Question: A contractor want to select a steel bars (diameter 16 mm) produced from two factories (A and B). The data below shows the results of tensile test; determine: 1. The mean and median. 2. Standard deviation and variance. 3. Find the percent of steel (325.5

Question: A contractor want to select a steel bars (diameter 16 mm) produced from two factories (A and B). The data below shows the results of tensile test; determine: 1. The mean and median. 2. Standard deviation and variance. 3. Find the percent of steel (325.5

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: A beam subjected to a bending moment of 37.7 Nm and having the following sectional properties:…

Q: snip

Q: 650 600 550 500 450 400 350 300 250 200 150 100 50 0.002 0.004 0.006 0.008 0.01 0.012 0.014 0.016…

A: Stress loading and stress and strain relationship is given in the question and it has been asked to…

Q: Q5: A/A tensile test was conducted for a sample and the relationship between stress and strain was…

A: As per the guidelines of Bartleby we are supposed to answer only first three sub-parts of a…

Q: 2.7 The following readings were recorded during a tensile test of a mild steel specimen 24 mm wide…

A: Given data, Width = 24 mm Depth = 10 mm Area = 240 mm2 Length l = 200 mm Graph for the first…

Q: Test Data and result Sample # Age (days) R (mm) Area (mm^2) Q(N) о (MPa) 1 7 100 400000 7 100 410000…

A: Compressive strength is defined as the ratio of the compressive force applied per unit surface area…

Q: How to make an effective stiffness matrix for this figure? M C L 2L 2L

A: The given diagram is shown below, To make the effective stiffness matrix

Q: A Charpy V Notch (CVN) test was performed on a steel specimen and produced the following readings:…

A: Charpy V-notch Test: The Charpy V-notch test is also known as Charpy impact test. This test is a…

Q: Problem 1.4. A tensile test was conducted on a mild steel bar. The following data was obtained from…

Q: 35) The following idealized data was obtained from tensile testing of steel. Answer the questions…

A: Introduction : Yield strength is a measurement of the greatest stress that a material can withstand…

Q: A certain material was tested for tension using three different specimens. For each trial, the load…

Q: A Charpy V Notch (CVN) test was performed on a steel specimen and produced the readings shown in…

A: We have been given the following values: Sr. No Temperature(C) Toughness, Joule (N.m) 1.…

Q: A wood specimen was prepared with actual dimensions of 25 mm * 25 mm * 150 mm and grain parallel to…

A: Given Data: The size of specimen is 25 mm x 25 mm x 150 mm. Area of the specimen subjected to…

Q: Q1- The following data was obtained tensile test on a specimen of 6 mm diameter and gauge length…

A: Stress: Stress is defined as the deformation offered by internal resistance. it is also defined as…

Q: Given the stress-strain diagram, determine the modulus of resilience of the steel casting.

A: The given stress-strain diagram is shown below:

Q: A results below were recorded during tensile test for a steel specimen to be used to manufacture…

A: Given- Dia of specimen (d) = 0.597 cmLoad at yield point (f) =8.15 kNTo Find-Yield stress (σ)

Q: A bar specimen of 36 mm diameter is subjected to a pull of 90 kN during a tension test. The…

A: Given data- A bar specimen- Diameter d=36 mm, Change in diameter ∆d=0.0046 mm, Gauge length L=200…

Q: Problem 1.4. A tensile test was conducted on a mild steel bar. The following data was tained from…

Q: What are the underlying assumptions when calculating for the upper and lower bounds of the elastic…

A: he lower-bound estimate of elastic modulus is calculated by: Ec = 1 / (ff / Ef + (1 – ff) / Em). On…

Q: Design Average Strength Strength (MPa) Specimen Diameter Batch No. Strength Age (days) (Mpa) Load…

Q: Q2/ A rectangular block of rubber is deformed as shown by the dotted line. Determine the average…

A: Given: b = 300 mm h = 450 mm

Q: a ga in tension with the following results: Applied 1 Strain Force (N) (mm) (%) 0 5.000 Stress (MPa)…

A: We…

Q: A wire of 3 mm diameter is bent into a circle and held with its ends and just in contact. If the…

A: A copper wire with a diameter of 3 mm is bent into a circle and held with its ends just touching.The…

Q: QUESTION 2 Test Engineers found that 22% of steel frames fracture within 15 years. The average…

A: Given: 30 Psi is the average stress Required: What refers 30 Psi Note: No shear and bending…

