help with this please?
Chapter 19 Solutions
Manufacturing Engineering & Technology
Ch. 19 - What are the forms of raw materials for processing...Ch. 19 - What is extrusion? What products are produced by...Ch. 19 - Describe the features of an extruder screw and...Ch. 19 - How are injection-molding machines rated?Ch. 19 - What is (a) a parison, (b) a plastisol, and (c) a...Ch. 19 - How is thin plastic film produced?Ch. 19 - List several common products that can be made by...Ch. 19 - What similarities and differences are there...Ch. 19 - Explain the difference between potting and...Ch. 19 - What is thermoforming?
Ch. 19 - Describe runner, gate, sprue, and well.Ch. 19 - Describe the advantages of cold-forming plastics...Ch. 19 - What are the characteristics of filament-wound...Ch. 19 - Describe the methods that can be used to make...Ch. 19 - What is pultrusion? Pulforming?Ch. 19 - How are very thin plastic film produced?Ch. 19 - What process is used to make foam drinking cups?Ch. 19 - If a polymer is in the form of a thin sheet, is it...Ch. 19 - How are polymer fibers made? Why are they much...Ch. 19 - What are the advantages of coextrusion?Ch. 19 - Explain how latex rubber gloves are made.Ch. 19 - Describe the features of a screw extruder...Ch. 19 - Explain why injection molding is capable of...Ch. 19 - Prob. 24QLPCh. 19 - Explain the reasons that some plastic-forming...Ch. 19 - Describe the problems involved in recycling...Ch. 19 - Can thermosetting plastics be used in injection...Ch. 19 - Inspect some plastic containers, such as those...Ch. 19 - An injection-molded nylon gear is found to contain...Ch. 19 - Explain why operations such as blow molding and...Ch. 19 - Prob. 31QLPCh. 19 - Typical production rates are given in Table 19.2....Ch. 19 - What determines the cycle time for (a) injection...Ch. 19 - Does the pull-in defect (sink marks) shown in Fig....Ch. 19 - What determines the intervals at which the...Ch. 19 - Identify processes that would be suitable for...Ch. 19 - Identify processes that are capable of producing...Ch. 19 - Inspect several electrical components, such as...Ch. 19 - Inspect several similar products that are made of...Ch. 19 - What are the advantages of using whiskers a...Ch. 19 - Construct a table that lists the main...Ch. 19 - Estimate the die-clamping force required for...Ch. 19 - A 2-Iitcr plastic beverage bottle is made by blow...Ch. 19 - Consider a Styrofoam drinking cup. Measure the...Ch. 19 - In Fig. 19.2, what flight angle, , should be used...Ch. 19 - Make a survey of a variety of sports equipment,...Ch. 19 - Explain the design considerations involved in...Ch. 19 - Give examples of several parts suitable for insert...Ch. 19 - Give other examples of design modifications in...Ch. 19 - With specific examples, discuss the design issues...Ch. 19 - Die swell in extrusion is radially uniform for...Ch. 19 - Inspect various plastic components in a typical...Ch. 19 - It is well known that plastic forks, spoons, and...Ch. 19 - Prob. 55SDPCh. 19 - Make a survey of the technical literature, and...Ch. 19 - Prob. 57SDPCh. 19 - Prob. 58SDPCh. 19 - Prob. 59SDPCh. 19 - Examine some common and colorful plastic poker...Ch. 19 - Obtain different styles of toothpaste tubes,...Ch. 19 - By incorporating small amounts of blowing agent,...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Which of the following are reasons why injection molding of thermosets is more difficult than injection molding of thermoplastics (two best answers): O allowances must be made for cross-linking of thermosets O barrel temperatures must be hotter for thermosets O cycle times are longer because of curing thermosets are denser O two injection units are requiredarrow_forward3. A dimension of 225.00 mm is specified for a particular injection moulded component manufactured in ABS. Calculate the corresponding dimension to which the mould cavity should be machined, using the value of shrinkage given in the table below. Typical values of shrinkage for moldings of selected thermoplastics. Shrinkage, mm/mm (in/in) Shrinkage, Plastic Plastic mm/mm (in/in) ABS Polyethylene Polystyrene 0.006 0.025 Nylon-6,6 Polycarbonate 0.020 0.004 0.007 PVC 0.005arrow_forwardIs compression molding a reversible process or irreversible process? Explain.arrow_forward
- How do i solve this question?arrow_forwardAn injection molded polyethylene part has a dimension of 6.25 cm. A new material, polycarbonate, is used in the same mold. What is the expected corresponding dimension of the polycarbonate molding?arrow_forwardReview Problems The extrusion die for a polyethylene parison used in blow molding has a mean diameter of 18.0 mm. The size of the ring opening in the die is 2.0 mm. The mean diameter of the parison is observed to swell to a size of 21.5 mm after exiting the die orifice. If the diameter of the blow molded container is to be 150 mm, determine (a) the corresponding wall thickness of the container and (b) the wall thickness of the parison.arrow_forward
- (b) Which of the following plastic and composite materials processing is most suitable for the application of polymer automotive body panel? Explain how the selected manufacturing process selected can be used to produce the product shown in Figure 1.2 below • Injection Moulding • Reaction injection Moulding (RIM) • Blow Moulding • Rotational Moulding • Thermoforming • Compression Moulding (CM) • Transfer Moulding (TM) • Casting • Foam Moulding SULIT SULIT (BMCG 2323) Figure 1.2 Example of polymer automotive body panelarrow_forwardA steel plate used for polymer forming is to be bent into a circular shape having an inside radius of 10 m. What maximum thickness can be used for the plate if the normal stress is not to exceed 267 MPa? Assume that the modulus of elasticity for the steel is 201 GPa.arrow_forwardExplain how macroscopic hardening occurs in semicrystalline polymers from the point of view of microscopic mechanisms (covered in the chapters indicated in the Callister's book). (maximum of 3 lines, not counting the space for possible schematic figures).arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY