Question

100%

Phosphorous was added to high purity silicon to produce a 10 ? charge carrier concentration at room temperature. Calculate the conductivity of this material at room temperature, assuming that the mobility of electrons and hollows is the same as for intrinsic material.

?e =0.14 y ?h=0.048 ?-3/V s.

? = 2240(Ω − ?)-1

Expert Solution

Step by step

Solved in 3 steps

SEE SOLUTION Check out a sample Q&A here

Blurred answer

Similar questions

Q2/ If the resistivity of pure silicon is 2300 (0. m) and assuming that the valance electrons of silicon is 4. Let T = 300 K. (a) Calculate the electron density per cubic meter (b) Calculate the electron mobility when the electron density is doubled. Note: Avogadro's number is 8.61 x 10 mol Atomic mass of silicon is 28.08 g/mol, mass density is 2.33 g/cm
Thermal Conductivity for Aluminum is 200 for silicone 0.2
1. Given the following properties for Germanium – Diamond cubic structure (a = 0.5658 nm; Intrinsic carrier density at 300K (n; = 2.4 x 1013 cm-3) Electron mobility (He = 3900 cm²/v-s) Hole mobility (uh = 1900 cm?/v-s) %3D %3D Calculate the following - a. The ratio of the intrinsic carrier density to the atomic density b. The conductivity of intrinsic Ge at 300K
a Bar of intrinsic -3 silicon having a cross-sectional area of 3x10-4 m² has an n; = 1.5×10¹6 m²³. If n = 0.14 m² /V.sand up = 0.05 m²/V.s, how long should the bar be in order that the current in it be 1.2 mA when 9 V is applied across its ends.
X. Determine the resistivity of a germanium crystal at 300 K that has the simultaneous presence of (i) donor impurity of 1 in 10' and (ii) acceptor impurity of 1 in 10%. Given data: Atomic concentration in Germanium is 4.4 x 1022 atoms/cm³, n₁ = 2.5 × 10¹3 /cm³, He = 3800 cm² /Vs and h= 180 cm² /V s.
3. For a Si bar of length 5um, doped n-type at 3x10¹ cm³, calculate the current density for an applied field of 3V across its length. Then do the same for a voltage of 3200V. You can assume that the electron and hole mobilities are 1500 and 500 cm²/V.s, respectively, in the ohmic region below 10¹V/cm and. For higher fields, both electrons and holes have a saturation velocity of 107cm/s.
Q3:- A bar of p-type silicon, has a cross-sectional area A = 10.6 em2 and a length L= 1.2x10 cm. For an applied voltage of 4 V, a current of 3 mA is required. What is the required (a) resistance, (b) resistivity, and te) Impurity doping concentration? td) What is the resulting hole mobility
Hand written solutions are strictly prohibited.
Using hand-drawn schematic diagrams, show curves that illustrate the temperature dependence of the electrical resistivity for the following types of materials: metals, semiconductors, and superconductors. Carefully diagram each curve, and labelling the plot axes.
(Electroplating) A steel part with surface area A = 130 cm² is to be tin-plated. What average plating thickness will result if 15 amps are applied for 10 min in an acid sulfate electrolyte bath? The cathode efficiency for tin is E = 90% and the plating constant C = 4.21 x 10-2 mm³/amp-s. V = CIt V = ECIt d = V A Typical cathode efficiencies in electroplating and values of plating constant C. Compiled from [18]. Plate Metal Electrolyte Cadmium (2) Cyanide Chromium (3) Chromium-acid-sulfate Copper (1) Gold (1) Nickel (2) Silver (1) Tin (4) Zinc (2) Cyanide Cyanide Acid sulfate Cyanide Acid sulfate Chloride Plating Constant ca Cathode Efficiency % mm³/amp-s (in³/amp-min) 6.73 × 10-² (2.47 × 10-4) X 2.50 × 10-2 (0.92 × 10-4) 7.35 x 10-2 10.6 x 10-² 3.42 x 10-2 (2.69 × 10-4) (3.87 × 10-4) (1.25 × 10-4) 10.7 x 10-2 (3.90 × 10-4) 4.21 x 10-2 (1.54 × 10-4) 4.75 × 10-2 (1.74 x 10-4) 90 15 98 80 95 100 90 95 ¹Most common valence given in parentheses (); this is the value assumed in determining…