Textbook Question
Chapter 13, Problem 39QTP
A rolling operation takes place under the conditions shown in Fig. P13.39. What is the position, xn, of the neutral point? Note that there are front and back tensions that have not been specified. Additional data are as follows: Material is 5052-O aluminum; hardened steel rolls; surface roughness of the rolls = 0.02 μm; rolling temperature = 210°C.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a rolling operation. As the thickness is reduced, the plate widens by 3%. The entrance speed of the plate is 13 m/min and the roll radius is 310 mm with a rotational speed of 30 rpm.
5.1 Calculate the minimum coefficient of friction required, that will make the rolling operation possible.
5.2 Calculate the exit velocity of the plate.
5.3 Calculate the forward slip.
5.4 If the final width of the sheet is 200 mm, calculate the required roll force.
5.5 Explain what is roll flattening, its effects and how it can be reduced.
Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a thickness of 6 mm. The roll radius is 200 mm, and the roll rotates at 200 rev/min; use coefficient of friction at the die-work interface (p)=0.1. A low carbon steel such as AISI 1020 has K (strength coefficient) = 530 MPa and n ( strain hardening exponent) =0.26a)1059 kWb)950 kWc)1183 kWd)875 kW
(c) A flat rolling operation is being carried out where the roll radius is 200 mm and the roll
rotates at 100 rpm. The workpiece material is annealed low carbon steel with 200 mm wide
and 10 mm thickness. The strength coefficient and the strain hardening of the carbon steel
are 530 MPa and 0.26, respectively. The coefficient of friction is 0.2.
(i)
Caicurae tne roll force and torque if the workpiece is rolled to a thickness of 4 mm.
(ii)
Calculate the maximum possible draft and evaluate how friction effect the thickness
of the rolled workpiece.
Chapter 13 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 13 - What is the difference between a plate and a...Ch. 13 - Define roll gap, neutral point, and draft.Ch. 13 - What factors contribute to spreading in flat...Ch. 13 - What is forward slip? Why is it important?Ch. 13 - Describe the types of deflections that rolls...Ch. 13 - Describe the difference between a bloom, a slab,...Ch. 13 - Why may roller leveling be a necessary operation?Ch. 13 - List the defects commonly observed in flat...Ch. 13 - What are the advantages of tandem rolling? Pack...Ch. 13 - How are seamless tubes produced?
Ch. 13 - Why is the surface finish of a rolled product...Ch. 13 - What is a Sendzimir mill? What are its important...Ch. 13 - What is the Mannesmann process? How is it...Ch. 13 - Describe ring rolling. Is there a neutral plane in...Ch. 13 - How is back tension generated?Ch. 13 - Explain why the rolling process was invented and...Ch. 13 - Flat rolling reduces the thickness of plates and...Ch. 13 - Explain how the residual stress patterns shown in...Ch. 13 - Explain whether it would be practical to apply the...Ch. 13 - Describe the factors that influence the magnitude...Ch. 13 - Explain how you would go about applying front and...Ch. 13 - What typically is done to make sure that the...Ch. 13 - Make a list of parts that can be made by (a) shape...Ch. 13 - Describe the methods by which roll flattening can...Ch. 13 - It was stated that spreading in flat rolling...Ch. 13 - Flat rolling can be carried out by front tension...Ch. 13 - Explain the consequence of applying too high a...Ch. 13 - Note in Fig. 13.3f that the driven rolls (powered...Ch. 13 - Describe the importance of controlling roll...Ch. 13 - In Fig. 13.9a, if you remove the top compressive...Ch. 13 - Name several products that can be made by each of...Ch. 13 - List the possible consequences of rolling at (a)...Ch. 13 - It is known that in thread rolling, as illustrated...Ch. 13 - If a rolling mill encounters chatter, what process...Ch. 13 - Can the forward slip ever become negative? Why or...Ch. 13 - In Example 13.1, calculate the roll force and the...Ch. 13 - Calculate the individual drafts in each of the...Ch. 13 - Estimate the roll force, F, and the torque for an...Ch. 13 - A rolling operation takes place under the...Ch. 13 - Estimate the roll force and power for annealed...Ch. 13 - A flat-rolling operation is being carried out...Ch. 13 - A simple sketch of a four-high mill stand is shown...Ch. 13 - Obtain a piece of soft, round rubber eraser, such...Ch. 13 - If you repeat the experiment in Problem 13.45 with...Ch. 13 - Design a set of rolls to produce cross-sections...Ch. 13 - Design an experimental procedure for determining...Ch. 13 - Derive an expression for the thickest workpiece...