Foundations of Materials Science and Engineering
6th Edition
ISBN: 9781259696558
Author: SMITH
Publisher: MCG
expand_more
expand_more
format_list_bulleted
Concept explainers
Videos
Textbook Question
Chapter 6.13, Problem 27KCP
What are the three main metallurgical stages that a sheet of cold-worked metal such as aluminum or copper goes through as it is heated from room temperature to an elevated temperature just below its melting point?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
We wish to produce a 0.3 inch thick plate of 3105 aluminum having a tensile strength of at least 25,000 psi and an elongation of at least 5%. The original thickness of the plate is 3 inches. The maximum cold work in each step is 85%. Which of the following procedures would achieve the correct final properties (more than one answer is possible!)?
Group of answer choices
Hot work from 3 in to 0.7 in; cold work from 0.7 in to 0.3 in
Cold work from 3 in to 0.7 in; do an anneal to recrystallize the material; cold work from 0.7 in to 0.3 in
Cold work from 3 inches to 0.3 inches
Cold work from 3 in to 0.7 in; cold work from 0.7 to 0.5 in; do an anneal to recrystallize the material; cold work from 0.5 in to 0.3 in
Hot work from 3 in to 0.5 in; do an anneal to recrystallize the material; hot work from 0.5 to 0.3 in
Hot work from 3 in to 0.7 in; do an anneal to recrystallize the material; hot work from 0.7 to 0.3 in
Cold work from 3 in to 0.5 in; do an anneal to recrystallize the…
Which of the following statements are
true for metals undergoing heat treating and cold working processes: (More than
one statement could be true)
O An increase in ductility correlates with an increase in yield strength.
A decrease in ductility correlates with a decrease in yield strength.
An increase in ductility correlates with a decrease in yield strength.
A decrease in ductility correlates with an increase in yield strength.
Please draw each scenario using the TTT diagram
Chapter 6 Solutions
Foundations of Materials Science and Engineering
Ch. 6.13 - (a) How are metal alloys made by the casting...Ch. 6.13 - Why are cast metal sheet ingots hot-rolled first...Ch. 6.13 - What type of heat treatment is given to the rolled...Ch. 6.13 - Describe and illustrate the following types of...Ch. 6.13 - Describe the forging process. What is the...Ch. 6.13 - What is the difference between open-die and...Ch. 6.13 - Describe the wire-drawing process. Why is it...Ch. 6.13 - Distinguish between elastic and plastic...Ch. 6.13 - Define (a) engineering stress and strain and (b)...Ch. 6.13 - Define (a) modulus of elasticity, (b) yield...
Ch. 6.13 - (a) Define the hardness of a metal. (b) How is the...Ch. 6.13 - What types of indenters are used in (a) the...Ch. 6.13 - What are slipbands and slip lines? What causes the...Ch. 6.13 - Describe the slip mechanism that enables a metal...Ch. 6.13 - (a) Why does slip in metals usually take place on...Ch. 6.13 - Prob. 16KCPCh. 6.13 - What other types of slip planes are important...Ch. 6.13 - Define the critical resolved shear stress for a...Ch. 6.13 - Describe the deformation twinning process that...Ch. 6.13 - What is the difference between the slip and...Ch. 6.13 - Prob. 21KCPCh. 6.13 - Prob. 22KCPCh. 6.13 - What experimental evidence shows that grain...Ch. 6.13 - (a) Describe the grain shape changes that occur...Ch. 6.13 - How is the ductility of a metal normally affected...Ch. 6.13 - (a) What is solid-solution strengthening? Describe...Ch. 6.13 - What are the three main metallurgical stages that...Ch. 6.13 - Describe the microstructure of a heavily...