The following question refer to the phase diagram shown here.Composition (at% Sn)60TTemperature (°C)300200OC0100327°CO 98 wt% SnO 100 %O 61.9 wt% Sn0 0%O 73 wt% Sn20TO 50%O 90 wt% Sn18.340T20183°Ca + ß40TLiquid61.980B+L80232°C97.8100→600010060Composition (wt% Sn)(Pb)(Sn)Adapted from Binary Alloy Phase Diagrams, 2nd edition, Vol. 3, T. B. Massalski (Editor-in-Chief), 1990. Reprintedby permission of ASM International, Materials Park, OH.In the Pb-Sn phase diagram, what is the approximate composition of the 3 phase for an alloy with 90 wt% Sn and at 200°C?500400B300 a200Temperature (°F)100

Given 90%wt Sn at 200oC To find Approximate composition of Beta phase

a + L in 18.3 20 183°C 40 a + ß Liquid 61.9 80 B+L 232°C 97.8 al 600 500 400 300 60 100 Composition (wt% Sn) (Sn) Alloy Phase Diagrams, 2nd edition, Vol. 3, T. B. Massalski (Editor-in-Chief), 1990. Reprinted M International, Materials Park, OH. phase diagram, what is the approximate composition of the 3 phase for an alloy with 90 wt% Sn and at 200°C? 200 100 Temperature (°F)

a + L in 18.3 20 183°C 40 a + ß Liquid 61.9 80 B+L 232°C 97.8 al 600 500 400 300 60 100 Composition (wt% Sn) (Sn) Alloy Phase Diagrams, 2nd edition, Vol. 3, T. B. Massalski (Editor-in-Chief), 1990. Reprinted M International, Materials Park, OH. phase diagram, what is the approximate composition of the 3 phase for an alloy with 90 wt% Sn and at 200°C? 200 100 Temperature (°F)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Use the Lead-Tin (Pb-Sn) phase diagram below to answer the following questions: Place the following microstructures in the correct order of formation for slowly cooling a 98 wt% Sn alloy from 300 °C to room temperature (point A to point B).
Temperature ("C) Temperature ($1 Consider 1 kg of Copper - Silver alloy (Cu - Ag) containing 75 wt% Ag. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 778 °C (just below the eutectic temperature). Calculate the mass in kg of the eutectic phase B (phase B that appears during the eutectic reaction) that forms? Composition (at% Ag 20 40 60 100 2200 80 1200 2000 Liquidus 1000 LIquid 1800 Solidus 1600 800 779°C (T 80 91.2 1400 IC. 1200 600 Solvus T000 400 800 200 20 40 80 100 (Cu) Composioon wt A
Hi i keep getting these wrong
According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
Temperature (°C) 700 600 0 500 400 300 0 (AI) a 5 a+L 10 Composition (at% Cu) 10 20 a +0 L 30 Composition (wt% Cu) 20 0+ L 0 (CuAl₂) 40 30 50 1200 1000 800 600 Temperature (°F) a) For the alloy represented by the phase diagram above, what is the wt% content of eutectic if an alloy of 2.5 wt% Cu is cooled very slowly from the molten state to 300°C? b) What phases are present in 2.5 wt% Cu material if it is quenched from 550°C?
Figure 2 refers to the phase diagram for silver and tin. Label the regions (1) to (5) Temperature, 0/°C 1000 800 600 400 200 0 Liquid 2 Ag,Sn 60 a 20 40 80 Mass percentage Ag/% 100 Question 6: What will be observed when liquids of composition of 40% Ag are cooled to 200 K? When will it begin to precipitate? When will it become solid?
Please help me urgent
5. [Phase Diagram] (1) Here is Cu-Ag phase diagram and two cases (composition and temperature) are given below. At each case, (i) cite the phase(s) present(s), (ii) estimate the phase composition(s), (iii) weight fraction of the phase(s) and (iv) sketch its microstructure for the following alloy. () a. 71.9 wt% Ag-28.1 wt% Cu at just above 779 °C b. 71.9 wt% Ag-28.1 wt% Cu at just below 779 °℃ Temperature (°C) 1200 A 1000 800 600 400 0 200 0 α C (Cu) B 8.0 (Ca E) -Solidus Solvus 20 20 a + L Composition (at% Ag) -Liquidus 779°C (TE) 40 40 a + B Liquid 60 Composition (wt% Ag) 60 E 71.9 (CE) 80 80 B+L 91.2 (CBE) G 100 B H 2200 2000 1800 F 1600 1400 1200 1000 800 600 400 100 (Ag) Temperature (°F)
Please tell me statements in the question is true or false with small reason of your answer Part 2
Composition lat% N 40 60 100 1600 2800 1500 1453 C 2600 Liquid 1400 Solidus line Liquidua line 2400 1300 1200 2200 1100 1085 C 2000 1000 20 40 100 Composition (wt N (NO What is the amount for each phase in 1kg of a 50% Ni-50% Cu alloy at temperatures of 1400, 1300, or 1200 degrees C for point A and point B? Temperature ('C) Temperature ("F)
please answer correctly and completly
5