At an axial load of 22 kN, a 15-mm-thick x 35-mm-wide polyimide polymer bar elongates 4.2 mm while the bar width contracts 0.25 mm. The bar is 215-mm long. At the 22-kN load, the stress in the polymer bar is less than its proportional limit. Determine Poisson's ratio. 0.366 61616 O 0.336 0.473 O 0.229 0.427

At an axial load of 22 kN, a 15-mm-thick x 35-mm-wide polyimide polymer bar elongates 4.2 mm while the bar width contracts 0.25 mm. The bar is 215-mm long. At the 22-kN load, the stress in the polymer bar is less than its proportional limit. Determine Poisson's ratio. 0.366 61616 O 0.336 0.473 O 0.229 0.427

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

An extruded polymer beam is subļected to a bending moment M. The length of the beam is L = 860 mm. The cross-sectional dimensions of the beam are bq = 36 mm, d = 89 mm, b2 = 22 mm, d2 = 22 mm, and a = 7 mm. For this material, the allowable tensile bending stress is 10 MPa, and the allowable compressive bending stress is 10 MPa. Determine the largest moment M that can be applied as shown to the beam. b2 ja a M d2 d1 A B b1 Answer: 410.8451 N-m
An aluminum rod is rigidly attached between a steel rod and a bronze rod as shown. Axial loads are applied at the positions indicated. Find the maximum value of P in kN that will not exceed a stress in steel of 140 MPa, in aluminum of 90 MPa, or in bronze of 100 MPa
A high-density polyethylene [E = 121 ksi and a = 61 x 10-6/°F] block (1) is positioned in a fixture. The block is 2.2 in. by 2.7 in. by 29 in. long. At room temperature, a gap of 0.11 in. exists between the block and the rigid support at B. Determine: (a) the normal stress o in block (1) caused by a temperature increase of 98°F. (b) the normal strain & in block (1) at the increased temperature. [ Answerrs: (a) o = (b) = 0.11 in. 29 in. Ans: (a) - 264.3725 με. (b) 3793.1033 psi.
ox The state of stress at a given point in a material component is = 120 MPa; Oy = - 80 MPa and t = 60 MPa The loading on the component is increased so that stresses are increased to values which are k times the given values. Determine the maximum value of k if the material can withstand maximum normal and shear stresses of 300 MPa and 200 MPa respectively. 1 11
At an axial load of 25 kN, a 50-mm-wide by 15-mm-thick polyimide polymer bar elongates 3.1 mm while the bar width contracts 0.26 mm. The bar is 220 mm long. At the 25-kN load, the stress in the polymer bar is less than its proportional limit Determine (a) the modulus of elasticity. (b) Poisson's ratio. (c) the change in the bar thickness. Answers: (a) E- (b) v- (c) Audness GPa mm
30. An aluminum alloy rod has a circular cross section with a diameter of 8mm. The rod is subjected to a tensile load of 5kN. Assume that the material is in the elastic region and E = 69 GPa. If Poisson's Ratio is 0.33, what will be the lateral strain? E= 6/8 v = -E(lateral)/(axial)
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 500 mm. The cross-sectional dimensions of the beam are b₁ = 38 mm, d₁ = 82 mm, b₂ = 23 mm, d₂ = 23 mm, and a = 7.5 mm. For this material, the allowable tensile bending stress is 14 MPa, and the allowable compressive bending stress is 12 MPa. Determine the largest moment M that can be applied as shown to the beam. b₂ a M d₁ B L N-m | A Answer: M= d₂ b₁
Knowing that a 0.03-in. gap exists when the temperature is 85 °F, determine the temperature at which the normal stress in the aluminum bar will be equal to-11 ksi. T= OF 0.03 in. 12 in. Bronze A = 2.2 in.² E = 15 × 106 psi a = 12 x 10-6°F 16 in.. Aluminum A = 2.8 in.² E = 10.6 × 106 psi a = 12.9 × 10 6 °F Ans = 250
In a steel railroad, the 12 meters long rails are laid with a clearance of 5 mm at a temperature of 20 degrees centigrade. The modulus of elasticity of steel is 200 GPa. a) At what temperature will the rails just touch if the coefficient of linear expansion is 11.7x10^-6/°C.? b) Determine the stress in the rails at 65 °C
In a tensile test on a metal specimen having a cross section 20 mm by 10 mm elastic breakdown occurred at a load of 70 000 N. A thin plate madec from the same material is to be subjected to loading such that at a certain point in the plate the stresses are o,=-70 N/mm², 7.y= 60 N/mm² and o. Determine the maximum allowable values of o, using the Tresca and von Mises theories of elastic breakdown. Ans. 259 N/mm² (Tresca), 294 N/mm² (von Mises).
6. Derive the resolved shear stress(RSS) equation for dislocation at an arbitrary plane at angle (e) with horizontal under nominal axial tensile stress(o) and plot the variation of Schmidt factor with
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 620 mm. The cross-sectional dimensions of the beam are b1 = 32 mm, d1 = 117 mm, b2 = 19 mm, d2 = 19 mm, and a = 6.5 mm. For this material, the allowable tensile bending stress is 13 MPa, and the allowable compressive bending stress is 13 MPa. Determine the largest moment M that can be applied as shown to the beam. b2 a M | A В