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Low carbon steel plate that is 1.65 inches thick is to be rolled down to 1.3 inches in a single pass. The plate gets 4% wider as the thickness gets smaller. The steel plate has a 174 MPa yield strength and a 290 MPa tensile strength. The plate enters at a pace of 0.6 inches per minute. The rotating speed is 49.0 rev/min, and the roll radius is 12.8 inches. Calculate: a) Determine the minimum required coefficient of friction that would make this rolling operation possible b) exit velocity of the plate (m/min) c) forward slip (m/min) Please submit the final answers in 2 decimal placesarrow_forwardQ/ A plate of 270 mm wide and 25 mm thick from carbon steel. A two-high rolling mill is used to reduce the thickness to 20 mm. Roll radius = 600 mm, and roll speed = 8 rpm. Strength coefficient = 500 MPa, and strain hardening exponent = 0.25. Determine (a) roll force, (b) roll torque, and (c) power required to perform the operation.arrow_forwardNeed neat and clean handwritten solution explaining every steps. Do not give copied solution from chegg else you will get downvotearrow_forward
- A 200 mm wide and 42.0 mm thick plate made of low carbon steel is to be reduced in one pass in a rolling operation. As the thickness is reduced, the plate widens by 4%. The entrance speed of the plate is 15.0 m/min. The roll radius is 325 mm and the rotational speed is 49.0 rev/min. i. If the current horsepower of the available rolling machine is 950 HP, how much thickness could the machine reduce the plate thickness to? ii. If the required thickness needs to be 34.0mm, how could the original width of the plate be changed in order to use the same machine?arrow_forwardA hot/cold rolling setup is shown right. The operation first hot rolls a 3/8” thick plate, 12” wide (w), of6061 Aluminum, to an intermediate thickness, then finally through cold rolling, down to 1/4” thick plate.The friction factor μ is assumed to be constant at 0.15 for the hot roll, 0.12 for the cold rolling stage. Thefirst set of rolls operate at 50 RPM. Also ignore any width increase during rolling. CW=13% or .13 What is the plate thickness (mm) prior to the last rolls, t1, if the last set of rollers perform cold work reduction listed below at .13 or 13% Note that 9.52 mm is equal to 3/8 of an inch.arrow_forward2. A 300 mm wide, 40 mm thick plate is reduced to 30 mm thickness in one pass by hot rolling. Roll diameter is 200 mm and entrance speed is 16 m/min. Material constants C and m at the process temperature are given as 50 MPa and 0.05 respectively. Determine: a. The minimum friction coefficient required to make this operation possible, b. Assuming that the minimum level of friction is maintained, calculate the exit velocity of the plate by considering there is no widening, c. Calculate the force and power requirement to apply the pass.arrow_forward
- Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thlck, rolled to a thickness of 6 mm The roll radius is 200 mm), and the roll rotates at 200 rev/min; use coefficient 0f friction at the die-work interface (p)= 0.1, Alow carbon steel such as AlSI 1020 has K (strength coefficient) = 530 MPaand n (stram hardening exponent) = 0.26arrow_forwardManufacturing processesarrow_forwardQuestion 3 A rolling operation on a 250 mm wide, 8 mm thick, 1112 cold rolled steel takes place using hardened steel rolls with a surface finish of 0.03 um. The rolls have a diameter of 350 mm and rotates at 115 rpm. The final thickness of the plate is 6 mm and the entry speed of the plate is 1.8 m/s. Calculate: 3.1 The minimum coefficient of friction required, that will make the rolling operation possible. 3.2 The required roll force. 3.3 The position of the neutral point, xn 3.4 Indicate, using a sketch, the neutral point showing all relevant notation and dimensions.arrow_forward
- Don't try if you don't know and don't provide handwritten solutionarrow_forwardA 10 mm thick plate is rolled to 7 mm thick in a rolling mill using 1000 mm diameter rigid rolls. The neutral point is located at an angle of 0.3 times the bite angle from the exit. What will be the thickness of the plate at the neutral point.arrow_forwardEstimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a thickness of 6 mm The roll radius is 200 mm, and the roll rotates at 200 rev/min; use coefficient of friction at the die-work interface (u)= 0.1. A low carbon steel such as AISI 1020 has K (strength coefficient) = 530 MPa and n ( strain hardening exponent) = 0.26 a) 1059 kW b) 950 kW C) 1183 kW d) 875 kWarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Types of Manufacturing Process | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=koULXptaBTs;License: Standard Youtube License