A cylindrical rod 500 mm long, having a diameter of 12.7 mm, is subjected to a tensile load of 30,000 N. The rod is to experience an elongation not more than 1.3 mm and FOS ≥ 1.5 setting yield strength as a criteria.

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter8: Engineering Materials

Section: Chapter Questions

Problem 60CQ

See similar textbooks

Similar questions

The frame of a space shuttle type vehicle must have a high yield strength and high stillness, and the most important design factor is weight. Of all the materials presented in this chapter, what material might be the most suitable for the frame of a space shuttle? Assume that there will be both tensile and compressive stresses. For a space shuttle, cost is not a limiting factor. (a) You can eliminate entire classes of materials from consideration with a brief statement about their unsuitability. (b) What material has the highest specific yield strength? Give the yield strength, specific gravity, specific yield strength, elastic modulus, and specific elastic modulus for this material. (c) What material has the highest specific elastic modulus? Give the yield strength, specific gravity, specific yield strength, elastic modulus, and specific elastic modulus for this material. (d) Compare the materials with the highest specific yield strength and highest specific elastic modulus for suitability in the space shuttle frame. (C) Discuss the suitability of the top-rated material for this design from the viewpoint of the ability to produce a frame.
Consider an 6061-T6 aluminun alloy having an elastic modulus of 75 GPa and yield strength of 260 MPa. What is the modulus of resilience of the given material ?
(a) the modulus of elasticity in GPa for the Aluminum B) the proportional limit in MPa for the Aluminum C) the ultimate strength in MPa for the Aluminum D) Ductility of material based on percent elongation
Sample: Malleable Steel (AISI 4145) Original Diameter: 6.14mm Gauge Length: 55 mm Final Length: 68.12 mm Final Diameter: 3.54mm Load (kN) Deformation (mm) Stress (MPa) 12.95 Strain (%) 0.3838 0.54 0.7841 0.95 26.48 1.3899 1.63 1.9485 2.07 3.3090 3.10 4.5821 4.22 5.9359 5.03 7.0340 5.51 8.2413 6.22 10.9446 7.22 13.1951 8.18 12.8228 8.77 12.2583 9.11 12.5915 9.61 13.2536 10.33 13.6636 10.71 13.9772 11.35 14.5433 12.63 15.1155 13.88 15.4970 15.10 15.6484 17.09 15.4031 17.79 14.7655 18.73 13.6721 19.28 10.4617 19.88
A cylindrical rod with a radius of 0.3 in. and a length of 15 in. is subjected to a tensile load. If the rod is to experience neither plastic deformation nor an elongation of more than 0.018 in. when the applied load is 7,000 lb, which of the four metals or alloys listed below are possible candidates? Justify your choice(s).
Three materials X, Y, and Z are available for a certain usage. Any material selected must have a good weldability. Tensile strength, stiffness, stability and fatigue strength are required with fatigue strength considered being the most important and stiffness the least important of these factors. The three materials are rated as follows in these factors. Properties X Y Weldability Excellent Рoor Good Tensile strength G E Fair Stiffness Very Good G G Stability G E G Fatigue strength F G E Which material should be selected? Explain your choice.
A cylindrical rod 360 mm long, having a diameter of 10.0 mm, is to be subjected to a tensile load. If the rodis to experience neither plastic deformation nor an elongation of more than 0.9 mm when the applied load is22500 N, which of the four metals or alloys listed below are possible candidates? Justify your choice(s).Material Modulus ofElasticity (GPa)Yield Strength(MPa)TensileStrength (MPa)Aluminum alloy 70 255 420Brass alloy 100 345 420Copper 110 210 290Steel alloy 207 450 550
A 1-cm-diameter, 30-cm-long titanium bar has a yield strength of 345 MPa, a modulus of elasticity of 110.3 * 10^3 MPa, and Poisson's ratio of 0.30. Determine the length and diameter of the bar when 2224N load is applied.
A cylindrical rod with a diameter of 15.24 mm and a gauge length of 400 mm is subjected to a tensile load. If the rod is to experience neither plastic deformation nor an elongation of more than 0.45 mm when the applied load is 31000 N, which of the four metals or alloys listed below are possible candi- dates? Justify your choice(3). TABLE P1.12 Material E (GPa) Yield Strength (MPa) Tensile Strength (MPa) Steel alloy 1 Steel alloy 2 Titanium alloy Сopper 180 860 502 200 400 250 110 900 730 117 220 70
A combined section of steel and copper is subjected to a compressive load. Refer to the table below for the properties of each Steel Copper Area, A 900 mm2 1,200 mm2 Modulus of elasticity, E 200 GPa 120 GPa Allowable compressive stress 140 MPa 70 MPa Which of the following most nearly gives the load, in percent, carried by the copper? Select the correct response: 44.44% 55.56% 66.67% O33.33%
i need quickly please please please Which of these cast iron would allow the greatest amount of plastic deformation before fracture . Nodular cast iron Grey cast iron White cast iron None of them can be worked. If the diameter of steel specimen stretched by tension load is doubled , then it’s tensile strength will be Halved Remain unaffected Doubled Become four times Temperature is proportional with Percent of elongation Tensile strength Modulus of elasticity All above The tensile strength of a steel specimen that have a 182 HB , equals to 490 MPa 910 MPa 627 MPa Not given…
A 7075-T651 alloy is used in a structural component in an airplane. The component must not fail when subjected to a stress of 250 MPa. Several surface flaws have been detected on the component. What is the largest (deepest) surface flaw that could be permitted with the 250 MPa maximum stress? Use data from Table 1 and assume this component geometry and loading condition result in a Y value of 1.25. Yield Strength KI Material MPa ksi MPa√m ksiVin. Metals Aluminum alloy (7075-T651) 495 72 24 22