Textbook Question
Chapter 1, Problem 46QTP
A technician determines that the grain size of a certain etched specimen is 8. Upon further checking, it is found that the magnification used was 125 x, instead of the 100 x that is required by the ASTM standards. Determine the correct grain size.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
If a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force direction) at a tensile stress of 50 MPa, slip will occur in the [0 1 1] direction on the (1 1 -1) plane. Use this information to answer the following questions.
Which of the following is the critical resolved shear stress on the slip plane in the slip direction?
Group of answer choices
24.49 MPa
34.65 MPa
12.25 MPa
102 MPa
You are called as an expert witness to analyze the fracture of a sintered silicon carbide plate that was fractured in bending when a blunt load was applied to the plate center. Measurement of the distance between the fracture origin and the mirror/mist boundary on the fracture surface gives a radius of 0.796 mm. You are given three pieces of the same SiC to test, and you determine that the mirror radius is 0.603, 0.203, and 0.162 mm for bending failure stress levels of 225, 368, and 442 MPa, respectively. What is your estimate of the stress present at the time of fracture for the original plate?
which is correct?
53.2 mm , 1.1 mm , 121.4 mm, 22.2 mm ,11.1 mm
Chapter 1 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 1 - What is the difference between an atom and a...Ch. 1 - Prob. 2RQCh. 1 - Prob. 3RQCh. 1 - Prob. 4RQCh. 1 - Define anisotropy. What is its significance?Ch. 1 - What effects does recrystallization have on the...Ch. 1 - What is strain hardening, and what effects does it...Ch. 1 - Explain what is meant by structure-sensitive and...Ch. 1 - Prob. 9RQCh. 1 - What influence does grain size have on the...
Ch. 1 - What is the relationship between the nucleation...Ch. 1 - What is a slip system, and what is its...Ch. 1 - Explain the difference between recovery and...Ch. 1 - What is hot shortness, and what is its...Ch. 1 - Explain the advantages and limitations of cold,...Ch. 1 - Describe what the orange peel effect is. Explain...Ch. 1 - Some metals, such as lead, do not become stronger...Ch. 1 - Describe the difference between preferred...Ch. 1 - Differentiate between stress relaxation and stress...Ch. 1 - What is twinning? How does it differ from slip?Ch. 1 - Prob. 21QLPCh. 1 - What is the significance of the fact that some...Ch. 1 - Is it possible for two pieces of the same metal to...Ch. 1 - Prob. 24QLPCh. 1 - A cold-worked piece of metal has been...Ch. 1 - What materials and structures can you think of...Ch. 1 - Two parts have been made of the same material, but...Ch. 1 - Do you think it might be important to know whether...Ch. 1 - Explain why the strength of a polycrystalline...Ch. 1 - Describe the technique you would use to reduce the...Ch. 1 - What is the significance of the fact that such...Ch. 1 - Prob. 32QLPCh. 1 - It has been noted that the more a metal has been...Ch. 1 - Is it possible to cold work a metal at...Ch. 1 - Comment on your observations regarding Fig. 1.14.Ch. 1 - Is it possible for a metal to be completely...Ch. 1 - Prob. 37QTPCh. 1 - Prob. 38QTPCh. 1 - Plot the data given in Table 1.1 in terms of...Ch. 1 - A strip of metal is reduced from 30 mm in...Ch. 1 - Prob. 41QTPCh. 1 - How many grains are there on the surface of the...Ch. 1 - Prob. 43QTPCh. 1 - Prob. 44QTPCh. 1 - Prob. 45QTPCh. 1 - A technician determines that the grain size of a...Ch. 1 - If the diameter of the aluminum atom is 0.28 nm,...Ch. 1 - The following data are obtained in tension tests...Ch. 1 - Prob. 50QTPCh. 1 - Prob. 51QTPCh. 1 - Prob. 52QTPCh. 1 - Same as Prob. 1.39, but ASTM no. versus...Ch. 1 - By stretching a thin strip of polished metal, as...Ch. 1 - Draw some analogies to mechanical fiberingfor...Ch. 1 - Draw some analogies to the phenomenon of hot...Ch. 1 - Take a deck of playing cards, place a rubber band...Ch. 1 - Give examples in which anisotropy is scale...Ch. 1 - The movement of an edge dislocation was described...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- 3. Two specimens with the same dimensions and made from two different materials, A and B, were subjected to tensile testing. The percentage reduction in the area of the specimen made of material 'A' was calculated 3 times that of the specimen made of material B. In this case, O A lthe ductility of material A and B is equal O Bthe material A is brittle and material B is ductile O Cthe material B is more ductile than material A O D nhe material A is more ductile than material B 1. 20 O Aramak için buraya yazıinarrow_forwardThe fine grains have lower toughness than coarse grains. Select one: True Falsearrow_forwardUnder which of the conditions below is the generalized Hooke’s law applicable for use in analysis? a. When the material distorts due to any of the normal stresses b. When the material has a negative value for Poisson’s ratio c. When the material exceeds its proportional limit but still remains elastic d. When the material’s cross-section changes along one direction Which of the following statements is false about the Poisson’s ratio? a. It is a dimensionless quantity b. It relates the modulus of elasticity E and the modulus of rigidity G c. It has a single value for isotropic and homogeneous materials d. Its magnitude is equal to the negative ratio of the longitudinal strain to the lateral strain.arrow_forward
- please just a three questions left I need answers for them .arrow_forward3 l Two tensile samples were cut from a titanium ingot that was cooled very slowly, and under specific conditions so that the ingot was a single crystal. The samples were then put in a tensile tester to determine their 0.2% offset σys. The σys for the two samples resulted in one sample having a value that was twice of the other. What could the cause be?arrow_forwardHello, I hope you are fine. I need to do this homework in Metal Engineering. I hope to get your help because I have an important homework.arrow_forward
- Sine bar is employed for the precise angle measurement along with slip gauge and dial test indicator in a workshop. At the end of the measuring process, the angle of the specimen found to be 390 for the slip gauge setting ( h ) of 46.12 mm for zero deflection of dial test indicator. Find the length of the sine bar using the above-mentioned data.(b) Using the following observation and find the actual size of the specimen in mm. LC=0.02 mm.arrow_forwardQUESTION 8 A small component is made from aluminium 7475 where Kc = 35.2 MPa m 1/2 Non-destructive testing by micro-computed tomography showed the component to contain cracks of up to 2a = 0.05 mm in length. Laboratory tests showed the crack growth rate under cyclic loading is given by: Where A= 1.10x10-13 Assuming that: da dN = ΑΔΚΑ (MN m-2)-4 m-1 and the component is subjected to an alternating stress of range A = 180 MPa about a mean tensile stress of 40/2. ΔΚ = Δονπα Calculate the number of cycles to failure, give your answer in number of 1000s of cycles to 3 significant figures (e.g. 101,000 cycles would be inputted as 101)arrow_forwardRequest: Can you please help me with answering the following question? Thank you. Question: A specimen of a ceramic material having an elastic modulus of 250 GPa (36.3 x 106 psi) is pulled in tension with a stress of 750 MPa (109,000 psi). Will the specimen fail if its “most severe flaw” is an internal crack that has a length of 0.20 mm (7.87 x 10-3 in.) and a tip radius of curvature of 0.001 mm (3.94 x 10-5 in.)? Why or why not?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Explanation of Solidification of Metals & Alloys | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=G5z9KknF_s8;License: Standard Youtube License