The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained. Concept introduction: The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300 − 2000 ° C to decrease the voids between atoms and increase the density.

Question

Want to see the full answer?

Answer 1

Question

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Students have asked these similar questions

Synthesis of 1-metilbenzotriazole from 1,2-diaminobenceno.

Synthesis of 1-metilbenzotriazole.

Indicate the formula of the compound, that is the result of the N- alquilación (nucleofílic substitution), in which an additional lateral chain was formed (NH-CH2-COOMe). F3C. CF3 NH NH2 Br о OMe K2CO3, DABCO, DMF

Answer 2

Question

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 3

Question

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 4

Question

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 5

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Answer 6

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Answer 7

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Answer 8

Expert Solution & Answer

Answer 9

Expert Solution & Answer

Answer 10

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 11

Ch. 12 - Calcium metal crystallizes in a cubic...Ch. 12 - Polonium metal crystallizes in a simple cubic...Ch. 12 - Polonium metal crystallizes in a simple cubic...Ch. 12 - The density of a sample of metal "as measured to...Ch. 12 - Zinc sulfide crystallizes in the following cubic...Ch. 12 - Prob. 12.6A Ch. 12 - Prob. 12.7P Ch. 12 - Prob. 12.8A Ch. 12 - Prob. 12.9P Ch. 12 - Prob. 12.10A

Solution Summary: The author explains the process that results in a final product of ceramic material from raw material is known as ceramic processing. The strength and ture toughness of these ceramics can be increased through reinforced by whiskers.

Concept explainers

Want to see the full answer?

Chapter 12 Solutions