Presume that we have 100 grams of an alloy with overall chemical composition of90 wt. pct. tin and 10 wt. pct. lead. The alloy (in the liquid state) is cooled atnear-equilibrium conditions.Determine the following:At slightly below 183oC, what are the following:(parts a-h at a temperature below 183C please!) Temperature (°C)a.300200b.10000327°C20Ta + L18.34020Composition (at% Sn)60183°C40a + BLiquid61.960Composition (wt% Sn)80B+L232°C97.81006005001400300200100(Pb)Figure 9.8 The lead-tin phase diagram.[Adapted from Binary Alloy Phase Diagrams, 2nd edition, Vol. 3, T. B. Massalski (Editor-in-Chief),1990. Reprinted by permission of ASM International, Materials Park, OH.]100(Sn)Presume that we have 100 grams of an alloy with overall chemical composition of90 wt. pct. tin and 10 wt. pct. lead. The alloy (in the liquid state) is cooled atnear-equilibrium conditions.Determine the following:At slightly below 183°C, what are the following:The chemical composition of proeutectic (or primary) a crystals.Temperature (°F)The chemical composition of proeutectic (or primary) ẞ crystals. C.d.e.f.g.h.The chemical composition of eutectic a crystals.The chemical composition of eutectic ß crystals.The amount of proeutectic a crystals.The amount of proeutectic ß crystals.The amount of eutectic a crystals.The amount of eutectic ß crystals.

The mass of alloy, m = 100 gm The composition of the alloy = 90 wt%Sn and 10 wt% Pb The temperature…

Presume that we have 100 grams of an alloy with overall chemical composition of 90 wt. pct. tin and 10 wt. pct. lead. The alloy (in the liquid state) is cooled at near-equilibrium conditions. Determine the following: At slightly below 183oC, what are the following: (parts a-h at a temperature below 183C please!)

Presume that we have 100 grams of an alloy with overall chemical composition of 90 wt. pct. tin and 10 wt. pct. lead. The alloy (in the liquid state) is cooled at near-equilibrium conditions. Determine the following: At slightly below 183oC, what are the following: (parts a-h at a temperature below 183C please!)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

