Question
Chapter 32, Problem 45SDP
To determine
Obtain a soldering iron and attempt to solder two wires together. First, try to apply the solder at the same time as you first put the soldering iron tip to the wires. Second, preheat the wires before applying the solder. Repeat the same procedure for a cool surface and a heated surface. Record your results and explain your findings.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A resistance spot-welding operation is
performed on two pieces of 1.5 mm thick
sheet steel using 12000 amps current for a
duration of 0.20 second. The electrodes are
6 mm in diameter at the contacting surfaces.
Resistance is assumed to be 0.0001 ohms
and the resulting weld nugget is 6 mm in
diameter and 2.5 mm thick. The unit melting
energy for the metal is 12 Jmm³. What portion
of heat generated was used to form the weld?
An RSW operation is used to join two pieces of sheet steel having a unit melting energy of 8369.85 J/cm3. The sheet steel has a thickness of 0.3125 cm. The weld duration will be set at 0.25 sec with a current of 11,000 amp. Based on the electrode diameter, the weld nugget will have a diameter of 0.75 cm. Experience has shown that 40% of the supplied heat melts the nugget and the rest is dissipated by the metal. If the electrical resistance between the surfaces is 130 micro-ohms, what is the thickness of the weld nugget assuming it has a uniform thickness?
What is a cold solder joint? Identify its causes, its appearance, and the means of correction.
Chapter 32 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 32 - What is the difference between brazing and...Ch. 32 - Are fluxes necessary in brazing? If so, why?Ch. 32 - Why is surface preparation important in...Ch. 32 - What materials are typically used in solder?Ch. 32 - Soldering is generally applied to thinner...Ch. 32 - Explain the reasons why a variety of mechanical...Ch. 32 - List three brazing and three soldering techniques.Ch. 32 - Describe the similarities and differences between...Ch. 32 - What precautions should be taken in the...Ch. 32 - What difficulties are involved in joining...
Ch. 32 - Prob. 11RQCh. 32 - What are the principles of (a) wave soldering...Ch. 32 - What is a peel test? Why is it useful?Ch. 32 - What is a combination joint?Ch. 32 - Prob. 15RQCh. 32 - Prob. 16QLPCh. 32 - Prob. 17QLPCh. 32 - Comment on your observations concerning the...Ch. 32 - Give examples of combination joints other than...Ch. 32 - Discuss the need for fixtures for holding...Ch. 32 - Explain why adhesively bonded joints tend to be...Ch. 32 - It is common practice to tin-plate electrical...Ch. 32 - Give three applications where adhesive-bonding is...Ch. 32 - Prob. 24QLPCh. 32 - If you are designing a joint that must be strong...Ch. 32 - Prob. 26QLPCh. 32 - Rate lap, butt, and scarf joints in terms of...Ch. 32 - Prob. 28QLPCh. 32 - Prob. 29QTPCh. 32 - Prob. 30QTPCh. 32 - Prob. 31QTPCh. 32 - Figure 32.4 shows qualitatively the tensile and...Ch. 32 - When manufacturing the fuselage of a commuter...Ch. 32 - Prob. 34SDPCh. 32 - Name several products that have been assembled...Ch. 32 - Suggest methods of attaching a round bar (made of...Ch. 32 - Prob. 38SDPCh. 32 - Prob. 39SDPCh. 32 - Prob. 40SDPCh. 32 - Prob. 41SDPCh. 32 - Describe part shapes that cannot be joined by...Ch. 32 - Prob. 43SDPCh. 32 - Prob. 44SDPCh. 32 - Prob. 45SDPCh. 32 - Prob. 46SDPCh. 32 - Review Fig. 32.9a and explain the shortcoming...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Hard soldering of metals can be done in the melting point temperature range of O 183°C-212°C 650°C-700°C O 1600°C-1700°C O 6000°C-7000°Carrow_forwardA GTAW operation is performed on low carbon steel, whose unit melting energy is 10.3 J/mm3. The welding voltage is 22 volts and the current is 135 amps. The heat transfer factor is 0.7 and the melting factor is 0.65. If filler metal wire of 3.5 mm diameter is added to the operation, the final weld bead is composed of 60% volume of filler and 40% volume base metal. If the travel speed in the operation is 5 mm/sec, determine (a) cross-sectional area of the weld bead, and (b) the feed rate (mm/sec) at which the filler wire must be supplied.arrow_forwardHow do most manufacturers classify or group hard-facing or wear-resistant electrodes?arrow_forward
