A brass alloy rod having a cross sectional area of 0.24 in.2and a modulus of 16 * 106 psi is subjected to a tensile load. Plastic deformation was observed to begin at a load of 8,944 lb.a. Determine the maximum stress that can be applied without plastic deformation.b. If the maximum length to which a specimen may be stretched without causing plastic deformation is 3.28 in., what is the original specimen length?

A brass alloy rod having a cross sectional area of 0.24 in.2and a modulus of 16 * 106 psi is subjected to a tensile load. Plastic deformation was observed to begin at a load of 8,944 lb.a. Determine the maximum stress that can be applied without plastic deformation.b. If the maximum length to which a specimen may be stretched without causing plastic deformation is 3.28 in., what is the original specimen length?

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.5P: The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen...

See similar textbooks

Related questions

Q: 5. A tensile test was done on a magnesium sample of original diameter and original length of 12mm…

A: To plot the stress v/s strain curve and to find the required parameters Note: as per the answering…

Q: 400 200 Strain 0.05 0.10 0.15 0.20 From your graph, plotting the yield stress against 1/vd, you…

Q: A specimen is originally 300mm long and has a diemter of 11mm and it subjected to a force of 4kN.…

Q: A strain gauge is attached to the surface of a circular shaft with a radius of 40 mm, as shown in…

A: Given, Radius of circular shaft = 40 mm Strain calculated by strain gauge = -200μ or -200 x 10-6 G…

Q: In a tensile test for an aluminum alloy, the sample used is 2 inches long and 0.5 inches in…

A: A tensile test is performed on an aluminum specimen, whose length is 2 inches and diameter is 0.5…

Q: An aluminum specimen originally 300 mm long is pulled in tension with a stress of 275 MPa. If the…

A: Hooke's law: With in the elastic limit , Stress is always directly proportional to strain. when we…

Q: The stress–strain diagram for a steel alloy having an original diameter of 0.5 in. and a gage length…

Q: Determine the following: a. Young's modulus within the linear portion b. Tangent modulus at a stress…

A: a).Young's Modulus : At the proportional limit, stress is directly proportional to strain stress α…

Q: Problem 4 The test data of the coupon tests of stainless steel alloys are given for three test…

A: Given, Stress strain data for three specimens To find : Elastic modulus, Yield stress and yield…

Q: 2- A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length…

A: Note:- Hi! Thank you for the question, As per the honor code, we are allowed to answer three…

Q: Q.3 The following data were obtained from the tensile test of Aluminum alloy. The initial diameter…

A: Given data; Gauge length = 2 in Initial diameter = 0.505 in

Q: For a bronze alloy, the stress at which plastic deformation begins is 280 MPa, with modulus of…

Q: A tension test performed on a metal specimen to fracture produced the stress– strain relationship…

A: The given figure is shown below:

Q: Consider a square aluminum element of 3in. Dimensions as shown in figure below. If a force is…

A: Poisson's ratio (μ) = 0.33 Deformation along y-axis (δLy) = 0.02 in. Determine the strain in the X…

Q: In a tensile test for an aluminum alloy, the sample used is 2 inches long and 0.5 inches in…

Question

A brass alloy rod having a cross sectional area of 0.24 in.²and a modulus of 16 * 106 psi is subjected to a tensile load. Plastic deformation was observed to begin at a load of 8,944 lb.
a. Determine the maximum stress that can be applied without plastic deformation.
b. If the maximum length to which a specimen may be stretched without causing plastic deformation is 3.28 in., what is the original specimen length?

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Step 5

Step 6

Trending now

This is a popular solution!

Step by step

Solved in 6 steps with 6 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
A brass alloy rod having a cross sectional area of 100 mm2 and a modulus of 110 GPa is subjected to a tensile load. Plastic deformation was observed to begin at a load of 39,872 N.a. Determine the maximum stress that can be applied without plastic deformation.b. If the maximum length to which a specimen may be stretched without causing plastic deformation is 67.21 mm, what is the original specimen length?
A steel alloy specimen having a rectangular cross section of dimensions 19.1 mm x 3.1 mm (0.7520 in. × 0.1220 in.) has the stress-strain behavior shown in the Animated Figure 6.22b. If this specimen is subjected to a tensile force of 98290 N (22100 Ib;) then (a) Determine the amount of elastic strain induced. (b) Determine the amount of plastic strain induced. (c) If its original length is 610 mm, what will be its final length after this force is applied and then released? The elastic modulus for steel is 207 GPa. (a) i (b) i (c) i mm
S Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 900 Metal A 600 Metal B 300 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, m/m FIGURE P1.16 Stress, MPa
Figure P1.16 shows the stress–strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calculations and units): Proportional limit Yield stress at an offset strain of 0.002 in./in. Ultimate strength Modulus of resilience Toughness Which metal is more ductile? Why?
Consider a cylindrical specimen of a steel alloy (Please see the figure) 0.33 in. in diameter and 3.15 inches long that is pulled in tension. given:-Elongation is 0.018 in-Tensile stress = 200 ksi -Tensile strain = 6.83*10^-3 -Ultimate stress = 281.82 ksi -Ultimate strain = 0.05solve: Fracture point (stress and strain values)
1.17 Figure P1.17 shows the stress-strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calcu- lations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 in./in. 150 - - Metal A 100 • Metal B 50 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, in./in. FIGURE P1.17 c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? Stress, ksi
If the yield stress in part c is considered failure stress, what is the maximumworking stress to be applied to this material if a factor of safety of 1.5 is used?
1. The following data were obtained during a tension test of an aluminum alloy. The initial diameter of the test specimen was 0.505 in., and the gage length was 2.0 in. Load ( Ib) Elongation (in.) Load ( Ib) Elongation (in.) 14000 0.020 2310 0.0022 14400 0.025 4640 0.0044 14 500 0.060 6950 0.0066 14600 0.080 9290 0.0088 14800 0.100 I1 600 0.0110 14600 0.120 13000 0.01 50 13600 Fracture Plot the stress-strain diagram and determine the following mechanical properties: a. proportional limit þ. modulus of elasticity S. vield stress at 0.2% offset d. ultimate stress e. nominal rupture stress.
Please answer letters a, b, c and d. Thank you!
Answer fast