2. Determine the amount of liquid phase in the a Cu-50% Ni alloy at 1300°C, % L 1500 1400 L. C +L 58 1300 1200 1100 1000 Cu 20 40 60 80 Ni Weight percent nickel Temperature (°C)
What is the composition, in wt% Cr2O3, of the liquid phase in an alloy containing 71 wt% Cr2O3 at 2200C?
In Figure 1 (phase diagram), an alloy composition of 95 wt% Mg and 5 wt% Al is cooled from 700 C to 475 C. An analysis of the resulting ε solid-phase composition reveals that it has a higher Mg content than is anticipated by the phase diagram.a) Explain why this might be the case and how your reasoning results in the higher-than-expected Mg content.b) Provide a sketch showing the likely distribution of Mg content within the volume of ε solid-phase.
Referring to Figure 1, please answer the following [NOTE: SHOW YOUR WORK on Figure 1]:a. provide the specific name for the phase boundary lines denoted by A and B. b. identify the phases present at equilibrium in the phase fields denoted by C, D, and E. c. identify the specific name for the point denoted by F. d. What is the maximum solid solubility of Mg in Al? At what temperature does it occur? e. An Al-Mg alloy (10 wt% Mg, 90 wt% Al) is heated slowly (to insure equilibrium) from a temperature of 200 C: i. At what temperature does the first liquid phase form? ii. What is the composition of the liquid phase at the temperature in part i.? iii. At what temperature does complete melting (no solid phase remaining) occur? iv. What is the composition of the last solid remaining prior to complete melting? f. Using the equilibrium phase diagram of Figure 1, identify the phases present, their compositions, and their relative mass fractions at equilibrium for a 70 wt% Mg – 30 wt% Al…
Q/ The phase present for a 30 wt% sn, 7O wt% pb of alloy at 200°c is (a+ L) Determine: Composition of (a) and (L) for both (sn) and (pb). * 327°C 300E Liquid 232°C a +L 200E B + L 183°C 18.3 61.9 97.8 100 a +B 20 40 60 80 100 (Pb) Composition (wt% Sn) (Sn) Ca =18 Wt% pb, CL=58 Wt% pb and Ca =82 Wt% Sn, CL=42 Wt% Sn. Ca =20 Wt% pb, CL=60 Wt% pb and Ca =80 Wt% Sn, CL=40 Wt% Sn. Ca =22 Wt% pb, CL=65 Wt% pb and Ca =78 Wt% Sn, CL=35 Wt% Sn. Ca =15 Wt% pb, CL=63 Wt% pb and Ca =85 Wt% Sn, CL=73 Wt% Sn. Temperature ("C)
Consider the phase diagram below. The three points A, B, and C are at concentrations of 26.4, 31.3, and 34 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300 L (liquid) 1200 20 A B C L + a C1 S liquidus L + a solidus a (solid) 50 wt% Ni a. Walpha=0.21; WL=0.33; Walpha/WL = 13.17 b. Walpha=0.09; WL=0.32; Walpha/WL = 15.00 c. Walpha=0.07; WL=0.46; Walpha/WL = 11.17 d. Walpha=0.14; WL=0.37; Walpha/WL = 9.00
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
Q.4) For 30 wt% Sn - 70 wr% Pb alloy at 125 °C, (a) what phases are present? (b) What are the compositions of the phases? (c) Calculate the relative mass fraction of each phase present. Composition (at% Br 100 80 60 40 20 A 3270 Temperature (C) 300 200 100 0 0. (Pb) Solvus Solidu a+L B 18.3 20 liquidus Liquid 183 C 61.9 40 60 Composition (wt% Sn) 80 L 232 C G 97.8 1 600 500 P 400 (3) angesadway 300 200 H 100 100 (Sn)
A hypothetical eutectic phase diagram for metals A and B shows that cooling a liquid melt with a concentration of 50 wt% A-50 wt% B to just below 625 °C (eutectic isotherm temperature) results in simultaneous formation of alpha and beta phases. The phase diagram also shows that alpha (A rich) and beta (B rich) phases exist at left and right extremes of the phase diagram, respectively. At the eutectic isotherm temperature, the maximum solubility of B in A and A in B is 10 wt% and 5 wt%, respectively. The phase diagram does not have any intermetallic compounds. A new solid alloy is made by melting together 86 gr of a 40 wt% A-60 wt% B alloy with 136 gr of 65 wt% A-35 wt% B alloy followed by cooling the melt to 400 °C. If the new alloy is heated up from 400 °C to just below 625 °C, answer the following questions: a. Calculate the overall alloy composition. b. Determine phases present and calculate their respective masses. Calculate the masses of the primary phase, eutectic phase, and…
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementite
A 10 30 70 1) For an A-B alloy of composition 25 wt% B (i) Draw the microstructure at T (just above the eutectoid temperature) and calculate the fraction of each phase in the microstructure. (ii) Draw the microstructure at T (just below the eutectoid temperature) and determine the amount of each phase, i.e., fraction of proeutectoid alpha, eutectoid alpha and eutectoid beta. 2) Provide a brief summary of phase transformations which are often observed in the iron-carbon alloy system due to various heat treatment procedures carried out to tune the microstructure. Compare mechanical strength and ductility of the materials/microstructures that form as a result of such heat treatment processes.
Calculate the amounts and compositions of phases at 726oC in a Fe-0.6% C alloy cooled under equilibrium conditions. Disregard the amounts of proeutectoid phases. A. 77.3% α, 22.7% Fe3C; C in α = 6.7% and C in Fe3C = 0.02% B. 91.3% α, 8.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% C. 77.3% α, 22.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% D. 91.3% α, 8.7% Fe3C; C in α = 0.05% and C in Fe3C = 8.4% E. None of the mentioned