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Describe what occurs microscopically when a...Ch. 6.13 - When a cold-worked metal is heated into the...Ch. 6.13 - Prob. 33KCPCh. 6.13 - Prob. 34KCPCh. 6.13 - Prob. 35KCPCh. 6.13 - Prob. 36KCPCh. 6.13 - Prob. 37KCPCh. 6.13 - Why are nanocrystalline materials stronger? Answer...Ch. 6.13 - A 70% Cu30% Zn brass sheet is 0.0955 cm thick and...Ch. 6.13 - A sheet of aluminum alloy is cold-rolled 30% to a...Ch. 6.13 - Calculate the percent cold reduction when an...Ch. 6.13 - Prob. 42AAPCh. 6.13 - What is the relationship between engineering...Ch. 6.13 - A tensile specimen of cartridge brass sheet has a...Ch. 6.13 - A 0.505-in.-diameter rod of an aluminum alloy is...Ch. 6.13 - In Figure 6.23, estimate the toughness of SAE 1340...Ch. 6.13 - The following engineering stress-strain data were...Ch. 6.13 - Prob. 49AAPCh. 6.13 - A 0.505-in.-diameter aluminum alloy test bar is...Ch. 6.13 - A 20-cm-long rod with a diameter of 0.250 cm is...Ch. 6.13 - Prob. 52AAPCh. 6.13 - Prob. 53AAPCh. 6.13 - Prob. 54AAPCh. 6.13 - Prob. 55AAPCh. 6.13 - Prob. 56AAPCh. 6.13 - A specimen of commercially pure titanium has a...Ch. 6.13 - Prob. 58AAPCh. 6.13 - Prob. 59AAPCh. 6.13 - Prob. 60AAPCh. 6.13 - Prob. 61AAPCh. 6.13 - Prob. 62AAPCh. 6.13 - Prob. 63AAPCh. 6.13 - Prob. 64AAPCh. 6.13 - Prob. 65SEPCh. 6.13 - Prob. 66SEPCh. 6.13 - A 20-mm-diameter, 350-mm-long rod made of an...Ch. 6.13 - Prob. 68SEPCh. 6.13 - Prob. 69SEPCh. 6.13 - Consider casting a cube and a sphere on the same...Ch. 6.13 - When manufacturing complex shapes using cold...Ch. 6.13 - Prob. 74SEPCh. 6.13 - Draw a generic engineering stress-strain diagram...Ch. 6.13 - (a) Draw a generic engineering stress-strain...Ch. 6.13 - Prob. 77SEPCh. 6.13 - Prob. 78SEPCh. 6.13 - Prob. 79SEPCh. 6.13 - The material for a rod of cross-sectional area...Ch. 6.13 - What do E, G, v, Ur, and toughness tell you about...Ch. 6.13 - A cylindrical component is loaded in tension until...Ch. 6.13 - Referring to Figures 6.20 and 6.21 (read the...Ch. 6.13 - (a) Show, using the definition of the Poissons...Ch. 6.13 - A one-inch cube of tempered stainless steel (alloy...Ch. 6.13 - Prob. 87SEPCh. 6.13 - Prob. 88SEPCh. 6.13 - Prob. 89SEPCh. 6.13 - Prob. 90SEPCh. 6.13 - Prob. 91SEPCh. 6.13 - Prob. 92SEPCh. 6.13 - Prob. 93SEPCh. 6.13 - Prob. 94SEPCh. 6.13 - Starting with a 2-in.-diameter rod of brass, we...Ch. 6.13 - Prob. 96SEPCh. 6.13 - Prob. 97SEPCh. 6.13 - Prob. 98SEPCh. 6.13 - The cupro-nickel substitutional solid solution...Ch. 6.13 - Prob. 100SEP
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
A nozzle at A discharges water with an initial velocity of 36 ft/s at an angle with the horizontal. Determine ...
Vector Mechanics For Engineers
Porter’s competitive forces model: The model is used to provide a general view about the firms, the competitors...
Management Information Systems: Managing The Digital Firm (16th Edition)
How are relationships between tables expressed in a relational database?
Modern Database Management
17–1C A high-speed aircraft is cruising in still air. How does the temperature of air at the nose of the aircra...
Thermodynamics: An Engineering Approach
Why is the study of database technology important?
Database Concepts (8th Edition)
What types of coolant are used in vehicles?
