2.77 A steel rod 3 ft long with a cross-sectional area of 0.3 in.² is stretched between two fixed points. The tensile force in the rod is 1200 lb at 40°F. Using a = 6.5 x 10-6/°F and E = 29 × 106 psi, calculate the temperature at which the stress in the rod will be (a) 10 ksi; and (b) zero.

2.77 A steel rod 3 ft long with a cross-sectional area of 0.3 in.² is stretched between two fixed points. The tensile force in the rod is 1200 lb at 40°F. Using a = 6.5 x 10-6/°F and E = 29 × 106 psi, calculate the temperature at which the stress in the rod will be (a) 10 ksi; and (b) zero.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A 23 mm diameter bronze bar 2.8 m long is placed between two rigid walls. At a temperature of -3°C, the gap Δ = 4.6 mm. Find the temperature(at degree-Celsius) at which the compressive stress in the bar will be 34 MPa. Use α = 18.09 × 10-6 m/(m·°C) and E = 82 GPa. Answer in two decimal places. Numerical values only. Don't indicate units here, just on the submitted solution.
A member is formed by connecting two steel bars shown below. Assuming that the bars are prevented from buckling sideways, calculate the magnitude force "P" that will cause the total length of the member to decrease 0.29 mm the values of elastic modulus for steel is 217 MPa. Take H1 = 4 cm, H2 = 11 cm, top bar (R) is 3 x 3 cm and bottom bar (Q) is 7 x 7 cm. Also, determine the stress-induced in each section of the bar. i) Magnitude Force, P = ii) Stress-induced in the top bar = iii) Stress-induced in the bottom bar =
Compound axial member ABC has a uniform diameter of d = 2.9 in. Segment (1) is an aluminum [E₁ = 10,000 ksi] alloy and segment (2) is a copper [E₂ = 17,000 ksi] alloy. The lengths of segments (1) and (2) are L₁ = 90 in. and L₂ = 130 in., respectively. Determine the force P required to stretch compound member ABC by a total of 0.30 in. L₁ P L2 Aluminum B Copper CP A Answer: P= i kips
Calculate the increase in stress for each segment of the compound bar shown. If the temperature increases by 100°F,assume that the length of the aluminum rod is 15 in and 20 in for the steel rod. Steel Aluminum A : 3.0 in² E = 10 x 105 psi a = 12.8 x 105/°F A = 1.5 in² E = 29 x 105 psi α = 6.5 x 10" / °F 10 in 15 in Figure P-266
The bronze bar 2.7 m long with a cross-sectional area of 415 mm2 is placed between two rigid walls. At a temperature of 8.1 °C, there is a gap Δ = 2.32 mm, as shown in the figure. Find the compressive force (in N) experienced by the bar at a temperature of 68.66 °C. Use α = 18 × 10-6 /°C and E = 80.71 GPa. Round off your answer to three decimal places.
The rigid, horizontal slab is attached to two identical copper rods. There is a gap = 0.18 mm between the middle bar, which is made of aluminum, and the slab. Neglecting the mass of the slab, calculate the stress in each rod when the temperature in the assembly is increased by 85 degrees Celsius. A(mm²) α/°C E (GPa) Copper Rod 500 16.8 x 10-6 120 Aluminum 400 23.1 x 10-6 70 Copper Aluminum Copper 750 mm
The 981-kg uniform bar AB is suspended from two cables AC and BD each with cross-sectional area 339 mm2. Find the location x (in mm) of P that can be safely applied to the bar if the stresses in AC and BD are limited to 119 MPa and 52 MPa, respectively. Express your answer in two decimal places.
50 mm PROBLEM 2.55 Brass 37.5 mm A brass link (E, = 105 GPa, a, = 20.9x10/°C) and a steel rod (E, = 200 GPa, a =11.7x10/°C) have the dimensions shown at a temperature of 20°C. The steel rod is cooled until it fits freely into the link. The temperature of the whole assembly is then raised to 45°C. Determine (a) the final stress in the steel rod, (b) the final length of the steel rod. 37.5 mm 0.12 mm -250 mm 30-mm diameter Steel A Section A-A 0, =-36.8 MPa L, = 250.147 mm %3D
The bronze bar 2.72 m long with a cross-sectional area of 496 mm2 is placed between two rigid walls. At a temperature of 8.61 °C, there is a gap Δ = 2.28 mm, as shown in the figure. Find the compressive force (in N) experienced by the bar at a temperature of 61.85 °C. Use α = 18 × 10-6 /°C and E = 80.84 GPa. Round off your answer to three decimal places.
A long metal plate (E = 210 GPa) with some cutouts in it is mounted between two rigid plates at 6 am. By noon, the temperature has risen by 20°C. The structure is made from aluminium with a coefficient of thermal expansion of a = 23 x 10-6/°C. Please use the stress concentration chart shown below for any relevant calculations. a10 h L b O Use the following values in your working out: K 3.2 3.0 2.8 2.6 2.4 2.2 2.0 L = 13 m 0 0.1 P 0.2 W W Javg 0.3 2r P (w2r)t 0.4 P ▬▬▬▬▬▬▬ 0.5 h = 5.3 m a = 0.8 m b = 1.6 m a) What is the average normal stress throughout the plate at noon? b) What is the maximum stress at any point in the structure? c) The material the plate is made from has a tensile yield stress of 416 MPa and a compressive yield stress of 200 MPa. Using these values, do you expect the plate to yield at/before noon?
A steel rod 3 ft long with a cross-sectional area of 0.3 in2 is stretched between two fixed points. The tensile force in the rod is 1200 lb at 40°F. Using α = 6.5 x 10-6/°F and E = 29 x 106 psi, calculate the temperature (in °F) at which the stress in the rod will be zero.
2. A wire is stretched between 2 rigid posts separated by a distance L. If the surrounding temperature changes from T₁ to T₂ with T₂ 0? Or is AF < 0? How does Young's modulus of elasticity figure in your analysis? Explain.