Chapter 36, Problem 21RQ
If a curved plate is to be straightened by flame straightening, should the heat be applied to the longer or shorter surface of the arc? Why?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Q6] (20 Marks) Select the most suitable choice for the following statements: modo digi
-1A 10 af5
1 -The copper-based alloy which is responded to age hardening is
a) copper-nickel
b) aluminum bronze c) copper - beryllium d) brass besincaluy
2- Highly elastic polymers may experience elongations to greater than....
b) 500%
bromsia-P
c) 1000%. d) 1200% 15m or -2
a)100%
3- The cooling rate of quenching the steel in saltwater will be ......the cooling rate of quenching ir
c) faster than sold) none of them
a) slower than
4- Adding of
a) Cr
b) the same as
...... Will lead to stabilize the
b) Mo
10
austenite in steel.
c) Nimble avolls 1d) Sized loloin nl
5- The adjacent linear chains of crosslinked polymers are joined one to another at various positic
DIR...
by.........bonds
c) covalent noisqo gd) ionic lg 120M
6- For the ceramic with coordination number 6 the cation to anion radius ratio will be
a) Van der Waals
a) 0.155-0.225
a) linear
b) hydrogen
(b) 0.225-0.414
c) 0.414 0.732
..polymers.…
Examine
Notes: Attempt Six Questions Only.
rever necessa ,
Q1] (20 Marks) Answer with true (T) or false (F), corrects the wrong phrases, and gives sho
reasons for correct and corrected statements:
1- High chromium irons are basically grey cast irons alloyed with 12 to 30 % Cr.
yous board-19qgo orT-1
2- The drawbacks of Al- Li alloys are their high young modulus and high density.&M 0) (0
3- Vulcanized rubbers are classified under thermoplastic polymers.
4- Diamond is a stable carbon polymorph at room temperature and atmospheric pressure. (
5- The metallic ions of ceramic are called anions, and they are positively charged.
yldgiH-S
69001(6
H.W 5.4
Calculate the load that will make point A move to the left by 6mm, E-228GPa. The diameters
of the rods are as shown in fig. below.
2P-
PA
50mm
B
200mm
2P
0.9m
1.3m
Chapter 36 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 36 - What is the principal fuel gas used in oxyfuel-gas...Ch. 36 - Why does an oxyfuel-gas welding torch usually have...Ch. 36 - What is the location of the maximum temperature in...Ch. 36 - What function or functions are performed by the...Ch. 36 - What three types of flames can be produced by...Ch. 36 - Which type of oxyfuel flame is most commonly used?Ch. 36 - What are some of the alternative fuels (other than...Ch. 36 - Why might a welder want to change the tip size (or...Ch. 36 - What is filler metal, and why might it be needed...Ch. 36 - What is the role of a welding flux?
Ch. 36 - Oxyfuel-gas welding has a low rate of heat input....Ch. 36 - For what types of applications is ox\fuel-gas...Ch. 36 - What are some of the more attractive features of...Ch. 36 - How does pressure gas welding differ from the...Ch. 36 - In what way does the torch cutting of ferrous...Ch. 36 - Why might it be possible to use only an oxygen...Ch. 36 - How does an oxyacetylene cutting torch differ from...Ch. 36 - What are some of the ways in which cutting torches...Ch. 36 - When might stack cutting be an attractive process?Ch. 36 - What modification must be incorporated into a...Ch. 36 - If a curved plate is to be straightened by flame...Ch. 36 - Why does the flame-straightening process not work...Ch. 36 - What sorts of problems plagued early attempts to...Ch. 36 - What are the three basic types of current and...Ch. 36 - What is the attractive feature of variable...Ch. 36 - What is the difference between a consumable and...Ch. 36 - What are the three types of metal transfer that...Ch. 36 - What are some of the process variables that must...Ch. 36 - What are the four primary consumable-electrode...Ch. 36 - What are some general properties of the...Ch. 36 - What are some of the functions of the electrode...Ch. 36 - How are welding electrodes commonly classified,...Ch. 36 - Why are shielded metal arc electrodes often baked...Ch. 36 - What are the functions of the fluxing constituents...Ch. 36 - What benefit can be obtained by placing iron...Ch. 36 - Why are shielded metal arc electrodes generally...Ch. 36 - Why is the