Q: Problem 1.4. A tensile test was conducted on a mild steel bar. The following data was Stained from…

Q: A bar of diameter 30 mm is subjected to a tensile Load such that the measured extension on a gauge…

Q: 5/ Determine the smallest value of uniform load that will cause a crack for the reinforced concrete…

Q: A tensile test is peformed on a brass specimen 10 mm in diameter using a gage length of 50 mm. When…

Q: A 650mm length of metal wire is being tested under a tensile load. The metal has a Young's modulus…

A: This question is related to the Stress and Strain from Strength of Material. We calculate load P for…

Q: Duestion: A contractor want to select a steel bars (diameter 16 mm) produced from two Eactories (A…

A: lower class upper class mid class no of sample mid class strength * no of sample…

Q: cord the stress and strain data as presented in Table 1. A 50 mm gauge arked on the specimen before…

A: To find:- percentage reduction of area if final diameter us 8mm final length of tested specimen if…

Q: Problem 1.4. A tensile test was conducted on a mild steel bar. The following data was obtained from…

Q: With modulus of elasticity, MoE = 7,920 N/mm² at 12% mc, what would be the expected MoE at 23 % mc?…

Concept explainers

Material Properties

Construction in civil engineering demands high strength, durability, and longevity. These targets can be achieved by better design and analysis, along with the correct choice of materials. Different materials have different properties and hence, they respond and performs differently under the various condition of external loadings. It is therefore a critical task of an engineer to select the right material based on the property that the material is supposed to function in real-time. When speaking about the property, there are different categories of material properties like chemical property, physical property, mechanical property, electrical property, magnetic property, thermal property, etc. These material properties form the basis of material selection in various applications.

Question

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1: Introduction

VIEW

Step 2: Mean, Median, Standard deviation and Variance

VIEW

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

pls box the final answer
Asapp.
7:50 ul LTE O A docs.google.com Choose the correct answer * During the tensile test, experiment on a sample of mild steel, data represented in the figure below was obtained with an initial diameter (do) of 0.505 inch. At failure, the reduced diameter (d) of the sample was 0.305 inch. Gauge Length (Lo) is 2 inches and final Gauge Length (L,) is 2.625 inches. Answer the questions below: Us 70 Tk LyP IR 50- FL PL ptiel linit AL or 6T P EL lastie lii UP per yied paint Lypi Lewer s us t uni mated streagth IR: Indicatul siregh Rupture TR True strugth Ruple fPL (propartimal timt) Direct strain & to to E strmin Cin/in) a b 1. Mild steel is: (a) brittle materials (b) ductile material (c) between the ductile and the brittle 2. Young's Modulus evaluates elasticity within the region from: (а) 0 - Proportional Limit. (b) Proportional Limit - Lower yield Point. (c) Lower
0.9
Find the value of modulus of elasticity if bulk modulus is 62 MPa and poisson ratio is 0.42
8.
C and D please
I need correct answer
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3⁄8 inch and the gage length (the length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress–strain data and draw a best-fit curve. c. Compute the modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress
Procedure: 1. Compression tests on specimens shall be made as soon as practicable after removal from the moist storage. A 28-day test shall be performed within +-20 hours of the 28thday. Test specimens shall be kept moist by any convenient method during the period between removals from moist storage and testing. They shall be tested in moist condition. 2. All test specimens for a given test age shall be broken within the permissible time tolerance prescribed below. TEST AGE PERMISSIBLE TOLERANCE 24 HOURS +-0.5 HOURS OR 2.1% 3 DAYS 2 HOURS OR 2.8% 7 DAYS 6 HOURS OR 3.6% 28 DAYS 20 HOURS OR 3.0% 90 DAYS 2 DAYS OR 2.2 % 3. With a clean rag or rush clean the bearing faces of the bearing blocks, test the specimens and exclusion controller (elastomeric cps). 4. Rest the specimen on the lower extrusion controller, place the top extrusion controller on the specimen, and check the spacing between the sides of the specimen and the extrusion controllers to ensure no contact between the cylinder…
A brass alloy rod having a cross sectional area of 0.24 in.2and a modulus of 16 * 106 psi is subjected to a tensile load. Plastic deformation was observed to begin at a load of 8,944 lb.a. Determine the maximum stress that can be applied without plastic deformation.b. If the maximum length to which a specimen may be stretched without causing plastic deformation is 3.28 in., what is the original specimen length?
Please answer complete question