- A continuous fillet wild is used to weld two pieces of 7.0-mm-thick austenitic stainless steel plate in an arc-welding operation. The plates are joined at a 90° angle using an inside fillet corner joint. The velocity of the welding head is 6 mm/sec. Assume the cross section of the weld bead approximates a right angle isosceles triangle (a right triangle with the two legs and their corresponding angles equal) with a leg length of 4.5 mm. The length of the weld = 230 mm. The melting factor of the setup = 0.65, the heat transfer factor = 0.90, and the Tm for austenitic stainless steel = 1670°K. Determine (a) The amount of heat (in joules) required to melt the volume of metal in (b) The heat that , (c) The rate of heat generation required at the welding source to accomplish the weld this weld (filler metal plus base metal) must be generated at the heat sourcearrow_forwardQUESTION 1 In an arc welding operation, a groove weld has a cross-sectional area=0.055 in² and is 24 in long. (Round your final answers to 1 decimal place) (a) What quantity of heat (in Btu) is required to accomplish the weld, if the metal to be welded is aluminum? Btu (b) How much heat must be generated at the welding source, if the heat transfer factor = 90% and the melting factor = 60%? H= Btuarrow_forwardIn one type of welding, electric charge flows between the welding tool and the metal pieces that are to be joined. This produces a glowing arc whose high temperature fuses the pieces together. Why must the tool be held close to the metal pieces? (i) To maximize the potential difference between tool and pieces; (ii) to minimize this potential difference; (iii) to maximize the electric field between tool and pieces; (iv) to minimize this electric field; (v) more than one of these.arrow_forward
- A welding operation is time-studied during which an operator was pace-rated as 120%. The operator took, on an average, 8 minutes for producing the weld-joint. If a total of 10% allowances are allowed for this operation. What is the expected standard production rate of the weld-joint in units per 8 hour day?arrow_forwardGive information about the reasons why the weld is preferred over other fastening methods.arrow_forwardTwo 3.5 mm thick metal (Um = 9.5 J/mm?) sheets are being joined using resistance spot welding. To achieve required strength, it is desired to form a weld nugget that is 5.5 mm in diameter and 4.0 mm thick. The weld duration will be set at 0.3 sec. If the electrical resistance between the surfaces is 140 microohms, and only onethird of the electrical energy generated will be used to form the weld nugget determine the current.arrow_forward
- Your boss requests a recommendation on which process to use to weld the high strength structural steel rail tank cars hull section. You have this additional information: P-GMAW Productivity is substantially lower. However, you have welders already qualified to do manual p-GMAW welding. Labor is 80% of total cost HYPERFILLⓇ® Productivity gains are important, and the volume of the product is sufficient on the rail tank cars to justify capital investment. With confidence, you respond: Use process because .(Give process and short explanation for why you want to use that process)arrow_forward9. For spot welding of two steel sheets (base metal) each of 3 mm thickness, welding current of 10000 A is applied for 0.2s. The heat dissipated to the base metal is 1000J. Assuming that the heat required for melting 1 mm³ volume of steel is 20J and interfacial contact resistance between sheets is 0.00022, the volume (in mm³) of weld nugget isarrow_forwardQuestion 1 1.1 Identify the weld defect shown in Figure 1 below. Provide reasons for your selection. Figure 1: Weld defect 1.2 Explain how the weld defect, shown in Figure 1, can occur. 1.3 Identify the joining process shown in Figure 2 and explain why this process is frequently used by automotive manufacturers. Figure 2: Joining process frequently used by automotive manufacturers 1.4 Explain the main differences between the joining process shown in Figure 2 and fusion welding processes. 1.5 Name important design considerations applicable to the joining process shown in Figure 2.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage Learning
Welding: Principles and Applications (MindTap Cou...
Mechanical Engineering
ISBN:9781305494695
Author:Larry Jeffus
Publisher:Cengage Learning
Metal Joining Process-Welding, Brazing and Soldering; Author: Toc H Kochi;https://www.youtube.com/watch?v=PPT5_fDSzGY;License: Standard YouTube License, CC-BY