shielded metal arc welding process...Ch. 36 - What are some of the attractive features of the...Ch. 36 - What is the advantage of placing the flux in the...Ch. 36 - What feature enables the welding current in FCAW...Ch. 36 - What are some of the advantages of gas metal arc...Ch. 36 - Describe the relative performance of argon,...Ch. 36 - For what welding conditions would short circuit...Ch. 36 - What is the least desired mode of metal transfer?Ch. 36 - Which of the metal transfer mechanisms is most...Ch. 36 - Describe the metal transfer that occurs during...Ch. 36 - What are some of the benefits that can be obtained...Ch. 36 - What are some of the attractive features of gas...Ch. 36 - What are some of the primary process variables in...Ch. 36 - What is the attractive feature of advanced gas...Ch. 36 - What other gas metal arc welding modifications...Ch. 36 - What benefits can be gained by using a rectangular...Ch. 36 - What are some of the functions of the flux in...Ch. 36 - What are some of the attractive features of...Ch. 36 - What is the primary goal or objective in bulk...Ch. 36 - What is the current (or proper) designation for...Ch. 36 - What types of shielding gases are used in the gas...Ch. 36 - What are some of the features that must be...Ch. 36 - What can be done to increase the rate of filler...Ch. 36 - What are some of the attractive features of gas...Ch. 36 - For the GTAW process, what are the attractive...Ch. 36 - What are some of the advantages of employing a...Ch. 36 - How are the spot welds produced by gas tungsten...Ch. 36 - How is the heating of the workpiece during plasma...Ch. 36 - What are the two different gas flows in plasma arc...Ch. 36 - What are some of the attractive features of plasma...Ch. 36 - What is the keyhole effect in plasma arc welding?Ch. 36 - What is the primary difference between plasma arc...Ch. 36 - What is the primary objective of stud welding?Ch. 36 - What is the function of the ceramic ferrule placed...Ch. 36 - 71- Describe the sequence of activity in flash...Ch. 36 - How is percussion welding different from flash...Ch. 36 - Prob. 73RQCh. 36 - Describe the ideal thermal cut.Ch. 36 - What is the purpose of the oxygen in oxygen arc...Ch. 36 - Why is plasma arc cutting an attractive wav of...Ch. 36 - What techniques can be used to constrict the arc...Ch. 36 - Compared to oxyfuel cutting, what are some of the...Ch. 36 - How can a nontransferred arc plasma torch be used...Ch. 36 - What are some of the attractive features of...Ch. 36 - What are some of the benefits of performing plasma...Ch. 36 - Describe the relative size of the heat-affected...Ch. 36 - Why might the residual stresses induced during...Ch. 36 - Prob. 84RQCh. 36 - What are typical arc welding currents and...Ch. 36 - What are the attractive features or benefits of an...Ch. 36 - What are jigs, fixtures or positioners, and how...Ch. 36 - Describe thermal deburring.Ch. 36 - When welds fail, it is not uncommon for the...Ch. 36 - For each of the conditions in Problem l, could...Ch. 36 - Using the Internet or technical literature,...Ch. 36 - Using the Internet or technical literature,...Ch. 36 - Identify a new or recent EPA or OSHA regulation...Ch. 36 - Magnesium, while not as strong as steel or...Ch. 36 - Numerous joints appear in bicycle frames, some of...
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
A nozzle at A discharges water with an initial velocity of 36 ft/s at an angle with the horizontal. Determine ...
Vector Mechanics For Engineers
Determine the maximum deflection of the simply supported beam. The beam is made of wood having a modulus of ela...
Mechanics of Materials (10th Edition)
The current source in the circuit shown generates the current pulse
Find (a) v (0); (b) the instant of time gr...
Electric Circuits. (11th Edition)
Consider a class BasketballGame that represents the state of a basketball game. Its attributes are The name of ...
Java: An Introduction to Problem Solving and Programming (8th Edition)
Words that have predefined meaning in a programming language are called _____ .
Starting Out With Visual Basic (8th Edition)
Multiple Stock Sales Use the method that you wrote for Programming Challenge 10 (Stock Profit) in a program tha...
