Figure 1 shows the phase diagram of platinum-silver (Pt-Ag) at equilibrium. Determine the phases present, composition, and amount of each phase at 1100 °C and 60 wt.% Ag. Alloy 1 Alloy 2 1800 1600 Liquid 9 1400 L+a a 1186°C 1200 L+B 1000 800 a + B 600 42.4 10 20 30 40 50 60 70 80 90 100% 100% Weight percent silver Ag Pt Temperature (°C)

Figure 1 shows the phase diagram of platinum-silver (Pt-Ag) at equilibrium. Determine the phases present, composition, and amount of each phase at 1100 °C and 60 wt.% Ag. Alloy 1 Alloy 2 1800 1600 Liquid 9 1400 L+a a 1186°C 1200 L+B 1000 800 a + B 600 42.4 10 20 30 40 50 60 70 80 90 100% 100% Weight percent silver Ag Pt Temperature (°C)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The following drawing shows the phase diagram at constant pressure for two liquids (A and B). When 30 g of pure A and 70 g of pure B are mixed: a) Reason what the diagram looks like and identify each part. b) At what temperature will the mixture start to boil? What will be the composition of the steam at that time? c) What is the amount of distillate at 130C°? 160 P= Tatm 150 140 O 130 120 T10 100 O 10 20 30 40 50 60 70 80 90 100 % B In weight
Use the phase diagrams for Cu-Ni and Cu-Ag systems below to answer the question: i. Wt% Ni in the liquid a Cu-Ni system at point B above.
26. Please help me answer all parts to this physics question
Q4: For a 98 wt% Fe-2 wt% C at a temperature 700 °C, determine the following: a) The Number and types of The Phases Present. b) The Amount Of Phases Present in Grams That forms per 100 G. c)Draw The Microstructure Of Phases Present At This Point And What is The React called? d) Specify the following on Iron- Carbon Phase Diagram: (y+ L) phase, Eutectoid Reaction
7. Consider 1.5 kg of a 99.6 wt% Fe-0.4 wt% C steel that is cooled to a temperature just below the eutectoid. (a) How many kilograms of ferrite (a) form? (b) How many kilograms of cementite (Fe;C) form? Include your tie line in the solution. 1600| L 1400 T(°C) 1200 (austenite) y+L 1148°C L+Fe;C 1000 Y + Fe;C 800 727°C 600 a + Fe;C 400 1 2 4 6 6.7 C, wt% C Fe;C (cementite)
Shown to the right is the solid-liquid phase behavior for mixtures of component A and component B at 1 atm. Use the phase diagram to answer the following questions. a) Specify the melting point of substance B at 1 atm b) What is the maximum composition (mole fraction) of component B that is possible for the mixture to exist in phase S2? At what temperature does this occur? c) 20mol of component A and 180mol of component B are mixed at 350°C and 1 atm. The mixture is cooled at constant pressure to 200°C. i) What phases are present at the final state? ii) What is the composition of each phase at the final state? iii) What is the number of moles of each phase at the final state?
At what temperature does the first liquid phase form at 90% Ni? T(°C) 1600 1500 1400 1300 1200 1100 1000, L (liquid) L+α solidus liquidus 80 100 20 40 60 80 wt% Ni
None
briefly explain the "spherical manipulator" in robotics
Consider Al- Cu system below. When Al-40%Cu is heated above 600°C and cooled slowly to a temperature of 545°C . Answer the following. Use the values of composition given in the phase diagram , no estimation .Each has two marks. 700 1200 600 L a + L 6 +L 548 1000 500 (CUAL) a + 6 800 400 600 300 5.65 10 20 30 32.7 40 50 52.5 (AI) Composition (wt % Cu) a. Percentage of the pro-eutectic phase present (% no decimal places) b. Composition of the pro- eutectic phase present (in %Cu one decimal place) c. What is the percentage of larger eutectic component present (% no decimal places) Temperature (°C) Temperature (°F)
1. four processes. 2. Fill out the blanks by labeling the phase regions. 3. Identify the Indicate an in- termediate compound, if any. 3. Temperature (°C) 1600 1400 1200 1000 800 600 400 1538°C 0 (Fe) -1493°C 1394°C 912°C y, Austenite 1 2 0.16 5 0,022 a, Ferrite A N 2.14 Composition (at% C) 15 10 3 1147°C L4 3 4 Composition (wt% C) 4.30 727°C Sketch the microstructure at A, label phases, figure out compositions. 20 Cementite (Fe3C). 5 6 25 6.70
A Pb-30% Sn alloy is cooled from 300°C to 50°C. a) What phases are present for this alloy at 50°C? b) How much of each phase is present at 50°C? c) What is the primary phase and its amount for this alloy at 50°C? Composition (at% Sn) 20 40 60 80 100 327°C 600 300 Liquid 500 232°C a + L 200 ß + L 400 183°C 18.3 61.9 97.8 300 100 a + B 200 100 40 60 80 100 (Pb) Composition (wt% Sn) (Sn) Temperature (°C) 20 Temperature (°F)