There are two dislocations A and B in the crystal. On applying a shear stress, the effect on the dislocations A and B needs to be explained. Concept Introduction: Shear stress is a tangential force which leads to the dislocation or slip of atomic structure. Dislocations are types of defects in the crystal. The two basic types of dislocations are edge and screw dislocations. Edge dislocation is easy to see in a lattice as an extra half-plane of atoms. Since, the defective points are produced due to dislocation in the line, this is called a line defect. The line runs along the extra half-plane at its top. The distortion is seen in the inter-atomic bonds near the dislocation line. As compared to the edge dislocation, the screw dislocation is hard to visualize. It also results from shear stress, but the movement of defect line is perpendicular to the stress direction and replacement of metal. Which is parallel in the case of edge distortion.

Question

"Please, the answer must be documented from a book, experience, or accurate information without using artificial intelligence." Suppose you have two push buttons connected to pins 7 & 8 and two LED's connected to pins 9 & 10 of an Arduino. Write a program to turn ON the LED's if the two push buttons are pressed according to the following scenario. push buttons push buttons LED (pin9) LED (pin10) Delay (pin7) (pin8) open open HIGH HIGH 2s closed open LOW HIGH 1s open closed HIGH LOW 1s closed closed LOW LOW 3s

Answer 1

Question

Chapter 4, Problem 4.30P

Interpretation Introduction

Interpretation:

There are two dislocations A and B in the crystal. On applying a shear stress, the effect on the dislocations A and B needs to be explained.

Concept Introduction:

Shear stress is a tangential force which leads to the dislocation or slip of atomic structure. Dislocations are types of defects in the crystal. The two basic types of dislocations are edge and screw dislocations.

Edge dislocation is easy to see in a lattice as an extra half-plane of atoms. Since, the defective points are produced due to dislocation in the line, this is called a line defect. The line runs along the extra half-plane at its top. The distortion is seen in the inter-atomic bonds near the dislocation line.

As compared to the edge dislocation, the screw dislocation is hard to visualize. It also results from shear stress, but the movement of defect line is perpendicular to the stress direction and replacement of metal. Which is parallel in the case of edge distortion.

Expert Solution & Answer

Trending nowThis is a popular solution!

See solution

Check out sample textbook solution

Students have asked these similar questions

"Please, the answer must be documented from a book, experience, or accurate information without using artificial intelligence." Suppose you have two push buttons connected to pins 7 & 8 and two LED's connected to pins 9 & 10 of an Arduino. Write a program to turn ON the LED's if the two push buttons are pressed according to the following scenario. push buttons push buttons LED (pin9) LED (pin10) Delay (pin7) (pin8) open open HIGH HIGH 2s closed open LOW HIGH 1s open closed HIGH LOW 1s closed closed LOW LOW 3s

"Please, the answer must be documented from a book, experience, or accurate information without using artificial intelligence." OF ENG Connect 8 LED's and one push button to an Arduino, write a program to glow the LED's in series one by one when the button is pressed. When the button is released it should stop and restart again when the button is pressed hold. And when the LED's sequence is complete it should stop and shouldn't restart unless the button is released and repressed.

Bars AD and CE (E=105 GPa, a = 20.9×10-6 °C) support a rigid bar ABC carrying a linearly increasing distributed load as shown. The temperature of Bar CE was then raised by 40°C while the temperature of Bar AD remained unchanged. If Bar AD has a cross-sectional area of 200 mm² while CE has 150 mm², determine the following: the normal force in bar AD, the normal force in bar CE, and the vertical displacement at Point A. D 0.4 m -0.8 m A -0.4 m- B -0.8 m- E 0.8 m C 18 kN/m