Steel sheets 400 mm wide by 2000 mm longby 2 mm thick are fabricated from SAE 4340 steel,which has a fracture toughnessKc= 98.9 MPa-m0.5. The sheets are inspected forcrack flaws after fabrication, but the inspectiondevice cannot detect flaws smaller than 5 mm. Thevalues of the coefficient and exponent for thismaterial are-9mmA = 4 x 10-⁹ cycles / [MPa¹ - m²/2] andn = 3.Part AUsing fracture-mechanics criteria, estimate the minimum potential cycle life of these sheets if they will be subjected to alengthwise tensile load that continuously varies from 50 to 480 kN.Express your answer using three significant figures.VE ΑΣΦ ↓↑ vecNf=SubmitRequest AnswerReturn to AssignmentProvide Feedback***?Reviewcycles

Given data: Steel sheets dimensions: 400 mm wide by 2000 mm long by 2 mm thick Material: SAE 4340…

Steel sheets 400 mm wide by 2000 mm long by 2 mm thick are fabricated from SAE 4340 steel, which has a fracture toughness K= 98.9 MPa-m0.5. The sheets are inspected for crack flaws after fabrication, but the inspection device cannot detect flaws smaller than 5 mm. The values of the coefficient and exponent for this material are A= 4 x 10-9 mm [MPa - m¹/2] and cycles n = 3. ▼ Part A Using fracture-mechanics criteria, estimate the minimum potential cycle life of these sheets if they will be subjected to a lengthwise tensile load that continuously varies from 50 to 480 kN. Express your answer using three significant figures. N₁ = ΨΕΙ ΑΣΦ | Η vec ? noview cycles

Steel sheets 400 mm wide by 2000 mm long by 2 mm thick are fabricated from SAE 4340 steel, which has a fracture toughness K= 98.9 MPa-m0.5. The sheets are inspected for crack flaws after fabrication, but the inspection device cannot detect flaws smaller than 5 mm. The values of the coefficient and exponent for this material are A= 4 x 10-9 mm [MPa - m¹/2] and cycles n = 3. ▼ Part A Using fracture-mechanics criteria, estimate the minimum potential cycle life of these sheets if they will be subjected to a lengthwise tensile load that continuously varies from 50 to 480 kN. Express your answer using three significant figures. N₁ = ΨΕΙ ΑΣΦ | Η vec ? noview cycles

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

1. For the stress-strain curve shown below, please estimate the properties indicated. (a) Fracture Strain Please do your work on a separate sheet of paper, and put your answers in the boxes on the right. Be sure to include the proper symbol and units. Stress Strain 70 60 50 Stress (ksi) 240 30 20 10 70 0 0.000 60 50 Stress (ksi) 40 20 10 KULL 0 0.000 0.010 0.050 0.100 Strain (in/in) Stress Strain 0.020 0.030 Strain (in/in) 0.040 0.150 0.050 (b) Ultimate Tensile Stress (c) Fracture Stress (d) Proportional Limit (e) Elastic Modulus (1) Yield Stress (g) Tensile Toughness (Modulus of Toughness) (h) Modulus of Resilience
You have been given the following test sample data following mechanical testing of 15 test pieces of Silicon Nitride. What is the Weibull modulus of this material? Would you advise the use of a similar material with a Weibull Modulus of 16.3 and a mean failure stress of 485 MPa, if you anticipate that the peak stress on the material could be 430 MPa? Sample 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 Select one or more: O a. No O b. 18.6 O C. 13.4 O d. Yes O e. 15.7 f. 17.1 Failure Stress (MPa) 423 459 496 432 447 467 473 499 485 479 505 530 526 490 510 <
I need an answer in a short time quickly please ..
Determine the percentage of ductility of a metal alloy having the following tensile stress-strain diagram. Tensile stress-strain diagram 450 400 350 300 250 200 150 100 NO 50 0.05 0.1 0.15 0.2 0.25 0.3 0 35 0.4 Strain 300 EN Stress (Mpa)
Question 2 Figure 2 shows the dependence of fatigue strength on testing cycles (S-N curve) of an acetal polymer. 60 50 40 30 20 10 104 105 106 107 108 Number of cycles to failure Figure 2 The S-N fatigue curve for an acetal polymer a. What is the fatigue strength, or maximum stress amplitude, at one million cycles of loading? b. An acetal polymer 30-cm-long bar with a diameter of 20 mm is designed to survive one million cycles of loading, what is the maximum allowable axial load that can be applied on one end of the bar? Magnitude of stress Reversal, MPa
A steel ruler of 40 cm, calibrated at 27°C, was used to measure a component in a relatively hot environment of 65°C. What would be the error % in the measurements if a .steel=17.7x10-6 °C^-1
This exercise requires showing the complete scanned strokes and procedures, adding it to a pdf document with evidence of all the exercises and the honesty letter. A Titanium specimen with a diameter of 0.8 [in] and 2.5 [in] in length is stretched in uniaxial tension. 1. What is the maximum elongation (DI) of the material. If the deformation is completely elastic? 2. What force is being applied Consider the material properties S_UTS=1205 [MPa]; Sy= 1075 [MPa]; E= 100 [GPa] in the following space write the values found as follows, do not forget the units (-0.5 pts if 4d units do not appear): ]; F= [];
The stainless steel specimen is shown in Figure 3 with tensile engineering stress-strain behaviour. a)Calculate true stress at an engineering strain of 0.04.
360 N marine in basic training climbs a 15 m vertical rope at uniform speed in 8 minutes. His output power
A Tensile Tests of structural steel indicate that it fails whe the axial tensile strain is 1.80x10 μ. 3 Let maximum change in length that 0.25 [in] diamoren in tension car with stand before failure Length Find Structural Steel rad it It is 24 [in] in ni sa 9102
Correct one
Compute the elongation, in %, of a cylindrical copper rod if it is cold worked such that the diameter is reduced from 15.9 mm to 10.4 mm