Starting Out with Java: From Control Structures through Objects (7th Edition) (What's New in Computer Science)
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- d₁ = = Two solid cylindrical road AB and BC are welded together at B and loaded as shown. Knowing that 30mm (for AB) and d₂ 50mm (for BC), find the average normal stress in each road and the total deformation of road AB and BC. E=220GPa H.W 5.3 60kN A For the previous example calculate the value of force P so that the point A will not move, and what is the total length of road AB at that force? P◄ A 125kN 125kN 0.9m 125kN 125kN 0.9m B B 1.3m 1.3marrow_forwardClass: B Calculate the load that will make point A move to the left by 6mm, E-228GPa The cross sections of the rods are as shown in fig. below. 183 P- Solution 1.418mm 200mm 80mm 3P- 18.3 A 080mm B 200mm 3P- 0.9m إعدادات العرض 1.3m 4.061mmarrow_forwardH.W6 Determine the largest weight W that can be supported by two wires shown in Fig. P109. The stress in either wire is not to exceed 30 ksi. The cross- sectional areas of wires AB and AC are 0.4 in2 and 0.5 in2, respectively. 50° 30° Warrow_forward
- Find equation of motion and natural frequency for the system shown in fig. by energy method. H.W2// For the system Fig below find 1-F.B.D 2-Eq.of motion 8wn 4-0 (5) m. Jo marrow_forward2. Read the following Vernier caliper measurements. (The scales have been enlarged for easier reading.) The Vernier caliper is calibrated in metric units. (a) 0 1 2 3 4 5 سلسلسله (b) 1 2 3 4 5 6 سلسل (c) 1 23456 (d) 1 2 3 4 5 6 سلسلسarrow_forwardExplain why on the interval 0<x<1000 mm and 1000<x<2000mm, Mt is equal to positive 160 Nm, but at x= 0mm and x=1000mm Mt is equal to -160 Nm (negative value!). What is the reason for the sign change of Mt?arrow_forward
- 20 3. 2-233 2520 Тр Gears 1079 A pair of helical gears consist of a 20 teeth pinion meshing with a 100 teeth gear. The pinion rotates at Ta 720 r.p.m. The normal pressure angle is 20° while the helix angle is 25°. The face width is 40 mm and the normal module is 4 mm. The pinion as well as gear are made of steel having ultimate strength of 600 MPa and heat treated to a surface hardness of 300 B.H.N. The service factor and factor of safety are 1.5 and 2 respectively. Assume that the velocity factor accounts for the dynamic load and calculate the power transmitting capacity of the gears. [Ans. 8.6 kWarrow_forward4. A single stage helical gear reducer is to receive power from a 1440 r.p.m., 25 kW induction motor. The gear tooth profile is involute full depth with 20° normal pressure angle. The helix angle is 23°, number of teeth on pinion is 20 and the gear ratio is 3. Both the gears are made of steel with allowable beam stress of 90 MPa and hardness 250 B.H.N. (a) Design the gears for 20% overload carrying capacity from standpoint of bending strength and wear, (b) If the incremental dynamic load of 8 kN is estimated in tangential plane, what will be the safe power transmitted by the pair at the same speed?arrow_forwardDetermine the stress in each section of the bar shown in Fig. when subjected to an axial tensile load shown in Fig. The central section is 30 mm hollow square cross- section; the other portions are of circular section, their diameters being indicated What will be the total deformation of the bar? For the bar material E = 210GPa. 20mi О 30mm 30mmm 2.6 15mm 30kN 1 2 10kN - 20kN 3 -329 91mm 100mm 371mmarrow_forward
- Calculate the load that will make point A move to the left by 6mm, E=228GPa. The diameters of the rods are as shown in fig. below. 2P- PA 80mm B 200mm 2P 0.9m 1.3m.arrow_forwardIf the rods are made from a square section with the dimension as shown. Calculate the load that will make point A move to the left by 6mm, E=228GPa. 2P- P A 80mm B 200mm 2P 0.9m 1.3marrow_forward3. 9. 10. The centrifugal tension in belts (a) increases power transmitted (b) decreases power transmitted (c) have no effect on the power transmitted (d) increases power transmitted upto a certain speed and then decreases When the belt is stationary, it is subjected to some tension, known as initial tension. The value of this tension is equal to the (a) tension in the tight side of the belt (b) tension in the slack side of the belt (c) sum of the tensions in the tight side and slack side of the belt (d) average tension of the tight side and slack side of the belt The relation between the pitch of the chain (p) and pitch circle diameter of the sprocket (d) is given by 60° (a) p=d sin (c) p=d sin (120° T where T Number of teeth on the sprocket. 90° (b) p=d sin T 180° (d) p=d sin Tarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage Learning
Welding: Principles and Applications (MindTap Cou...
Mechanical Engineering
ISBN:9781305494695
Author:Larry Jeffus
Publisher:Cengage Learning
Metal Joining Process-Welding, Brazing and Soldering; Author: Toc H Kochi;https://www.youtube.com/watch?v=PPT5_fDSzGY;License: Standard YouTube License, CC-BY