Textbook Question
Chapter 10.7, Problem 74P
If a machine part is made of titanium (TI-6A1-4V) and a critical point in the material is subjected to plane stress, such that the principal stresses are σ1 and σ2 = 0.5σ1, determine the magnitude of σ1 in MPa that will cause yielding according to (a) the maximum shear stress theory, and (b) the maximum distortion energy theory.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A small element at the critical section of a component is in bi-axial state of stress with two principal stresses being 360 MPa and 140 MPa. The maximum working stress according to distortion energy theory (in MPa) is
The principal stresses at a point inside a solid object
are ơ1 = 100 MPa, 02= 100 MPa and 03= 0 MPa. The yield
strength of the material is 200 MPa. The factor of safety
calculated using Tresca (maximum shear stress) theory is
n, and the factor of safety calculated using von Mices
(maximum distortional energy) theory is ny.
Determine the yield strength of a material required such that the component would not fail when subject to the following stresses sigma1 = 2 MPa and sigma 2= -15 MPa sigma 3 = 10 MPa). Use a yield criterion that assumes that yield failure will occur when the maximum shear stress in the complex system becomes equal to the limiting shear strength in a simple tensile test.
Chapter 10 Solutions
MECHANICS OF MATERIALS
Ch. 10.3 - Prove that the sum of the normal strains in...Ch. 10.3 - The state of strain at the point on the arm has...Ch. 10.3 - The state of strain at the point on the leaf of...Ch. 10.3 - Use the strain transformation equations and...Ch. 10.3 - Determine the equivalent state of strain on an...Ch. 10.3 - Determine the equivalent state of strain which...Ch. 10.3 - Use the strain transformation equations to...Ch. 10.3 - Determine the equivalent state of strain, which...Ch. 10.3 - Solve Prob.103 using Mohrs circle. 103. The state...Ch. 10.5 - The strain at point A on the bracket has...
Ch. 10.5 - Determine (a) the principal strains at A, (b) the...Ch. 10.6 - For the case of plane stress, show that Hookes law...Ch. 10.6 - to develop the strain tranformation equations....Ch. 10.6 - Determine the associated principal stresses at the...Ch. 10.6 - Determine the applied load P. What is the shear...Ch. 10.6 - If a load of P = 3 kip is applied to the A-36...Ch. 10.7 - A material is subjected to plane stress. Express...Ch. 10.7 - A material is subjected to plane stress. Express...Ch. 10.7 - Solve Prob. 1061 using the maximum distortion...Ch. 10.7 - Solve Prob.1063 using the maximum distortion...Ch. 10.7 - Prob. 70PCh. 10.7 - The plate is made of Tobin bronze, which yields at...Ch. 10.7 - If a machine part is made of titanium (TI-6A1-4V)...Ch. 10.7 - The components of plane stress at a critical point...Ch. 10.7 - If Y = 50 ksi, determine the factor of safety for...Ch. 10.7 - Prob. 82PCh. 10.7 - If the yield stress for steel is Y = 36 ksi,...Ch. 10.7 - Prob. 84PCh. 10.7 - The state of stress acting at a critical point on...Ch. 10.7 - The shaft consists of a solid segment AB and a...Ch. 10 - In the case of plane stress, where the in-plane...Ch. 10 - The plate is made of material having a modulus of...Ch. 10 - If the material is machine steel having a yield...Ch. 10 - Determine if yielding has occurred on the basis of...Ch. 10 - The 60 strain rosette is mounted on a beam. The...Ch. 10 - Use the strain transformation equations to...Ch. 10 - If the strain gages a and b at points give...Ch. 10 - Use the strain-transformation equations and...Ch. 10 - Use the strain transformation equations to...Ch. 10 - Specify the orientation of the corresponding...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- For a certain metal the strength coefficient K = 600 MPa and the strain hardening exponent n =0.20. During a forming operation, the final true strain that the metal experiences ε = 0.73.Determine the flow stress at this strain and the average flow stress that the metal experiencedduring the operation.arrow_forwardA bracket is under a loading condition is shown below. It's made from a steel with the yield strength (Sy) of 420 MPa. Using either maximum shear stress theory or distortion energy theory, determine the maximum load P that can be applied before yielding happens.arrow_forwardI need the answer as soon as possiblearrow_forward