Automotive Technology: Principles, Diagnosis, And Service (6th Edition) (halderman Automotive Series)
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- As a materials engineer in a metal-processing company, you are given a section of metal to heat treat after cold working. You are also able to view the microstructure of the metal before and after heat treatment and characterise its mechanical properties. Which of the following describes what you expect to find, when comparing the properties of the metal after heat treatment to before? Select one or more: a. Increased strength b. Reduced strength □ C. Increased ductility d. Reduced ductilityarrow_forwardin the diagram below, which one of the temperatures cannot be used for hot metal forming?arrow_forwardHow can the effects of thermal expansion be controlled so as not to significantly affect integrity of engineering materials?arrow_forward
- 2a: How a material can be mechanically strengthened by designing the grain size after thermomechanical treatments? 2b: How can the extent of cold work be defined? 2c: Specimen A (1008 steel) has an ASTM grain size number of 8 and specimen B (1008 steel) has a grain size number of 4. Which specimen will be having larger grains? A or B 2d: How increasing grain size can play role in decreasing the Toughness? 2e: Is EBSD without using specimen stage tilting is possible?arrow_forwarda) I first bent the unprocessed copper rod. What is the technical name for the type of processing that occurs during bending? How did processing the rod in this way effect its strength? b) What is the technical name for the type of processing that was per formed on the rod heated to 700°C? How did processing the rod in this way effect its strength?arrow_forward1) The stresses and strains in metal forming are of which type? Elastic_plastic_ultimatefracture_none of these 2) The applied stresses in most bulk deformation processes are- Shear_tensile_compressive_bending_none of these 3) What is the difference between the physical shape of bulk deformation and sheet metalworking manufacturing processes?. In bulk deformation, the work parts have a. area-to-volume ratio, whereas in sheet metalworking, the area-to-volume ratio is Low, high_high,low_high,high,low,low 4) is a bulk deformation process in which a workpiece is compressed between two opposing dies, so that the die shapes are imparted to the work. Rolling_forging_drawing_extrusions_none of these 5) is a compression bulk deformation process in which the work material is forced to flow through a die orifice, thereby forcing its cross section to assume the profile of the orifice Forging.extrusion_drawing.extendingrollingnone of these 6) is a bulk deformation process in which the diameter of a…arrow_forward
- The properties of some very ductile metals, such as certain low- carbon steels, change at low temperatures at their particular transition zone. How can this information help an engineer design machinery that will be operating in subzero temperatures?arrow_forwardWhen performing a quench to cool a product, the quench rate affects the outcome of the process. TRUE OR FALSE: 3 principal driving forces for the development of mechanical properties during heat treatment. Group of answer choices Microstructure Changes Formation of Surface Oxide Cooling Rate Ambient Temperature Heating Rate Diffusion Rate Heating Methodarrow_forward2. Could the maximum shear stress theory and the Von Mises theory be used for copper and aluminum alloys?arrow_forward
- Heat treatment is the controlled heating and cooling of metals to alter their physical and mechanical properties without changing the product shape. When performing the cooling step of the tempering process, knife makers have used material such as clay to cover portions of the blade to slow the cooling rate of the covered steel. Why may this technique be beneficial for making a sword which holds a sharp edge while remaining flexible enough to withstand the forces subjected to it in battle?arrow_forwardFor cast iron components, subjected to steady loading which of the following strength is considered to be the failure criterion? O Endurance limit strength O Ultimate tensile strength O Modulus of rigidity O Yield Strengtharrow_forwardI need the answer as soon as possiblearrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Welding: Principles and Applications (MindTap Cou...Mechanical EngineeringISBN:9781305494695Author:Larry JeffusPublisher:Cengage Learning
Welding: Principles and Applications (MindTap Cou...
Mechanical Engineering
ISBN:9781305494695
Author:Larry Jeffus
Publisher:Cengage Learning
First Law of Thermodynamics, Basic Introduction - Internal Energy, Heat and Work - Chemistry; Author: The Organic Chemistry Tutor;https://www.youtube.com/watch?v=NyOYW07-L5g;License: Standard youtube license