Textbook Question
Chapter 34, Problem 28QTP
Estimate the plating thickness in electroplating a 20-mm solid-metal ball using a current of 10 A and a plating time of 1.5 h. Assume that c = 0.08 in Eq. (34.1).
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
(a)
Figure 1 shows surface roughness and tolerances obtained in Chemical
Machining (CM) and Electrochemical Machining (ECM) process for different
types of electronic products.
Comment on the differences between chemical and electrochemical machining
process in terms of surface roughness and tolerance of the machined product as
illustrated in Figure 1.
0.9
CM
0.8
0.7
Z ECM
0.6
0.5
0.4
0.3
0.2
0.1
Product A
Product B
Product C
Product D
Products
25
E ČM
20
Z ECM
15
10
Product A
Product B
Product C
Product D
Products
Figure 1: Surface roughness and tolerances of various electronic products
Surface roughness, Ra
Tolerance, (t mm x 10)
A part made of sheet steel is to be nickel plated. The part is a rectangular flat plate that is 0.075
cm thick and whose face dimensions are 14 cm by 19 cm. The plating operation is carried out in an
acid sulfate electrolyte, using a current = 20 amps for a duration = 30 min. Determine the average
thickness of the plated metal resulting from this operation. Assume, C= 3.42 x 102 mm/A-s, cathode
efficiency E = 95%.
G .l DO o e (iv) Dimensionless film thickness is greater 0 ) 0} ) Question 5: As the temperature is increased coefficient of friction based on the lubrcation regime. Question 6: Which of the following is a desir property of boundary lubricant? igh melting point.
Chapter 34 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 34 - Explain why surface treatments may be necessary...Ch. 34 - What is shot peening? Why is it performed?Ch. 34 - What are the advantages of roller burnishing?Ch. 34 - Explain the difference between case hardening and...Ch. 34 - Describe the principles of physical and chemical...Ch. 34 - Review Fig. 34.2 and describe the principles...Ch. 34 - Prob. 7RQCh. 34 - Prob. 8RQCh. 34 - Prob. 9RQCh. 34 - Prob. 10RQ
Ch. 34 - Prob. 11RQCh. 34 - Prob. 12RQCh. 34 - Prob. 13RQCh. 34 - Prob. 14RQCh. 34 - Prob. 15RQCh. 34 - Prob. 16RQCh. 34 - Describe how roller-burnishing processes induce...Ch. 34 - Explain why some parts may be coated with...Ch. 34 - Prob. 19QLPCh. 34 - Prob. 20QLPCh. 34 - Prob. 21QLPCh. 34 - It is well known that coatings may be removed or...Ch. 34 - Make a list of the coating processes described in...Ch. 34 - Sort the coating processes described in this...Ch. 34 - Why is galvanizing important for automotive-body...Ch. 34 - Explain the principles involved in various...Ch. 34 - Taking a simple example, such as the parts shown...Ch. 34 - Estimate the plating thickness in electroplating a...Ch. 34 - Which surface treatments are functional, and which...Ch. 34 - An artificial implant has a porous surface area...Ch. 34 - If one is interested in obtaining a textured...Ch. 34 - It is known that a mirrorlike surface finish can...Ch. 34 - It has been observed in practice that a thin layer...Ch. 34 - Prob. 34SDPCh. 34 - Prob. 35SDPCh. 34 - Because they evaporate, solvents and similar...Ch. 34 - Prob. 37SDPCh. 34 - The shot-peening process can be demonstrated with...Ch. 34 - Prob. 39SDPCh. 34 - Prob. 40SDP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- The temperature distribution at a certain input of time in concrete slab during curing is given by T= 3+3r + 16 where x is in cm and T is in K. The rate of change of temperature with time is given (a = 0.003 cm2/s). (a) 0.009 K/s (b) 0.0048 K/s (c) -0.0012 K/s (d) -0.0018 K/sarrow_forwardWhat would be the grating constant for a grating with 300 lines/mm? (Express the constant in nanometers).arrow_forward69 alll O ... ۱:۲۰ ۱ ص Sheet 3.pdf Sheet 5 Fatigue Design Note: Assume any missing data QI: Aluminum plate shown: Sut=640 Mpa, is 310 MPa Calculate the diameter at the fillet. reliability is 90%, factor of safety is 2, the size Neglect the transverse shear stress. factor is 0.87, notch sensitivity factor is 0.81, machined surface. Determine the plate thickness (t) for infinite life. 0.2d -50 kN 4.5d- P=+ 50 kN +100 100 P-1 50 kN 50 '150KN 100mm 200mm Q5: A steel cantilever shaft.The fillet is 6 mm, Sut= 560 MPa and Sy= 420 MPa. Assume the shaft surface is cold-rolled, operating temperature is 550c, reliability is 50%. Calculate the design safety factor Nrusing Good-Man theory of failure. Q2: A rotating steel shaft shown: carried by bearings A and E. Machined surface, Su = 500 MPa, reliability is 90%, r=3 mm. What is the life of the shaft if design factor 3? 100 100 js KN 200 300 R6 400N M-- ---- 025 6ODN 3r -3r A 300 350 450 500N 250N Q3: A steel cantilever beam: Sut = 550 MPa, notch…arrow_forward
- After a machinist quickly slips a hot, snugly fitting iron ring over a very cold brass cylinder, the two cannot be separated intact. Can you explain why this is so?arrow_forwardA metallic disc of 20 mm diameter is to be punched from a sheet of thickness 2 mm. Radial clearance is 3 % of sheet thickness. Find out the required punch size?arrow_forwardPlease explain solution.arrow_forward
- 10. Two previously undeformed specimens of the same metal are to be plastically deformed by reducing their cross-sectional areas. One has a circular cross section, and the other is rectangular; during deformation the circular cross section is to remain circular, and the rectangular is to remain as such. Their original and deformed dimensions are as follows: Original dimensions Deformed dimensions Circular (diameter, mm) 15.4 12.1 Rectangular (mm) 129 x 175 75 x 164 Which of these specimens will be the hardest after plastic deformation?arrow_forwardkindly help me with this one please. Thank you! Asap :( General Instructions:>>Show the complete and organize solution. Write your answer with four decimal places and enclose them in a box. Solve as neatly as possible. FOLLOW THIS FORMAT ( GIVEN REQUIRED SOLUTION)arrow_forwardCircles of a metal are being punched that will be later stamped into coins. The metal has a shear strength of 32,575 psi. The sheets are 2.1 mm thick. The coin blanks are to be 16.5 mm in diameter. If sheet of metal is expected to produce 50 coin blanks, how much force is required to punch the sheets?arrow_forward
- A figure shown below is to be blanking through a blanking die The material is 4mm thick stainless steel (half hard) with Ac =0.075. Determine the dimensions of the blanking punch and the die openingarrow_forwardDescribe the relationship between force and surface area using specific quantitative examples. What type of measuring devices would be needed to provide the quantitiesarrow_forward2. In the electrochemical machining of an iron surface with 20 mm× 20 mm in cross-section, the NaCl in water is adopted as electrolyte. The gap between the tool and workpiece is 0.2 mm. The supply voltage is 15 V DC. The specific resistance of the electrolyte is 2 Q cm. (For iron, valency=2, atomic weight=55.85, and density=7860 kg/m³). Please estimate the material removal rate and the tool feedrate.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Understanding Thermal Radiation; Author: The Efficient Engineer;https://www.youtube.com/watch?v=FDmYCI_xYlA;License: Standard youtube license