(a) Interpretation: To calculate the yield strength hardness & % elongation of 1050 steel. Concept Introduction: Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Question

Want to see the full answer?

Answer 1

Question

Chapter 13, Problem 13.23P

Interpretation Introduction

(a)

Interpretation:

To calculate the yield strength hardness & % elongation of 1050 steel.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(b)

Interpretation:

If yield strength of steel is found 125000 psi instead of 170,000psi then the change which will occur in 1050 steel should be determined.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(c)

Interpretation:

If Brinell hardness found to be 525 HB instead of 405 HB then the causes to this high hardness should be stated.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Students have asked these similar questions

The system in Fig. consists of 1200 m of 5 cm cast-iron pipe e=0.26mm, two 45° and four 90° elbows, a globe valve, and a sharp exit into a reservoir. If the elevation at point 1 is 400 m, what gage pressure is required at point 1 to deliver 0.005 m3/s of water into the reservoir? U= 10-6m² 1 * sec -, K 45° elbows= 0.2, K 90° flanged = 0.2, K globe valve 10, K Sharp exit=1 G Elevation 500 m 45° Open globe 45° Sharp exit

Solve

Provide the full blue terminal commands & output and other things that are useful

Answer 2

Question

Chapter 13, Problem 13.23P

Interpretation Introduction

(a)

Interpretation:

To calculate the yield strength hardness & % elongation of 1050 steel.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(b)

Interpretation:

If yield strength of steel is found 125000 psi instead of 170,000psi then the change which will occur in 1050 steel should be determined.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(c)

Interpretation:

If Brinell hardness found to be 525 HB instead of 405 HB then the causes to this high hardness should be stated.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 3

Question

Chapter 13, Problem 13.23P

Interpretation Introduction

(a)

Interpretation:

To calculate the yield strength hardness & % elongation of 1050 steel.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(b)

Interpretation:

If yield strength of steel is found 125000 psi instead of 170,000psi then the change which will occur in 1050 steel should be determined.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(c)

Interpretation:

If Brinell hardness found to be 525 HB instead of 405 HB then the causes to this high hardness should be stated.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 4

Question

Chapter 13, Problem 13.23P

Interpretation Introduction

(a)

Interpretation:

To calculate the yield strength hardness & % elongation of 1050 steel.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(b)

Interpretation:

If yield strength of steel is found 125000 psi instead of 170,000psi then the change which will occur in 1050 steel should be determined.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(c)

Interpretation:

If Brinell hardness found to be 525 HB instead of 405 HB then the causes to this high hardness should be stated.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 5

Chapter 13, Problem 13.23P

Interpretation Introduction

(a)

Interpretation:

To calculate the yield strength hardness & % elongation of 1050 steel.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(b)

Interpretation:

If yield strength of steel is found 125000 psi instead of 170,000psi then the change which will occur in 1050 steel should be determined.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Interpretation Introduction

(c)

Interpretation:

If Brinell hardness found to be 525 HB instead of 405 HB then the causes to this high hardness should be stated.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Answer 6

Chapter 13, Problem 13.23P

Interpretation Introduction

(a)

Interpretation:

To calculate the yield strength hardness & % elongation of 1050 steel.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Answer 7

Chapter 13, Problem 13.23P

Interpretation Introduction

(a)

Interpretation:

To calculate the yield strength hardness & % elongation of 1050 steel.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Answer 8

Interpretation Introduction

(b)

Interpretation:

If yield strength of steel is found 125000 psi instead of 170,000psi then the change which will occur in 1050 steel should be determined.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Answer 9

Interpretation Introduction

(b)

Interpretation:

If yield strength of steel is found 125000 psi instead of 170,000psi then the change which will occur in 1050 steel should be determined.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Answer 10

Interpretation Introduction

(c)

Interpretation:

If Brinell hardness found to be 525 HB instead of 405 HB then the causes to this high hardness should be stated.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Answer 11

Interpretation Introduction

(c)

Interpretation:

If Brinell hardness found to be 525 HB instead of 405 HB then the causes to this high hardness should be stated.

Concept Introduction:

Heat treatment is the metalworking process used to change the physical properties as well as chemical properties of the material that treatment is commonly used in metallurgical for the manufacturing of glass. Heat treatment uses heating on chilling to the extreme temperature to achieve desired properties such as hardening or softening of a material. Under heat treatment various technique uses such as annealing case precipitation, hardening, strengthening, tempering & carburizing quenching.

Answer 12

Expert Solution & Answer

Answer 13

Expert Solution & Answer

Answer 14

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 15

Ch. 13 - Prob. 13.1P Ch. 13 - Prob. 13.2P Ch. 13 - Prob. 13.3P Ch. 13 - Prob. 13.4P Ch. 13 - Prob. 13.5P Ch. 13 - Prob. 13.6P Ch. 13 - Prob. 13.7P Ch. 13 - Prob. 13.8P Ch. 13 - Prob. 13.9P Ch. 13 - Prob. 13.10P

Solution Summary: The author calculates the yield strength hardness & % elongation of 1050 steel.

Want to see the full answer?

Chapter 13 Solutions