- To determine the nominal or engineering stress and strain experienced by a specimen of a material while it is subjected to a tension test, and to be able to read important values from a conventional stress-strain diagram obtained from the test. A tension test is being conducted on a steel-rod specimen with a gauge length of L0=50 mm and initial diameter of d0=13 mm. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 506 MPa , e = 689 MPa , g = 585 MPa , and h = 0.146 mm/mm . A) Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 53.0 mm . B) Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 16.0 kN , find the nominal stress experienced by the rod. C)Determine the force P needed to reach the ultimate stress in the steel-rod specimen.arrow_forward(Suppose you need to design a tension test machine capable of testing specimens that have nominal ultimate stresses as high as σu = 100 ksi . How much force must the machine be capable of generating? Assume the testing specimen has the ASTM shape shown. Answer for this is 19.6 kip) (If the maximum nominal strain is ϵf = 0.7 just before the test specimen fractures and the test machine operates by moving only one grip, how far must that grip be designed to travel? The total length of the deforming part of the specimen is 3 in. Answer for this is 2.10 in) Do not know if this info is needed but this was the other 2 partsarrow_forwardTo determine the nominal or engineering stress and strain experienced by a specimen of a material while it is subjected to a tension test, and to be able to read important values from a conventional stress-strain diagram obtained from the test.A tension test is being conducted on a steel-rod specimen with a gauge length of L0=2 in and initial diameter of d0=0.5 in. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 73.0 ksi , e = 101.0 ksi g=83.0ksi, and h=0.15in/in Part A - Nominal or engineering strain in the rod Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 2.5 in . Express the nominal strain in inches per inch to three significant figures. Part B - Nominal or engineering stress in the specimen Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 8.0 kips ,…arrow_forward
- A machine element is subjected to the following bi-axial state of stress; sigma x = 80 MPa; sigma y = 20 MPa; Txy=40 MPa. If the shear strength of the materials is 100 MPa, find the factor of safety as per Tresca's maximum shear stress theory.arrow_forwardQ1. (i) Initial strain Please enter your answers here Q1. (i) Your Answers: Please enter your supplied question data Q1. (ii) E0 B (hr1¹Pa-¹) n Fracture 0.003 4.60E-34 Mechanics of Materials 2 Tutorial 6 Q1. (ii) E General guidance on the Tutorial Portfolio assignment was provided at the beginning of Tutorial Exercise 1 and is available separately on-line on the module website. B 3.2 A Q2. σ (Pa) σo (Pa) 780,000,000 This tutorial exercise assesses fundamental understanding of the creep and stress relaxation response of metals subjected to either constant load or constant strain. It is designed to reinforce learning of principles set out in your current stage 2 lecture notes in "Creep Failure and Stress Relaxation" and to build on knowledge previously presented in the stage 1 module "Solids & Structures". C Q3. t (hr) For further information you may refer to Chapter 21 (Creep and Viscoelasticity) of Benham, Crawford, and Armstrong (1996), 2nd Ed. Q1. A typical graph of strain (e) versus…arrow_forwardA 316 steel plate sample is under the following loading condition:?(sigma) = 90 40 0 40 −50 0 0 0 0 MPaa. Plot the shear and normal stresses on a given oblique plane (rotated plane) on a graph (stress vs. angle) and show the max. shear plane and the principal planes.b. Draw the Mohr circle for the loading state above to scale (using a proper computer program or using a compass with correct scales on the axes) and show the angles you found in (a).c. If the steel sample has a Young’s modulus of 193 GPa, compute the dimensional changes of the plate under the above loading conditionarrow_forward
- A brittle material has the properties Sut = 30 kpsi and Suc = 90 kpsi. Using the brittle Coulomb- Mohr and modified- Mohr theories, determine the factors of safety for the following states of plane stress: a. x = 20 kpsi, Txy = −10 kpsi b. σx = - 15 kpsi, σy = 10 kpsi, Txy = -15 kpsiarrow_forwardThree cases of plane stress at yield or fracture are shown in the figures. Examine each case and determine what type of failure is likely to occur. Limit the choice of criteria to the maximum normal-stress, distortion-energy, and maximum shear-stress theories. Explain your reasoning.arrow_forwardWhat is the change in dimension in the 2 direction in mm? What is the σ1 component of the stresses required to cause these deformations in GPa? What is the σ3 component of the stresses required to cause these deformations in MPa?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Understanding Failure Theories (Tresca, von Mises etc...); Author: The Efficient Engineer;https://www.youtube.com/watch?v=xkbQnBAOFEg;License: Standard youtube license